PDS-TPrime130-1-6-0520 1
T-Prime 130-1
EPOXY TOOLING INFUSION SYSTEM
Thermally stable up to 130 C (266 F) when fully postcured
Resistant to thermal cycling damage
Low initial mixed viscosity for easier infusion; 247 cP at 25 C (77 F)
Long pot-life and gel time; capable of infusing large or complex moulds
Ambient curing and low shrinkage for accurate mould manufacture
INTRODUCTION
T-Prime 130-1 is an epoxy tooling system for manufacturing glass or carbon moulds from liquid infusion processes.
T-Prime 130-1 is compatible with Gurit s range of 130 C tooling gelcoat, laminating and repair systems.
T-Prime 130-1 is a low shrinkage ambient curing system, which provides a simple way to produce high accuracy
moulds. Designed for infusion and cure at ambient temperatures, it should then be mid-cured at 40 C (104 F) for 4
hours to guarantee the strength needed for demoulding. It can then be postcured off the plug to give a material that
is thermally stable to 130 C (266 F). Exceeding this temperature will cause a rapid loss in stiffness and a safety
margin is required for the maximum tool operating temperature to prevent distortion or tool damage.
T-Prime 130-1 is a further improvement on T-Prime 130 giving improved storage stability and an extended pot-life.
2 PDS-TPrime130-1-6-0520
MIX RATIO
T-Prime 130-1 should be mixed at the following mix ratio:
T-Prime 130-1 Resin T-Prime 130-1 Hardener
100:27 (by weight)
100:33.3 (by volume)
Any deviation from the prescribed mix ratio may degrade the
thermal capability and physical properties of the material. The
mix ratio of the newer T-Prime 130-1 is different to the older
version of the product, T-Prime 130.
SYSTEM INFORMATION
Component Properties
Resin Hardener
Viscosity at 20 C 918 cP 30.4 cP
Viscosity at 25 C 595 cP 25.8 cP
Viscosity at 30 C 383 cP 21.9 cP
Shelf Life (Months) 12 12
Colour (Gardner) 1 (Opaque) 0 (Clear)
Density gm/cm
3
(lb/ft
3
) 1.150 (71.8) 0.974 (60.8)
Working Properties
Mixed Density @ 20 C 1.11 gm/cm
3
(69.5 lb/ft
3
)
Initial Mixed Viscosity at 25 C 247 cP
Gel Time (150g in Water at 25 C) 5:27 (hours:minutes)
Pot Life (500g in Air at 20 C)* 3:25 (hours:minutes)
Pot Life (300g in Air at 25 C) 2:15 (hours:minutes)
Resin Gel times vs Temperature
20 C
(68 F)
25 C
(77 F)
30 C
(86 F)
40 C
(104 F)
Latest flow under vacuum (5,000P
Theoretical thin film) (hr:min)
7:00 4:20 3:40 2:23
Earliest Vacuum off time (100,000P
Theoretical thin film) (hr:min)
9:22 5:44 4:45 3:02
Demould Time Recommended 4 hours at 40 C (104 F) after system has gelled to reduced risk of laminate damage
Overcoating window on T-Gel 130-1
Slow. 20 C (68 F), 50-70% RH
1-6 days.
* Pot life in larger volumes can be reduced. Material approaching its pot life is typically 40-50 C (104 122 F) in the centre of the pot and it will then thicken as it cools
in the laminate and feed pipes. This material will have already seen higher temperature will reach a higher viscosity more quickly than the thin film data at a given
workshop temperature.
PDS-TPrime130-1-6-0520 3
isothermal @ 20 C
isothermal @ 25 C
isothermal @ 30 C
isothermal @ 40 C
Time (minutes)
Viscosity (P)
0 60120 180 360300240
0
200
400
600
800
1000
1200
T-Prime 130-1 Viscosity Isothermal CAP 2000 Cone 6, 50rpm
Time / Minutes
Temperature C
0 60 120 180 240
0
20
30
50
60
80
30 90 150 210
10
40
70
Pot Centre 20 C Test
Air 20 C Test
Pot Life 20 C
Pot Centre 25 C Test
Air 25 C Test (Actual 26 C)
Pot-Life at 25 C
20 C = 205min
25 C = 135min
T-Prime 130-1 Temperature vs Time at Centre of 500g Pot Life Test
Large volumes of T-Prime 130-1 left in bulk > 50mm deep can exotherm strongly and the excess will need to be dispensed into a
shallower vessel. Ideally this should be less than 30mm deep or the pot placed into water to cool.
