Description
Zyvax

Sealer 1050 is a solvent-based semi-permanent
sealer for the advanced composites industry which affords
easy application in one step using a wipe-on, let-dry
method. Zyvax

Sealer 1050 is designed to treat both the
chemical and physical bonding sites found on every raw
mold surface. In addition, Zyvax

Sealer 1050 provides the
base needed to extend the life of the release coating and
will allow optimal performance
.
Mold Preparation
1. Tool surfaces should be thoroughly cleaned to remove
all resin build-up, wax, oils, sealers, and other release
agents.
2. Perform a final cleaning of the tool using an
appropriate Zyvax

mold cleaner.

3. If the mold is composite or polymeric, treat with a
Zyvax

mold primer.

Application Instructions
1. Dampen an approved cloth with Zyvax

Sealer 1050
sealer and apply a light and even coat to the entire tool
surface ensuring slight overlaps between wipes to
ensure full coverage.
2. As a guide to achieving a “light coat”, the wet film should
shine, but there should be no runs when applied to a
vertical surface.
3. Continue working across the tool until the entire surface
has been coated.
4. Allow the sealer to cure for a minimum of 15 minutes
prior to applying additional coats.
5. Using the same method, apply additional coats as
necessary for a total of 2 – 4 coats.
6. Allow the sealer to cure for a minimum of 30 minutes
after the final coat has been applied before applying the
appropriate release agent.

Important
The recommended number of coats and cure times are a
general guideline found to be more than sufficient in a
broad spectrum of molding conditions. When molding
products with extreme geometries or experiencing low-
humidity conditions in the shop, the customer may find the
need to extend the cure time between coats and increase
the number of coats applied to the mold. The efficiency of
a release film is best determined through a combination of
tape tests and experimentation.

Storage
Do not store at temperatures above 49 C/120 F. Keep
container tightly sealed to prevent evaporation and/or
contamination. If stored in cold temperatures allow
warming to room temperature before using.

Packaging
Zyvax

Sealer 1050 is available in a variety of package
sizes. Please contact Chem-Trend customer service for
details.

Safety Data
Safety Data Sheets are available for all products and
should be consulted prior to use of the product.

While the technical information and suggestions for use contained herein are
believed to be accurate and reliable, nothing stated in this bulletin is to be
taken as a warranty either expressed or implied.

Further Information

Request information on our complete range of materials: custom-
formulated release agents for polyurethane molding; tire lubes and
bladder coatings; Mono-Coat

semi-permanent release coatings;
aerosol formulations; mold cleaners and sealers; specialized coatings
and application equipment.

Zyvax

Sealer 1050
Mold Sealer

LOCTITE

Frekote WOLO
KnownasFrekoteWOLO
January-2015

PRODUCTDESCRIPTION
LOCTITE

Frekote WOLO providesthefollowingproduct
characteristics:
Technology MoldRelease
Appearance Clear,colorless
LMS
ChemicalType SolventBasedPolymer
Odor Hydrocarbon
Cure Romtemperaturecure
CuredThermalStability 400 C
Application ReleaseCoatings
ApplicationTemperature13 to41 C
SpecificBenefit Highglossfinish
Easyapplication
Fastcuring
Multiplereleases
Minimalmoldbuild-up
LOCTITE

Frekote WOLO isaunique,lowVOCpolymer
releaseagentthatcuresquicklyandprovidesmultiplerelease
ofallpolyesterresins.Applicationsanduseofareleaseagent
hasneverbeeneasier,simplywipeonandleaveontoproduce
ahighglossfinishwithnoneedtopolish.
TYPICALPROPERTIESOFUNCUREDMATERIAL
SpecificGravity@25 C 0.71 to0.73
LMS
FlashPoint-SeeSDS
GENERALINFORMATION
Thisproductisnotrecommendedforuseinpureoxygen
and/oroxygenrichsystemsandshouldnotbeselectedas
asealantforchlorineorotherstrongoxidizing materials.
Forsafehandlinginformationonthisproduct,consultthe
SafetyDataSheet(SDS).
MoldPreparation
Cleaning:
Moldsurfacesmustbethor ghlycleanedanddried.Alltraces
ofpriorreleasemustberemoved.Thismaybeaccomplished
byusing Frekote

PMCorothersuitablecleaner. Frekote

915WB orlightabrasivescanbeusedforheavybuild-up.

SealingNew/RepairedMolds:
Fullycuredunusedmoldssh ldbesealedbeforeuse.This
canbeaccomplishedbyapplying4additionalcoatsof
LOCTITE

Frekote WOLO .Freshor”productionline”
repairs,newfiberglassandepoxymoldssh ldbecuredper
manufacturer’sinstructions,usuallyaminimumof2-3weeks
at22 Cbeforestartingfull-scaleproduction.Occasionally,
greenorfreshlyrepairedmoldsarerushedintoservicepriorto
completecurecausinganincreasedam ntoffreestyreneon
themoldsurface.Theseareasofthemoldsurfacew ldbe
consideredextremelygreenduetotheshortcuretimeandwill
requiretheextrastyrenesealingcapabilityofFrekote Mold
Sealer.Sealingmaybeaccomplishedbywiping2-3coatsof
Frekote

MoldSealer ontotherepairedarea(s). Allowfullcure
oftheappropriateFrekote

moldsealerbeforey applythe
firstcoatofLOCTITE

Frekote WOLO as tlinedinthe
directionsofuse.
Directionsforuse:
1.ApplyLOCTITE

Frekote WOLO withaclean,lintfree,
cottonwipingcloth.WettheclothwithLOCTITE

Frekote WOLO untilitisdampbutnotdripping.
2.Wipeasmoth,wetfilmovertheentiremoldsurface.For
largermolds,applyLOCTITE

