HYDROPEL
RO1O-FPA SERIES
VINYL ESTER RESIN
VINYL ESTER RESIN FOR INFUSION
Typical Cast Mechanical Properties
1
Test Unit of Measure Nominal Test Method
Tensile Strength psi/MPa 13,980/96 ASTM D 638
Tensile Modulus psi/GPa 540,000/3.9 ASTM D 638
Tensile Elongation % 4.7 ASTM D 638
Flexural Strength psi/MPa 22,660/156 ASTM D 790
Flexural Modulus psi/GPa 540,000/3.7 ASTM D 790
Heat Distortion Temp. F/ C @264 psi 239/115 ASTM D 648
Typical Liquid Properties
2
VERSIONS Catalyst % GT
Gel
to
Peak
Peak
Exotherm
( F/ C)
Visc SP rpm cps
%
Styrene
R010-FPA-17 MEKP-925 1.0 17 7 376/191 LV 3 30 150 36
*Typical properties are not to be construed as specifications.
DESCRIPTION
AOC’s Hydropel R010-FPA is a non-
thixed and pre-promoted vinyl ester
resin system. Other gel time versions
can be considered, either by promo-
tion changes or inhibitor recommen-
dations.
APPLICATION
AOC’s Hydropel R010-FPA is suited
for manufacturing boats and marine
craft along with other composite ap-
plications needing superior properties
that utilize the Vacuum Infusion pro-
cess.
BENEFITS
Low viscosity allowing for fast and
controlled infusing times.
Excellent strength and toughness
of the resultant laminate /compo-
site.
AOC World Headquarters
955 Highway 57 East, Collierville, TN 38017
+01 901.854.2800
AOC-Resins.com
SALES CONTACTS
NORTH AMERICA
Toll free: +1 866 319 8827
northamerica@aoc-resins.com
EUROPE
+44 1206 390415
europe@aoc-resins.com
INDIA
+44 1206 390415
india@aoc-resins.com
LATIN AMERICA
+01 863 815 5016
latinamerica@aoc-resins.com
AOC UK LTD.
+44 1206 390400
salesUK@aoc-resins.com
ASIA/AUSTRALIA
+44 1206 390415
asia@aoc-resins.com
MIDDLE EAST
+44 1206 390415
middleeast@aoc-resins.com
AOC is a registered trademark of AOC, LLC.
The information contained in this data sheet is based on laboratory data and field experience. We believe this information to be reliable, but do not guarantee its applicability to the user s process or
assume any liability for occurrences arising out of its use. The user, by accepting the products described herein, agrees to be responsible for thoroughly testing each such product before commit-
ting to production. Our recommendations should not be taken as inducements to infringe any patent or violate any law, safety code or insurance regulation. This data sheet and its contents are the
confidential and proprietary information of AOC and it may not be modified altered deconstructed or presented in any other manner without the explicit authorization of AOC and/or its legal counsel.
HYDROPEL
R010-FPA SERIES VINYL ESTER RESIN
PERFORMANCE GUID ELINES
A. Keep full strength catalyst levels
between 1.0% – 2.0% of the total resin
weight.
B. Maintain shop temperatures be-
tween 65 F/18 C and 90 F/32 C
and humidity between 40% and 90%.
Consistent shop conditions contribute
to consistent gel times and will help
the fabricator make a high quality part.
C. Sanding and/or grinding is recom-
mended if a secondary bond is applied
to a laminate that was made with a
resin containing wax.
STORAGE STABILITY
This product is stable for three months
from the date of manufacture when
stored in the original containers, away
from direct sunlight or other UV light
sources and at or below 77 F/25 C.
Storage stability of two months or less
should be anticipated if the storage
temperature exceeds 86 F/30 C.
After extended storage, some drift
may occur in the product viscosity
and gel time.
SAFETY
See the appropriate Safety Data Sheet
for guidelines.
ISO 9001:2008 CERTIFIED
The Quality Management Systems at
every AOC manufacturing facility have
been certified as meeting ISO
9001:2008 standards. This certifica-
tion recognizes that each AOC facility
has an internationally accepted model
in place for managing and assuring
quality. We follow the practices set
forth in this model to add value to the
resins we make for our customers.
FOOTNOTES
(1.) Based on tests at 77 F/25 C and 50% relative
humidity. All tests performed on unreinforced
cured resin castings. Thixotropic components, if
applicable are excluded from casting samples.
Castings were post cured.
(2.) The gel times shown are typical but may be
affected by catalyst, promoter, inhibitor concentra-
tion, resin, mold, and shop temperature. Variations
in gelling characteristics can be expected between
different lots of catalysts and at extremely high
humidities. Pigment and/or filler can retard or
accelerate gelation. It is recommended that the
fabricator check the gelling characteristics of a
small quantity of resin under actual operating
conditions prior to use.