4 PDS-TPrime130-1-6-0520
APPLICATION NOTES
nA good level of understanding of the infusion process is
required to achieve a high quality mould. Contact SP-High
Modulus for further advice or refer to SP-High Modulus process
notes for further information.
nAny deviation from the prescribed mix ratio may degrade the
thermal capability and physical properties of the material
nRecommended workshop temperature is between 18 C and
25 C (64 F and 77 F)
nIf drill style mixing is used, this must be on the lowest
setting to reduce the air introduced. Particular attention is
needed to mix the sides and bottom of the container
nAllowing the mixed resin to stand for 5-10 minutes before
use in order to allow air to dissipate to improve the final
laminate quality.
nFor large components pre-weigh and dispense into labelled
or coloured pots rather than pre-mix all the material to extend
pot life for large infusions. This also avoids potential exotherm
problems with large quantities of unused mixed system.
nIf large quantities are left in feed buckets and vacuum pots
at the end of the infusion it is recommended to transfer some
of the bulk material into a shallow vessel, with a large surface
area, to dissipate heat. It is recommended to always keep the
bottom of feed pipes covered in resin to avoid the risk of air
inclusion even after the feed pipes are closed / clamped.
nDepending on the infusion design it can take a large amount
of time to infuse the final 10% of a part as the flow rate slows
with distance from the final feed pipe. This is a critical time to
monitor the resin pot life and change to new resin if required.
Material close to the pot life can build in viscosity and block the
feed pipes. If the infusion is running slowly it is recommended
to allow the resin levels to lower in the feed pot and aim to
supply new resin every 2.5 hours at 20 C and 1 to 1.5 hours at
25 C if there looks like there will be a problem with filling the
final laminate.
nIf emptying a receiving bucket inside a vacuum pot
remember to allow time for the vacuum to fully build back up
inside the pot before opening the control valves to the part
otherwise any air inside the vacuum pot may be pulled back
into the part.
nIf using T-Gel 130-1 Slow allow at least 24 hours at 20 C
(68 F) before applying vacuum to begin the infusion to ensure
sufficient stiffness of T-Gel 130-1. Infusing too soon can lift the
gelcoat and cause sink marks.
CURED PROPERTIES
AMBIENT CURE
The mechanical strength after 24 hours at 20 C (68 F) is still
low and a mid cure is needed to de-mould.
If more than one infusion stage is used allow at least 2 days
at 20 C (68 F), or cure elevated temperature, before removing
peel ply and other infusion consumables. This is to remove
the risk of delamination and subsequent blisters from lifting
the part cured laminate.
If peel ply is removed before a full cure the part cured shards
of resin created can contain a significant amount of un-reacted
epoxy. Un-reacted epoxy dust is a particular skin irritant and
the appropriate personal protective equipment (PPE) should
be used.
MID CURE
A mid cure of at least 4 hours at 40 C (104 F) is
recommended before de-moulding to maximise gelcoat
adhesion and build sufficient resin strength for demould.
Ramp rate is not critical at this stage.
PDS-TPrime130-1-6-0520 5
APPROXIMATE MATERIALS COVERAGE
Approx net resin use and thickness for Gurit woven and stitched carbon and glass structural laminates infused at 100% vacuum.
Other fabrics such as Tissues and Chop Strand Mat materials use additional resin test panels may be needed to verify usage for
these material.
Structural Glass Laminates (32% Resin Content) Resin & Thickness by Fibre gsm
Fibre gsm Resin gsm Total /Kg/m
2
Thickness /mm
200 94 0.294 0.155
300 141 0.441 0.233
450 211 0.661 0.349
600 281 0.881 0.465
900 422 1.322 0.698
1200 563 1.763 0.930
Structural Glass Laminates (32% Resin Content) Fibre & Resin for Set Thickness
Fibre gsm Resin /Kg Total /Kg/m
2
Thickness /mm
7,740 3.63 11.37 6.0
12,900 6.05 18.95 10.0
Net Resin Figures – No waste allowance
POST CURE
To achieve full postcure ramp at 0.2 C /min to 120 C (8.5 hours) and dwell for 2 hours (0.36 F /min to 248 F). Faster postcure risks
thermal softening of the tool. Contact Gurit for advice when in doubt.
Cured Properties
Property Unit Mid Cure 4 Hours at 40 C (104 F)
Mid Cure + Postcure
2 hours at 120 C (248 F)
Tg2 by DSC C ( F) 53 C (127 F) 133 C (271 F)
6 PDS-TPrime130-1-6-0520
Structural Carbon Laminates (40% Resin Content) – Resin & Thickness by Fibre gsm
Fibre gsm Resin gsm Total /Kg/m
2
Thickness /mm
200 134 0.334 0.221
300 201 0.501 0.331
450 301 0.751 0.497
600 401 1.001 0.663
900 602 1.502 0.994
1200 802 2.002 1.326
Structural Carbon Laminates (40% Resin Content) Fibre & Resin for Set Thickness
Fibre gsm Resin /Kg Total /Kg/m
2
Thickness /mm
5,430 3.63 9.06 6
9,050 6.05 15.10 10
Net Resin Figures – No waste allowance
A general 10 to 15% waste value is then recommended for purchase estimation. Additional resin is also required for infusion
consumables. Resin waste in feed meshes and pipework depends on the component geometry and infusion design. As approx
guide resin allow;
nSmall Infusion (Up to 2m2) Approx 2 Kg/m
2(Generally have a higher % waste)
nLarge Infusion (20m2 and above)Approx 1 Kg/m
2
For the first components, and when new to infusion, allow extra resin for feed pots.