Frekote WOLO tothe
surfaceonesectionatatimestartingatoneendand
workingtowardstheother.Continuetoworkthematerial
intothemoldbylightlywipingthewetfilm(10-30
seconds)untilathinanduniformcoatingisobtained,and
thenallowtheproducttoevaporate.
3.Allowaminimumof5minutesbeforeapplyingnextcoat.
Applyaminimumoff rcoatsinthismanner.Dampen
clothlightlyasneeded.
4.Allowthefinalcoattocurefor15minutesat20 C.
5.NOTE: Iftheclothdries tduringy rcoatingprocess,
useafreshcleanclothtoapplythenextcoat.This
preventsresinaccumulationontheclothfrombeing
depositedonthemoldsurface.Ifstreakingoccurs,
replacetheclothwithacleandryoneand/ormakesure
thattheclothisjustdampandnotsoakingwet.Avoid
over-application,asthiswillcausestreakingonthetoling
surface.Streaksorwipelinescanberemovedeasilyby
wipingthemoldsurfacelightlywithadrycloth.Productis
moisturesensitive,keepcontainertightlyclosedwhennot
inuse.
6.NOTE: Formaximumnumberofreleases,applyat ch
upcoatafterthefirst2-3partsarereleasedasabreakin
periodaftertheinitialapplication.Ondeeporhighwear
areas,applyanextra1-2coatsofLOCTITE

Frekote WOLO .Thiswillhelpincreasetheslipeven
furtherinthesehighdragareas.
MoldTouchup
Abrasionwillgraduallycausewearandpartswillbeginto
adheretothemoldsurfaceifacontinu sreleasefilmisnot
maintained.It’sbesttoalwayst ch-upthemoldatthefirst

TDSLOCTITE

Frekote WOLO , January-2015
signofdiminishedrelease,beforereleasebecomesdifficult.
Simplyt ch-uptheentiremoldorapplyspott ch-upstohigh
wearareasfollowingsteps1-3underdirectionsforuse.Only1
coatisusuallyrequiredfort ch-up.Typically,15 minutescure
timeisrequiredpriortoresumptionofmolding.
LoctiteMaterialSpecification
LMS
LMSdated January-24,2007. Testreportsforeachbatchare
availablefortheindicatedproperties. LMStestreportsinclude
selectedQCtestparametersconsideredappropriateto
specificationsforcustomeruse. Additionally,comprehensive
controlsareinplacetoassureproductqualityand
consistency. Specialcustomerspecificationrequirementsmay
becordinatedthr ghHenkel Quality.
Storage
Theproductisclassifiedasflammableandmustbestoredin
anappropriatemannerincompliancewithrelevant
regulations. Donotstorenearoxidizingagentsorcombustible
materials. Storeproductintheunopenedcontainerinadry
location. Storageinformationmayalsobeindicatedonthe
productcontainerlabelling.
OptimalStorage: 8 Cto21 C. Storagebelow8 Cor
greaterthan28 Ccanadverselyaffectproductproperties.
Materialremovedfromcontainersmaybecontaminatedduring
use. Donotreturnproducttotheoriginalcontainer. Henkel
cannotassumeresponsibilityforproductwhichhasbeen
contaminatedorstoredunderconditionsotherthanthose
previ slyindicated. Ifadditionalinformationisrequired,
pleasecontacty rlocalTechnicalServiceCenteror
CustomerServiceRepresentive.
Conversions
( Cx1.8)+32= F
kV/mmx25.4=V/mil
mm/25.4=inches
m/25.4=mil
Nx0.225=lb
N/mmx5.71=lb/in
N/mm x145=psi
MPax145=psi
N m x 8.851= lb in
N mx0.738=lb ft
N mm x0.142=oz in
mPa s=cP
Note:
TheinformationprovidedinthisTechnicalDataSheet(TDS)includingthe
recommendationsforuseandapplicationoftheproductarebasedon r
knowledgeandexperienceoftheproductasatthedateofthisTDS.Theproduct
canhaveavarietyofdifferentapplicationsaswellasdifferingapplicationand
workingconditionsiny renvironmentthatarebeyond rcontrol.Henkelis,
therefore,notliableforthesuitabilityof rproductfortheproductionprocesses
andconditionsinrespectofwhichy usethem,aswellastheintended
applicationsandresults.Westronglyrecommendthaty carry ty rown
priortrialstoconfirmsuchsuitabilityof rproduct.
AnyliabilityinrespectoftheinformationintheTechnicalDataSheetoranyother
writtenororalrecommendation(s)regardingtheconcernedproductisexcluded,
exceptifotherwiseexplicitlyagreedandexceptinrelationtodeathorpersonal
injurycausedby rnegligenceandanyliabilityunderanyapplicablemandatory
productliabilitylaw.
IncaseproductsaredeliveredbyHenkelBelgiumNV,HenkelElectronic
MaterialsNV,HenkelNederlandBV,HenkelTechnologiesFranceSASand
HenkelFranceSApleaseadditionallynotethefollowing:
IncaseHenkelw ldbeneverthelessheldliable,onwhateverlegalgr nd,
Henkel sliabilitywillinnoeventexceedtheam ntoftheconcerneddelivery.
IncaseproductsaredeliveredbyHenkelColombiana,S.A.S.thefollowing
disclaimerisapplicable:
TheinformationprovidedinthisTechnicalDataSheet(TDS)includingthe
recommendationsforuseandapplicationoftheproductarebasedon r
knowledgeandexperienceoftheproductasatthedateofthisTDS.Henkelis,
therefore,notliableforthesuitabilityof rproductfortheproductionprocesses
andconditionsinrespectofwhichy usethem,aswellastheintended
applicationsandresults.Westronglyrecommendthaty carry ty rown
priortrialstoconfirmsuchsuitabilityof rproduct.
AnyliabilityinrespectoftheinformationintheTechnicalDataSheetoranyother
writtenororalrecommendation(s)regardingtheconcernedproductisexcluded,
exceptifotherwiseexplicitlyagreedandexceptinrelationtodeathorpersonal
injurycausedby rnegligenceandanyliabilityunderanyapplicablemandatory
productliabilitylaw.
IncaseproductsaredeliveredbyHenkelCorporation,ResinTechnology
Group,Inc.,orHenkelCanadaCorporation,thefollowingdisclaimeris
applicable:
Thedatacontainedhereinarefurnishedforinformationonlyandarebelievedto
bereliable.Wecannotassumeresponsibilityfortheresultsobtainedbyothers
overwhosemethodswehavenocontrol.Itistheuser’sresponsibilityto
determinesuitabilityfortheuser’spurposeofanyproductionmethodsmentioned
hereinandtoadoptsuchprecautionsasmaybeadvisablefortheprotectionof
propertyandofpersonsagainstanyhazardsthatmaybeinvolvedinthehandling
andusethereof.Inlightoftheforegoing,HenkelCorporationspecifically
disclaimsallwarrantiesexpressedorimplied,includingwarrantiesof
merchantabilityorfitnessforaparticularpurpose,arisingfromsaleoruse
ofHenkelCorporation sproducts.HenkelCorporationspecifically
disclaimsanyliabilityforconsequentialorincidentaldamagesofanykind,
includinglostprofits.Thediscussionhereinofvari sprocessesor
compositionsisnottobeinterpretedasrepresentationthattheyarefreefrom
dominationofpatentsownedbyothersorasalicenseunderanyHenkel
Corporationpatentsthatmaycoversuchprocessesorcompositions.We
recommendthateachprospectiveusertesthisproposedapplicationbefore
repetitiveuse,usingthisdataasaguide.Thisproductmaybecoveredbyoneor
moreUnitedStatesorforeignpatentsorpatentapplications.
Trademarkusage
Exceptasotherwisenoted,alltrademarksinthisdocumentare trademarksof
HenkelCorporationintheU.S.andelsewhere.

