Method State
Weight Resin
Volume Hardener
Property
Hardness
Compression Yield 7,770
Tensile Strength 5,330
Tensile Modulus 2.80E+05
Tensile Elongation
Flexural Strength 9,540
Flexural Modulus 2.97E+05
Lap Shear on 1018 Steel 2,880
Lap Shear on 2024T Aluminum 2,860
Tensile Adhesion to 1018 Steel 4,300
Tensile Adhesion to 2024T Aluminum 3,410
Property
Tg DSC Onset 1st Heat 129(54)
Heat Deflection Temperature 118(48)
2015 Gougeon Brothers, Inc.
72 F (22 C)
HANDLING PROPERTIES
Technical Data
Property Standard Units
100g Pot Life ASTM D2471minutes 27-33
Working Time (1/2″ bead)ASTM D2471minutes 81-99
Minimum Cure Temp ASTM D2196 F ( C) 60 (16)
MIX RATIO DENSITY
72 F (22 C)
2.24:1 100:44.6 lb/gal (g/cc)9.76 (1.17)
MECHANICAL PROPERTIES
SUPER-TOUGHENED
ADHESIVE EPOXY
Resin:HardenerResin:Hardener Units
2.00:1 100:50.0 lb/gal (g/cc)8.76 (1.05)
Standard Units 72 F (22 C) x 2 wk
ASTM D2240 Type D 80
ASTM D695 psi (MPa) (54)
ASTM D638 psi (MPa) (37)
ASTM D638 psi (GPa) (1.93)
ASTM D638 % 10.1
ASTM D790 psi (MPa) (66)
ASTM D790 psi (GPa) (2.05)
ASTM D1002psi (MPa) (20)
ASTM D1002psi (MPa) (20)
ASTM D4541psi (MPa) (30)
ASTM D4541psi (MPa) (24)
ASTM D648 F ( C)
1
Store PRO-SET Epoxy resins and hardeners at room temperature in sealed containers until shortly before use. As with many
high-performance epoxy resins, repeated exposure to low temperatures during storage may cause the resin to crystallize. If this
occurs, warm the resin to 125 F and stir to dissolve crystals. Hardeners may form carbamation when exposed to CO
2 and
moisture in the atmosphere for extended periods of time. Prevent carbamation by protecting hardeners from exposure until
immediately prior to processing.
Test specimens were neat epoxy (without fiber reinforcement).
Typical values, not to be construed as specification.
Rev 4 / Dec 2015
THERMAL PROPERTIES
Standard Units 72 F (22 C) x 2 wk
ASTM E1356 F ( C)
COMBINED FEATURES
Shear thinning resins and hardeners are
thixotropic gels. The mixture fills gaps and will not
sag on vertical surfaces. The material wets out the
substrate, making priming or pre-wetting
unnecessary on most surfaces, while ensuring a
good bond.
Slow cure speed hardener provides
approximately 90 minutes of working time at 72 F
(22 C).
Room temperature cure properties suitable for
many composite components and structures.
High performance pre-thickened, two-part epoxy
adhesive delivers toughness and superior peel
strength for heavily loaded applications and
difficult to bond substrates including pre-preg,
SMC, metals and most plastics. Also for
secondary bonding of laminated composites, steel,
aluminum, cast iron, concrete, stone, and most
wood species. PRO-SET Adhesive bonds these
material in any combination.
Coverage one cartridge set dispenses
approximately 47′ of 1/4″ bead, or 17′ of 1/2″ bead
and will cover approximately 7 sq ft when spread
with a 1/8″ x 1/8″ notched spreader, or 12 sq ft
with a 1/16″ x 1/16″ notched spreader.
Shelf life is 18 months for resin and 18 months for
hardener when properly stored
1
.
ADV-176
ADV-276