PDS-TPrime130-1-6-0520 7
HEALTH AND SAFETY
The T-Prime 130-1 system has been designed for use in closed
mould processes. Users should ensure that some elevated
temperature cure is applied to the component before trying to
machine it. In a component made from T-Prime 130-1, which has
seen no heat, there will only be a partial cure. Therefore the
sanding dust will be more irritating than dust from a laminate
cured at elevated temperature, in which there will be more
thorough cross linking. Particular care should also be taken
when removing peel plies from part cured material as this can
also product a dust like particle, and an elevated cure or
personal protective equipment is recommended.
The following points must be considered:
1. Skin contact must be avoided by wearing protective gloves.
Gurit recommends the use of disposable nitrile gloves for
most applications. The use of barrier creams is not
recommended, but to preserve skin condition a
moisturising cream should be used after washing.
2. Overalls or other protective clothing should be worn when
mixing, laminating or sanding. Contaminated work clothes
should be thoroughly cleaned before re-use.
3. Eye protection should be worn if there is a risk of resin,
hardener, solvent or dust entering the eyes. If this occurs
flush the eye with water for 15 minutes, holding the eyelid
open, and seek medical attention.
4. Ensure adequate ventilation in work areas. Respiratory
protection should be worn if there is insufficient ventilation.
Solvent vapours should not be inhaled as they can cause
dizziness, headaches, loss of consciousness and can have
long term health effects.
5. If the skin becomes contaminated, then the area must be
immediately cleansed. The use of resin-removing cleansers
is recommended. To finish, wash with soap and warm
water. The use of solvents on the skin to remove resins etc
must be avoided.
Washing should be part of routine practice:
nbefore eating or drinking
nbefore smoking
nbefore using the lavatory
nafter finishing work
6. The inhalation of sanding dust should be avoided and if it
settles on the skin then it should be washed off. After more
extensive sanding operations a shower/bath and hair wash
is advised.
Gurit produces a separate full Safety Data Sheet for all
hazardous products. Please ensure that you have the correct
SDS to hand for the materials you are using before
commencing work. A more detailed guide for the safe use of
Gurit resin systems is also available from Gurit, and can be
found on our website at www.gurit.com
APPLICABLE RISK & SAFETY
PHRASES
Please refer to product SDS for up to date information specific
to this product.
8 PDS-TPrime130-1-6-0520
TRANSPORT & STORAGE
The resin and hardener should be kept in securely closed containers during transport and
storage. Any accidental spillage should be soaked up with sand, sawdust, cotton waste or any
other absorbent material. The area should then be washed clean (see appropriate Safety Data
Sheet).
Adequate long term storage conditions will result in a shelf life of 12 months for both the resin
and hardener. Storage should be in a warm dry place out of direct sunlight and protected from
frost. The temperature should be between 10 C and 25 C. Containers should be firmly
closed. Hardeners, in particular, will suffer serious degradation if left exposed to air. The
materials should be stirred before use.
NOTICE
All advice, instruction or recommendation is given in good faith but the selling Gurit entity (the
Company) only warrants that advice in writing is given with reasonable skill and care. No further duty
or responsibility is accepted by the Company. All advice is given subject to the terms and conditions
of sale (the Conditions) which are available on request from the Company or may be viewed at
Gurit s Website: www.gurit.com/terms-and-conditions.aspx
The Company strongly recommends that Customers make test panels in the final process
conditions and conduct appropriate testing of any goods or materials supplied by the Company prior
to final use to ensure that they are suitable for the Customer s planned application. Such testing
should include testing under conditions as close as possible to those to which the final component
may be subjected. The Company specifically excludes any warranty of fitness for purpose of the
goods other than as set out in writing by the Company. Due to the varied nature of end-use
applications, the Company does, in particular, not warrant that the test panels in the final process
conditions and/or the final component pass any fire standards.
The Company reserves the right to change specifications and prices without notice and Customers
should satisfy themselves that information relied on by the Customer is that which is currently
published by the Company on its website. Any queries may be addressed to the Technical Services
Department.
Gurit is continuously reviewing and updating literature. Please ensure that you have the current
version by contacting your sales contact and quoting the revision number in the bottom right-hand
corner of this page.
TECHNICAL CONTACT INFORMATION
For all other enquiries such as technical queries:
Telephone + 44 1983 828000 (08:30 17:00 GMT)
Email technical.support@gurit.com
24-HOUR CHEMICAL EMERGENCY NUMBER
For advice on chemical emergencies, spillages, fires or exposures:
Europe +44 1273 289451
Americas +1 646 844 7309