denotesatrademark
registeredintheU.S.PatentandTrademarkOffice.

Reference0.1
Americas
+860.571.5100
Europe
+49.89.320800.1800
Asia
+86.21.2891.8863
Forthemostdirectaccesstolocalsalesandtechnicalsupportvisitwww.henkel.com/industrial

TR INDUSTRIES
11022 Vulcan Street
South Gate, CA 90280-0893
Phone 562 -923-0838 Fax 562-861-3475
www.trmoldrelease.com info@trmoldrelease.com

TR-315
COARSE COMPOUND
HEAVY CUTTING PASTE

DESCRIPTION:
TR-315 is a heavy duty paste compound specifically to provide rapid removal of coarse sanding marks, scratches,
overspray, surface stains, orange peel and heavy oxidation on polyester gel-coat.

PRODUCT FEATURES:
Fast cutting action for quick removal of deep surface scratches and other imperfections
Developed for use on gel -coat, but also effective on acrylic lacquers, baked enamels & metals
Minimizes sanding steps for increased efficiency
Easy brush application when working on large vertical surfaces
Contains no silicones or waxes
Economically priced

PHYSICAL PROPERTIES:
Specific Gravity: 1.23 (10.25lbs./Gal)
Viscosity: soft paste water/petroleum emulsion blend
Color: Light orange/reddish

USES:
Initial compound to remove coarse sanding scratches (400g) and blemishes on polyester and vinyl-ester gel -coated
surfaces including finished parts, tooling and master patterns.

APPLICATION:
Apply compound to surface and spread evenly. Using a high speed electric variable speed buffer equipped with all
wool twisted buffing pad set buffer speed to 1,200-1, 500 RPM for best results. Work in a 2 x 2 overlapping surface
area using medium pressure to remove sanding marks and other imperfections. As polish begins to dry gradually
reduce buffing pressure to achieve a smooth uniform semi -gloss appearance. Wipe surface clean if any residual
buffing compound remains before beginning subsequent compounding or polishing while also using a new buffing
pad. Use a buffing spur to clean pad frequently during use to remove excess compound build up.

NOTE:
Recommend following with TR-311 Super Duty Compound to achieve high er gloss smooth finish and then follow
with TR-308 Fine Finish II for optimum high gloss swirl free class A finish.

PACKAGING:
TR-315 is available in Gallon 4×1 case, 5gal pail or 55gal drum. Recommended to store in a cool dry place to
maintain one year shelf life stability.

FOR INDUSTRIAL USE ONLY

The information contained herein is based on tests considered to be reliable and accurate. Because of the wide variance of associated materials
and conditions, however no warranty is expressed or implied. Each user is encouraged to prepare a test part for their particular application.

TR INDUSTRIES
11022 Vulcan Street
South Gate, CA 90280-0893
Phone 562 -923-0838 Fax 562-861-3475
www.trmoldrelease.com info@trmoldrelease.com

TR-905
MOLD PREP CLEANER
SOLVENT

DESCRIPTION:
A proprietary solvent mixture to remove wax, oils and other surface contaminants from reinforced polyester tooling and
other hard surface molds

PRODUCT FEATURES:
Fast evaporation with excellent cleaning ability
Removes compound residue after polishing
Effective on polyester, epoxy and metal tooling
Does not reduce gloss on mold surface
Promotes bonding of sealer/release to mold
Aids in moisture removal after water cleaning

USES:
Recommended for preparation and cleaning of mold surface prior to application of TR-900 Series MULT-PULL Semi-
Permanent Releases or the TR-910 Sealer.

APPLICATION:
Apply TR-905 solvent to mold surface using a clean all cotton (no synthetic blends) cloth working an area sufficient to
stay wet dissolving previously used wax or similar releases. While still wet or dissolved in mold cleaner, wipe dry with
another clean dry cloth, turning and changing cloth frequently to facilitate pick-up. Repeat as necessary until mold is
thoroughly cleaned and dry. Some molds may require use of a light buffing compound for previously used releases or
sealers. The mold prep cleaner should be used after water washing to remove buffing compound residue remaining on
the mold surface. The mold surface should always be wiped dry prior to use of the TR-900 series releases or TR-910
mold sealer.

PHYSICAL PROPERTIES:
Solvent Carrier: Blended aromatic/ ketone solvent
Specific Gravity: 0.83
Wt./Gal: 6.91lbs./gal
Flash Point: 34 F (0.8 C)
Evaporation Rate: >1 (butyl acetate = 1)

STORAGE AND PRECAUTIONS:
TR-905 mold prep cleaner contains flammable solvents. Keep aw ay from spark, open flame or other sources of
ignition. Close container after use and keep stored in cool area. Avoid prolonged exposure to breathing and contact
with skin. Use only with adequate ventilation. Use respirators or fresh air masks in confined areas.

