Property Standard Units 77 F (25 C)85 F (29 C)
150g Pot Life ASTM D2471minutes 24-30 18-24
500g Pot Life ASTM D2471minutes 22-28 18-22
Viscosity MixedASTM D2196 cP 241 188
Viscosity (resin)ASTM D2196 cP
Viscosity (hardener)ASTM D2196 cP
Method Resin:Hardener
COMBINED FEATURES Weight 3.65:1
Weight Range 3.92:1 3.56:1
Volume 3.00:1
Volume Range 3.23:1 2.94:1
State Units 72 F (22 C)
Cured lb/gal (g/cc)9.53 (1.14)
Resin lb/gal (g/cc)9.49 (1.14)
Hardener lb/gal (g/cc)7.82 (0.94)
2015 Gougeon Brothers, Inc.
Rev 3 / Dec 2015
Test specimens were neat epoxy (without fiber reinforcement).
Typical values, not to be construed as specification.
VISCOSITY VS TEMPERATURE
DENSITY
100:25.5 100:28.1
100:30.9 100:34.0
100:33.3
100:27.4
Resin:Hardener
1433
16
INFUSION EPOXY
MIX RATIO
304
HANDLING PROPERTIES
Technical Data
72 F (22 C)
28-36
27-33
Very low viscosity for rapid saturation of
fiberglass, Kevlar and carbon fiber laminate
with resin infusion and VARTM processes.
Fast cure speed hardener provides
approximately 75 to 90 minutes of working
time at 77 F (25 C). A typical laminate will be
gelled in 2 to 3 hours.
This combination is formulated specifically
for resin infusion and VARTM processes. Do
not use in open mold applications.
Room temperature cure properties suitable
for many composite components and
structures.
T
g as high as 197 F (92 C) with proper post
cure providing excellent temperature stability
and great part cosmetics.
Cost effective, high performance epoxy
formulation for synthetic composite
manufacturing.
Quality-control tinting is available at no extra
charge; simply add “QC” after the product
code on your order.
Shelf life is 3 years for resin and 2 years for
hardener when properly stored
3
.
0
100
200
300
400
500
600
50 60 70 80 90 100110120130
Viscosity (cP)
Temperature ( F)
INF-114
INF-210
Hardness ASTM D2240Type D
Compression Yield ASTM D695psi (MPa)
Tensile Strength ASTM D638psi (MPa)
Tensile Modulus ASTM D638psi (GPa)
Tensile Elongation ASTM D638 %
Flexural Strength ASTM D790psi (MPa)
Flexural Modulus ASTM D790psi (GPa)
Tg DMA Peak Tan Delta ASTM E1640
1
F ( C)
Tg DMA Onset Storage ModulusASTM E1640
1
F ( C)
Tg DSC Onset 1st Heat ASTM E1356 F ( C)
Heat Deflection TemperatureASTM D648 F ( C)
Tg DSC Ultimate ASTM E1356 F ( C)
Rev 3 / Dec 2015
2015 Gougeon Brothers, Inc.
185 (85)
1
1 Hz, 3 C per minute.
2
Additional post cure may be required; contact Technical Department for details.
Test specimens were neat epoxy (without fiber reinforcement).
Typical values, not to be construed as specification.
3
Store PRO-SET Epoxy resins and hardeners at room temperature in sealed containers until shortly before use. As with many high-
performance epoxy resins, repeated exposure to low temperatures during storage may cause the resin to crystallize. If this occurs, warm the
resin to 125 F and stir to dissolve crystals. Hardeners may form carbamation when exposed to CO
2 and moisture in the atmosphere for
extended periods of time. Prevent carbamation by protecting hardeners from exposure until immediately prior to processing.
185 (85)
134 (57) 136 (58) 153 (67) 164 (73) 175 (79)
148 (64) 146 (63) 166 (75) 182 (83) 197 (92)
141 (61) 142 (61) 168 (76) 176 (80)
(3.37)4.90E+05
77 F (25 C)
x 2 wk
RT Gelation
+ 120 F (49 C)
x 8 hrs
RT Gelation
+ 140 F (60 C)
x 8 hrs
RT Gelation
+ 180 F (82 C)
x 8 hrs
165 (74) 167 (75) 191 (88) 204 (96) 217 (103)
15,900(110) 18,600
THERMAL PROPERTIES
Property Standard Units
72 F (22 C)
x 4 wk
4.89E+05
4.56E+05(3.14)
2.0 2.6 4.7 4.9 5.7
(3.38)4.69E+05(3.23)
(128) 18,800(130) 19,300(133)
4.83E+5(3.33) 5.28E+5(3.64)
13,500(93)
5.57E+5(3.84) 5.2E+5(3.59)5.06E+05(3.49)4.96E+05(3.42)
(103) 15,000(103)
8,670(60) 10,100(70) 11,000(76) 11,000(76) 11,300(78)
RT Gelation
+ 140 F (60 C)
x 8 hrs
RT Gelation
+ 180 F (82 C)
x 8 hrs
86 86 86
Property Standard Units
72 F (22 C)
x 4 wk
77 F (25 C)
x 2 wk
86 86
14,700(101) 16,000(110) 14,800(102) 14,900
INF-114~INF-210
INFUSION EPOXY
MECHANICAL PROPERTIES
RT Gelation
+ 120 F (49 C)
x 8 hrs