PACKAGING:
Available in gallon 4×1/cases, 5 gallon pail and 55 gallon drum. Please contact your local TR distributor or call direct.

FOR INDUSTRIAL USE ONLY

The information contained herein is based on tests considered to be reliable and accurate. Because of the wide variance of associated materials
and conditions, no warranty is expressed or implied. Each user is encouraged to prepare a test part for their particular application .

www.trmoldrelease.com info@trmoldrelease.com
TR-900
MULTI-PULL
LIQUID SEMI-PERMANENT RELEASE
DESCRIPTION:
TR-900 is a high temp semi-permanent release coating which dries rapidly under atmospheric conditions, bonding an
ultra thin clear release film to the mold surface. Exceptional multiple releases per application for various polyester
molding processes and other resin fiberglass fabrication.
PRODUCT FEATURES:
Excellent hi-temp properties (Thermally Stable 750 F )(400 C)
Multiple release per application
Rapid cure time speeds production cycle
No pre-release or transfer
Wipes to high gloss finish
Easily recoats without build-up
SUGGESTED USES: An ef fective multiple release agent for the FRP and related molders
Open mold hand or spray lay-up
Compression molding
Injection molded parts
Vacuum bag
Resin transfer molding (RTM)
APPLICATION: Always use and apply with a clean, lint-free 100% cotton white cloth (no synthetic blends). Clean
mold surface thoroughly of all previous release agents and sealers using the TR-905 mold prep solvent. Surface
should be completely dry and free of any contaminates. Apply TR-900 by wiping a thin wet coat onto a small area
(approx. 3 x 3 ft.) of the mold surface starting at an end point of the mold. (Do not apply heavily or excessively
wet). While the release film is still wet, wipe gently with another clean dry cotton cloth, turning and changing
cloths as required for proper drying. Avoid excessive hard rubbing or wiping of the treated surface which ensures a
more uniform and effective film deposit. Apply each application overlapping the previous small area until the entire
mold surface is complete. Repeat this for 3-4 coats to the entire mold surface allowing minimum 15 minutes
between coats and 30 minutes after final coat. Maximum results obtained if mold is allowed to stand overnight
before first use. A touch-up coat is recommended for the first 2-3 initial releases to maximize mold conditioning
and durability. When spraying, use a dry air source or airless spray, applying in a thin continuous smooth film,
avoiding excess flooding or runs. Wipe with a clean dry cotton cloth as noted in wipe application.
NOTE: Recommend use of TR-910 SEALER on new or green or repaired molds, more porous or rough mold
surfaces for maximum performance of the TR-900 RELEASE.
PHYSICAL PROPERTIES:
Solvent Carrier: Blend of aliphatic and aromatic naphtha solvent
Specific Gravity: 0.87
Wt./Gal.: 7.25 lbs./Gal.
Coverage: Approx. 1200 Sq. Ft./Gal.
Cure Time: Approx. 15 min. at Room Temp. (75 F) between coats and 30min after final coat
Appearance: Clear thin liquid with characteristic odor.
Cure Method: Chemical reaction with atmospheric moistur e following solvent evaporation

STORAGE AND PRECAUTIONS:
TR-900 contains flammable solvents. Keep away from spark, open flame or other sources of ignition. Store in a cool
dry place and keep in original unopened container. Product will react with atmospheric moisture and container should
be kept tightly closed when not in use. Avoid creating static discharge, do not use microfiber cloth.

PACKAGING:
Available in gallon 4×1 case, 5 gallon pail and 55 gallon drum. Please c ontact your local TR distributor or call direct.

FOR INDUSTRIAL USE ONLY

The information contained herein is based on tests considered to be reliable and accurate. Because of the wide variance of associated materials
and conditions, no warranty is expressed or implied. Each user is encouraged to prepare a test part for their particular application.

STORAGE AND PRECAUTIONS:
TR-920 contains flammable solvents. Keep away from spark, open flame or other sources of ignition. Store in a cool
dry place and keep in original unopened container. Product will react with atmospheric moisture and container
should be kept tightly closed when not in use. Avoid creating static discharge, do not use microfiber cloth.

PACKAGING:
Available in gallon 4×1 case, 5 gallon pail and 55 gallon drum. Please c ontact your local TR distributor or call direct.

FOR INDUSTRIAL USE ONLY

The information contained herein is based on tests considered to be reliable and accurate. Because of the wide variance of associated materials
and conditions, no warranty is expressed or implied. Each user is encouraged to prepare a test part for their particular application.

STORAGE AND PRECAUTIONS:
TR-920 contains flammable solvents. Keep away from spark, open flame or other sources of ignition. Store in a cool
dry place and keep in original unopened container. Product will react with atmospheric moisture and container
should be kept tightly closed when not in use. Avoid creating static discharge, do not use microfiber cloth.

PACKAGING:
Available in gallon 4×1 case, 5 gallon pail and 55 gallon drum. Please c ontact your local TR distributor or call direct.

FOR INDUSTRIAL USE ONLY

The information contained herein is based on tests considered to be reliable and accurate. Because of the wide variance of associated materials
and conditions, no warranty is expressed or implied. Each user is encouraged to prepare a test part for their particular application.

TR-930
MULTI-PULL
LIQUID SEMI- PERMANENT RELEASE
DESCRIPTION:
TR-930 is a high-temp multiple capability semi-permanent release coating which cures under atmospheric condition,
bonding a durable thin, clear release coating to the mold surface. Multiple releases per application for polyester, epoxy,
polyimides, BMC, SMC, and various other advanced resins in fiberglass or graphite composite molding processes,
thermoplastic rotational and rubber molding.
PRODUCT FEATURES:
Excellent hi-temp properties (Thermally Stable to 750 F)(400 C)
Multiple release per application
Ease of application and fast cure time
No pre-release or transfer
Wipes to high gloss finish.
Easily recoats without build-up
SUGGESTED USES: An effective multiple release agent for the FRP and related molders.
Open mold hand or spray lay-up
Compression molding
Injection molded parts
Vacuum bag
Resin transfer molding (RTM)
APPLICATION: HIGH GLOSS POLYESTER
Always use and apply with a clean, lint free all cotton cloth (no synthetic blends). Clean mold surface thoroughly of all
previous release agents and sealers using TR -905 mold prep solvent. Surface should be completely dry and free of
any contaminates. Apply TR-930 by wiping a thin wet coat onto a small area (approx. 3×3 ft.) of the mold surface
starting at an end point of the mold. While the release film is still wet, wipe gently with another clean dry cotton cloth, turning and changing cloths as required for proper drying. Avoid excessive hard rubbing or wiping of the treated surface which ensures a more uniform and effective film deposit. Apply each application overlapping the previous small area until the entire mold surface is complete. Repeat this for 3 4 coats to the entire mold surface. Cure time of
the release film at room temperature (75 F) is approximately 10-15 minutes between coats allowing 20-30min after
final coat before u sing mold. A touch-up coat is recommended for the first 2-3 initial releases to maximize mold
conditioning and durability. When spraying, use a dry air source or airless spray, applying in a thin continuous smooth film, avoiding excess flooding or runs. Wipe with a clean dry cotton cloth as noted in wipe application.
NON-GLOSS OR EPOXY APPLICATIONS: Apply 3-4 thin wet coats allowing solvents to flash. Wait additional 10-15
minutes after solvent evaporation before applying subsequent coats. Surface should be dry and not tacky.
PHYSICAL PROPERTIES:
Solvent Carrier: Blend of Aliphatic and Aromatic Naphthas
Specific Gravity: 0.76
Wt./Gal.: 6.3 lbs./Gal.
Coverage: Approx. 1200 Sq. Ft./Gal.
Cure Time: Approx. 10-20 min. at room temp. (75 F) or 5 min. at 250 F
Appearance: Clear thin liquid with characteristic odor.
Cure Method: Chemical reaction with atmospheric moisture following solvent evaporation.

NOTE: Recommend use of the TR -910 SEALER on new or green and repaired molds or for more porous or rough mold
surfaces and maximum performance of the TR -930 RELEASE.

STORAGE AND PRECAUTIONS: TR- 930 contains flammable solvents. Keep away from spark, open flame or other
sources of ignition. Store in a cool dry place and keep in original unopened container. Product will react with atmospheric
moisture and container should be kept tightly closed when not in use. Avoid creating static discharge, do not use microfiber
cloth.

PACKAGING:
Available in gallon 4×1 case, 5 gallon pail and 55 gallon drum. Please contact your local TR distributor or call direct.

FOR INDUSTRIAL USE ONLY

The information contained herein is based on tests considered to be reliable and ac curate. Because of the wide variance of associated materials
and conditions, however, no warranty is expressed or implied. Each user is encouraged to prepare a test part for his particular application.

TR-930
MULTI-PULL
LIQUID SEMI- PERMANENT RELEASE
DESCRIPTION:
TR-930 is a high-temp multiple capability semi-permanent release coating which cures under atmospheric condition,
bonding a durable thin, clear release coating to the mold surface. Multiple releases per application for polyester, epoxy,
polyimides, BMC, SMC, and various other advanced resins in fiberglass or graphite composite molding processes,
thermoplastic rotational and rubber molding.
PRODUCT FEATURES:
Excellent hi-temp properties (Thermally Stable to 750 F)(400 C)
Multiple release per application
Ease of application and fast cure time
No pre-release or transfer
Wipes to high gloss finish.
Easily recoats without build-up
SUGGESTED USES: An effective multiple release agent for the FRP and related molders.
Open mold hand or spray lay-up
Compression molding
Injection molded parts
Vacuum bag
Resin transfer molding (RTM)
APPLICATION: HIGH GLOSS POLYESTER
Always use and apply with a clean, lint free all cotton cloth (no synthetic blends). Clean mold surface thoroughly of all
previous release agents and sealers using TR -905 mold prep solvent. Surface should be completely dry and free of
any contaminates. Apply TR-930 by wiping a thin wet coat onto a small area (approx. 3×3 ft.) of the mold surface
starting at an end point of the mold. While the release film is still wet, wipe gently with another clean dry cotton cloth, turning and changing cloths as required for proper drying. Avoid excessive hard rubbing or wiping of the treated surface which ensures a more uniform and effective film deposit. Apply each application overlapping the previous small area until the entire mold surface is complete. Repeat this for 3 4 coats to the entire mold surface. Cure time of
the release film at room temperature (75 F) is approximately 10-15 minutes between coats allowing 20-30min after
final coat before u sing mold. A touch-up coat is recommended for the first 2-3 initial releases to maximize mold
conditioning and durability. When spraying, use a dry air source or airless spray, applying in a thin continuous smooth film, avoiding excess flooding or runs. Wipe with a clean dry cotton cloth as noted in wipe application.
NON-GLOSS OR EPOXY APPLICATIONS: Apply 3-4 thin wet coats allowing solvents to flash. Wait additional 10-15
minutes after solvent evaporation before applying subsequent coats. Surface should be dry and not tacky.
PHYSICAL PROPERTIES:
Solvent Carrier: Blend of Aliphatic and Aromatic Naphthas
Specific Gravity: 0.76
Wt./Gal.: 6.3 lbs./Gal.
Coverage: Approx. 1200 Sq. Ft./Gal.
Cure Time: Approx. 10-20 min. at room temp. (75 F) or 5 min. at 250 F
Appearance: Clear thin liquid with characteristic odor.
Cure Method: Chemical reaction with atmospheric moisture following solvent evaporation.

NOTE: Recommend use of the TR -910 SEALER on new or green and repaired molds or for more porous or rough mold
surfaces and maximum performance of the TR -930 RELEASE.

STORAGE AND PRECAUTIONS: TR- 930 contains flammable solvents. Keep away from spark, open flame or other
sources of ignition. Store in a cool dry place and keep in original unopened container. Product will react with atmospheric
moisture and container should be kept tightly closed when not in use. Avoid creating static discharge, do not use microfiber
cloth.

PACKAGING:
Available in gallon 4×1 case, 5 gallon pail and 55 gallon drum. Please contact your local TR distributor or call direct.

FOR INDUSTRIAL USE ONLY

The information contained herein is based on tests considered to be reliable and ac curate. Because of the wide variance of associated materials
and conditions, however, no warranty is expressed or implied. Each user is encouraged to prepare a test part for his particular application.

TR INDUSTRIES
11022 Vulcan Street
South Gate, CA 90280-0893
Phone 562 -923-0838 Fax 562-861-3475
www.trmoldrelease.com info@trmoldrelease.com

TR-309
REGULAR COMPOUND
MEDIUM CUTTING PASTE

DESCRIPTION:
TR-309 is a medium coarse off-white paste compound developed specifically for light oxidation and sanding scratch
removal on polyester gel-coats.

PRODUCT FEATURES:
Fast cutting action for quick effective removal light sanding marks
Good initial gloss achieved on finished parts when sanding for minor defect repair
Remains moist while buffing with less spotting and drying
Restores gloss to lightly oxidized & weathered finishes
Contains no silicones or waxes
Economically priced

PHYSICAL PROPERTIES:
Specific Gravity: 1.23 (10.25lbs./Gal)
Viscosity: soft paste water/petroleum emulsion blend
Color: off-white

USES:
To provide good initial uniform gloss while removing sanding scratches (600g-800g), light oxidation and minor
surface imperfections on all gel coated finishes.

APPLICATION:
Apply TR-309 to gel-coated surface and spread evenly. Using a high speed electric variable speed buffer equipped
with all wool twisted buffing pad set buffer speed to 2,400 RPM for best results. Work in a 2 x 2 overlapping
surface area using medium pressure to keep surface moist to avoid drying out and burnishing. As polish begins to
dry gradually reduce buffing pressure to achieve a smooth uniform gloss appearance. Use a buffing spur to clean
pad frequently during use to remove excess compound build up.

NOTE:
For optimum results polish with TR-308 Fine Finish II to achieve a high gloss mirror like swirl free finish after using
TR-309 regular compound.

PACKAGING:
TR-309 is available in Gallon 4×1 case, 5gal pail or 55gal drum. Recommended to store in a cool dry place to
maintain one year shelf life stability.

FOR INDUSTRIAL USE ONLY

The information contained herein is based on tests considered to be reliable and accurate. Because of the wide variance of associated materials
and conditions, however no warranty is expressed or implied. Each user is encouraged to prepare a test part for their particular application.

?@ABCDE
FGHIAF?@JKKJLME
HJNOJPEQRHPE@GHGSFGE

PGFT@JK?JRLUE
VWXYZ[ ] ^ _`ab c^d ef_f^]f g^]fb hi hae jkWlkmnk g^]f o^]pf c^d ^ib g_fib hq ^rpsf r_f^iit ]h_sfip] ph
efbarf ^ib uiuvf ]pwefif ^ib c^d ef_f^]f ga_bXao he ^rraua_^phix

K@RPOT?EIGS?O@GFUE
y^]f hq ^oo_r^phi z hif ]pfo r_f^ife{ef_f^]f
|^]p bew puf z uoehsfb oehbarphi rwr_f]
}ehsbf] ^ib u^ip^i] ~t~ t_h]] ^oof^e^irf
ydrf__fip qhe bfp^_fb he ihiX] b pwof uh_b ]aeq^rf

OFGFUE^ _`ab c^d ef_f^]f qhe a]f hi ^__ |W} phh_it ufp^_ ^ib hp~fe ~^eb ]aeq^rf uh_b]x
EE ofi uh_b ~^ib he ]oe^w _^w ao
EE ^eg_f hp~fe p~r r^]pit ^oo_r^phi]
WV ^ib rhuoef]]hi uh_bit
jheeh]hi z p^i ] ooit

K FJTSHEK@RKG@?JGFUE
ew Vuf EEkooehdu^pf uiapf] ^p |
ofrqr e^spw EEx xY _g]x{ ^_
V~feu^_ p^g_pw EEZ [ | X Y[[ | Y j X j
jh_he EE_t~p wf__hc p~i _`ab
j E x Y_g]x{t^_ Zt{_

SKKHJTS?JRLUE `ab uh_b ef_f^]f ] efrhuufibfb qhe a]f hi_w hi cf__ rhibphifb phh_itx nef^ Xi ifc he
efrhibphifb uh_b ]aeq^rf] qe]p cp~ he VWX [ZE f^_fe _^vf ^ib VWXZ[YEhe VWXZ[ }^]pf ^d Wf_f^]fx p^ep a]f hq
p~f _`ab c^d ^qpfe X bfXuh_bit he ef_f^]f] a]it o^]pf c^dxE

koo_w cp~ rhpphi r_hp~ coit aiqheu_w i rera_^e uhphix kqpfe ^__hcit bewit X ui ^ib oh_]~it cp~ rhpphi
r_hp~ ph ~t~ t_h]] qi]~ oehrffb cp~ oehbarphi rwr_fx y^r~ ^oo_r^phi he a]f hq p~f hifX]pfo r_f^ife ef_f^]f
efuhsf] ]pwefif ~^vf ^ib fdrf]] c^d qehu uh_b ]aeq^rfx Wfof^pfb a]f u^ip^i] t_h]] efpfiphi ^ib rhipegapf] ph
whae uh_b u^ipfi^irfx j^i ^_]h gf ]oe^wfb he gea]~fbx nea]~it iph uhef bfp^_fb he ihiX] b ]aeq^rf] ^ib p~fi
cofb uufb^pf_w c__ ~f_o r_f^i p~^p pwof hq ]aeq^rfx fp oh_]~it ba__fb he _hcfe t_h]] ^ef^] c__ ef]phef _a]pfe he
]~if ph p~f ^qqfrpfb ^ef^] ^ib fipef uh_b ]aeq^rfx

LR?GUEWf`aef] ^tp^phi gfqhef ^ib baeit a]f ph fi]aef ^bf`a^pf c^d q_u p~r if]] hi uh_bx }h_wf]pfe phh_it
a]f hi_w hi uh_b] qe]p rhibphifb cp~ ^ o^]pf c^d ^ib ef_f^]f hq ^ qfc o^ep]x E

F?R@SMGESLPEK@GTSO?JRLFUE |_^uu^g_f _`ab ]phef i ^ rhh_ bew o_^rf ^ib ffo i heti^_ aihofifb
rhip^ifex ffo ^c^w qehu ]o^e hofi q_^uf he hp~fe ]haerf] hq tiphixE

KST SMJLMUEVWXYZ[E] ^s^_^g_f i t^__hi ^ib t^__hi beau]x }_f^]f rhip^rp whae _hr^_ VW b]pegaphe he r^__ befrpxE
E
IR@EJLPOF?@JSHEOFGERLH E

(& <#='%8"$<'# !'#$"<#&9 (&%&<# <: ":&9 '# $&:$: !'#:<9&%&9 $' & %& <" & "#9 "!! %"$&7 &!" :& '= $(& 6<9& "%<"#!& '= "::'!<"$&9 8"$&%<" : "#9 !'#9<$<'#:* #' 6"%%"#$ <: &3 %&::&9 '% <8 <&97 "!( :&% <: &#!' %" &9 $' %& "%& " $&:$ "%$ ='% $(&<% "%$ ]]> https://revchem.com/document/37wa121_tds-pdf/ Sat, 27 Sep 2025 10:06:24 +0000 https://revchem.com/document/37wa121_tds-pdf/ RELEASES COMPOUNDS POLISHES SEALERS

TR INDUSTRIES
11022 Vulcan Street
South Gate, CA 90280-0893
Phone 562 -923-0838 Fax 562-861-3475
www.trmoldrelease.com info@trmoldrelease.com

TR-104
HI-TEMP MOLD RELEASE

DESCRIPTION:
An industry standard premium paste release for use in higher exothermic applications. Formulated using only the
highest quality refined carnauba wax, blended with other high temperature synthetic waxes and additives producing
the highest quality mold release wax for the composites market.

PRODUCT FEATURES:
Ease of application and removal may be allowed to stand before polishing
Provides hard film with superior heat and chemical properties
Polishes to high gloss without streaking
Reduced wax build-up and styrene accumulation

PHYSICAL PROPERTIES:
Dry Time: 5-10 minutes@ 72 F. Varies depending on working temperature
Wax Melting or Softening Point: 195 – 210 F (88 – 99 C)
Penetration Hardness: 1 at 25 C (carnauba wax)
Color: light blue tint (color coded for identification)
VOC Content: 4.84lbs./gal (580g/l)

USES:
As a release agent for composite molding on all FRP tooling, Formica, metal and other hard surface molds.
Open mold hand or spray lay up
Resin Transfer/injection (RTM) & (RIM)
Vacuum bag and compression molding
Polyester & epoxy resins

NOTE: Check suitability when heat curing or higher temperature molding above 215 F (102 C)

APPLICATION:
On new or reconditioned tooling, suggest use of our sealer glaze TR -301 or TR-910 semi-permanent sealer prior to
waxing for added release, gloss and mold life. Apply wax with sponge applicator in thin even circular motion to the mold
surface. Allow to haze dry (approx. 5-10 min) depending on ambient temperature and polish wipe to gloss finish with soft
cloth (do not use microfiber cloth). For new or reconditioned molds, apply a minimum of 6 coats of paste wax, waiting
approximately 30-60 minutes between applications for the wax to set & harden after the polish wipe. Best results are
obtained, if after application, mold is allowed to stand overnight and a subsequent final coat of wax release applied the
following day prior to gel coating. Follow with a coat of wax for the first 2-3 parts released. Then determine how many
parts can be effectively produced before re-waxing is required. This will vary depending on molding condition,
configuration, resin, mold cycles, effective cure of production gel coat and other factors.

STORAGE AND PRECAUTIONS:
Flammable solid, store in a cool dry place and keep in original unopened container. Keep away from spark, open flame
or other sources of ignition.

PACKAGING:
Available in 14oz (397g) cans and packaged in case quantity of 12 . Contact your local TR distributor or call direct.

FOR INDUSTRIAL USE ONLY

The information contained herein is based on tests considered to be reliable and accurate. Because of the wide variance of associated materials
and conditions, however no warranty is expressed or implied. Each user is encouraged to prepare a test part for their particular application.

TR INDUSTRIES
11022 Vulcan Street
South Gate, CA 90280-0893
Phone 562 -923-0838 Fax 562-861-3475
www.trmoldrelease.com info@trmoldrelease.com

TR-102
REGULAR MOLD RELEASE

DESCRIPTION:
A high production paste wax mold release with excellent breakdown characteristics for fast, even coverage. A firm
carnauba based mold release paste wax blended with other synthetic waxes for use in various thermo-set composite
molding applications.

PRODUCT FEATURES:
High carnauba wax content polishes to high gloss without streaking
Good heat and chemical resistance properties
Easy application and wipe off characteristics
Reduced wax build up and styrene accumulation

PHYSICAL PROPERTIES:
Dry Time: 5-10 minutes@ 72 F. Varies depending on working temperature
Specific Gravity: .80-.82 (approx. 6.75lbs./Gal)
Wax Melting or Softening Point: 185 – 200 F (85 – 93 C)
Color: Off-white

USES:
As a release agent for composite molding on all FRP tooling, metal and other hard surface molds.
Open mold hand or spray lay up
Resin Transfer/injection (RTM) & (RIM)
Vacuum bag and compression molding
Polyester & epoxy resins

NOTE: Check suitability when heat curing or higher temperature molding above 200 F (93 C)

APPLICATION:
On new or reconditioned tooling, suggest use of our sealer glaze TR -301 or TR-910 semi-permanent sealer prior to
waxing for added release, gloss and mold life. Apply wax with sponge applicator in thin even circular motion to the mold
surface. Allow to haze dry (approx. 5-10 min) depending on ambient temperature and polish wipe to gloss finish with soft
cloth (do not use microfiber cloth). For new or reconditioned molds, apply a minimum of 6 coats of paste wax, waiting
approximately 30-60 minutes between applications for the wax to set & harden after the polish wipe. Best results are
obtained, if after application, mold is allowed to stand overnight and a subsequent final coat of wax release applied the
following day prior to gel coating. Follow with a coat of wax for the first 2-3 parts released. Then determine how many
parts can be effectively produced before re-waxing is required. This will vary depending on molding condition,
configuration, resin, mold cycles, effective cure of production gel coat and other factors.

STORAGE AND PRECAUTIONS:
Flammable solid, store in a cool dry place and keep in original unopened container. Keep away from spark, open flame
or other sources of ignition.

PACKAGING:
Available in 14oz (397g) cans and packaged in case quantity of 12. Please contact your local TR distributor or call
direct.

FOR INDUSTRIAL USE ONLY

The information contained herein is based on tests considered to be reliable and accurate. Because of the wide variance of associated materials
and conditions, however no warranty is expressed or implied. Each user is encouraged to prepare a test part for their particular application.

TR INDUSTRIES
11022 Vulcan Street
South Gate, CA 90280-0893
Phone 562 -923-0838 Fax 562-861-3475
www.trmoldrelease.com info@trmoldrelease.com

TR-930HS
MULTI-PULL
LIQUID SEMI-PERMANENT RELEASE

DESCRIPTION:
TR-930HS is a high slip low odor fast curing multiple capability s emi-permanent mold release for use molding various
polymers (polyester, epoxy, polyamide, SMC, BMC, etc.). Excellent for difficult to release closed mold processes,
filament winding and non gel-coat polyester applications.

PRODUCT FEATURES:
High temperature properties up to 750 F (400 C)
High slip – multiple releases per application
Easy wipe on leave on or spray application
No pre-release or transfer
Durable high gloss coating
Easily recoats without build-up

USES:
Open mold hand or spray lay-up
Compression & Prepreg molding
Injection molded parts
Vacuum bag/RTM
Filament winding/Rotational Molding

APPLICATION:
Clean mold surface thoroughly of all previous sealers and release agents using TR-905 mold prep solvent. Light
abrasive compounding may be necessary to remove the various types of release agents or sealers previously used.
After compounding, first water wash and wipe dry to remove compound residue. Then completely clean the mold
surface with TR-905 mo ld prep solvent.

Apply a thin wet film to mold surfaces either by wipe or spray. Use an ALL-COTTON cloth when wiping to avoid possible
binders in other fabrics dissolving from solvent carriers. Use an airless spray unit or a dry air source when spraying
holding spray nozzle approximately 8-10 inches from mold surface. Start at one end of a mold working small areas or
sections to the other end ensuring a thin wet film is applied to entire mold surface. Secondary polish step is not required.
If desired gloss is reduced after application, lightly polish with 100% cotton cloth after final coat.

For initial break-in, apply 3-5 coats. Allow 5-10 minutes between each application and 10-15 minutes after final
application for solvent release and cure. Recoat for the first 2 -3 initial pulls or de- molding to aid full conditioning and
mold life. Recoat will vary depending upon mold design or materials. Apply again at first sign of release difficulties. Use
the TR-910 sealer if mold surface is porous, less smooth, or to provide improved initial release on new or green and
repaired molds.

PHYSICAL PROPERTIES:
Solvent Carrier: Blend of hydrocarbon naphtha
Specific Gravity: 0.725
Wt/Gal.: 6.04 lbs./Gal
Shelf Life: 1 year from date of manufacture
Cure Time: Approx. 5-10min. between coats and 10-15 min after final coat at room temp (75 F)
Appearance: Clear colorless with characteristic odor
Cure Method: Chemical reaction with atmospheric moisture following solvent evaporation

NOTE: Do not apply subsequent coats until complete solvent evaporation of prior coat.

STORAGE AND PRECAUTIONS:
TR-930HS contains flammable solvents. Keep away from spark, open flame or other sources of ignition. Store in a cool
dry place and keep in original un-opened container. Product will react with atmospheric moisture and container should
be kept tightly closed when not in use. Avoid creating static discharge, do not use microfiber cloth.

PACKAGING:
Available in gallon 4×1/cases, 5 gallon and 55 gallon drum. Please contact your local TR distributor or call direct.

FOR INDUSTRIAL USE ONLY

The information contained herein is based on tests considered to be reliable and accurate. Because of the wide variance of associated materials
and conditions, no warranty is expressed or implied. Each user is encouraged to prepare a test part for their particular application.

RELEASES COMPOUNDS POLISHES

TR-111
SLURRY WAX RELEASE

FLANGES EDGES HATS

DESCRIPTION:
A soft white compounded wax based on refined petroleum waxes. Leaves no discoloration to molded
parts and contains no silicones.

PRODUCT FEATURES:
Easy spreading and wipe characteristics
Provides positive releases, remains soft and ease of removal
Effectively fills rough surfaces and is PVA compatible
Good thermal stability with reduced build up

USES:
For all mold flanges, edges and hats in cultured marble, onyx or granite production, FRP Tubs, showers,
spa fabrication, polymer concrete and general polyester molding applications. Any surface where gloss
or cosmetics is not a critical requirement for finished part. Sealer on porous substrates for prototypes and
mock-ups or in conjunction with PVA sprayed film.

APPLICATION:
Apply a minimum of two coats with brush or cloth allowing each coat to dry prior to applying additional
coats. This provides a base film for initial release. Apply again lightly after first part is pulled and then
subsequent coats as needed. Applications will vary dependent on surface conditions, molding cycle,
fabrication methods and general shop practices.

Available in gallon 4×1/cases, 5 gallon and 55 gallon drum. Please contact your local TR distributor or
call direct.

The information contained herein is based on tests considered to be reliable and accurate. Because of the wide variance of
associated materials and conditions, no warranty is expressed or implied. Each user is encouraged to prepare a test part for
their particular application.