Property Standard Units 77 F (25 C)85 F (29 C)
150g Pot Life ASTM D2471minutes 235-289 163-207
500g Pot Life ASTM D2471minutes 157-193 121-149
Viscosity MixedASTM D2196 cP 255 189
Viscosity (resin)ASTM D2196 cP
Viscosity (hardener)ASTM D2196 cP
Method Resin:Hardener
Weight 3.65:1
Weight Range 3.77:1 3.41:1
Volume 3.00:1
Volume Range 3.11:1 2.81:1
State Units 72 F (22 C)
Cured lb/gal (g/cc)9.54 (1.14)
Resin lb/gal (g/cc)9.49 (1.14)
Hardener lb/gal (g/cc)7.82 (0.94)
2015 Gougeon Brothers, Inc.
HANDLING PROPERTIES
Technical Data
72 F (22 C)
381-467
204-250
325
1433
13
INFUSION EPOXY MIX RATIO
Resin:Hardener
100:27.4
100:26.5 100:29.3
100:32.2 100:35.6
100:33.3
DENSITY
Rev 3 / Dec 2015
Test specimens were neat epoxy (without fiber reinforcement).
Typical values, not to be construed as specification.
VISCOSITY VS TEMPERATURE
COMBINED FEATURES
Very low viscosity for rapid saturation of
fiberglass, Kevlar and carbon fiber laminate
with resin infusion and VARTM processes.
Extra slow cure speed hardener provides up
to 10 hours of working time at 77 F (25 C). A
typical laminate will be gelled in approximately
14 to 18 hours at this temperature.
This combination is formulated specifically
for resin infusion and VARTM processes. Do
not use in open mold applications.
Room temperature cure properties suitable
for many composite components and
structures.
T
g as high as 193 F (89 C) with proper post
cure providing excellent temperature stability
and great part cosmetics.
Cost effective, high performance epoxy
formulation for synthetic composite
manufacturing.
Quality-control tinting is available at no extra
charge; simply add “QC” after the product
code on your order.
Shelf life is 3 years for resin and 2 years for
hardener when properly stored
3
.
0
100
200
300
400
500
600
50 60 70 80 90 100 110 120 130
Viscosity (cP)
Temperature ( F)
INF-114
INF-213
Hardness ASTM D2240Type D
Compression Yield ASTM D695psi (MPa)
Tensile Strength ASTM D638psi (MPa)
Tensile Modulus ASTM D638psi (GPa)
Tensile Elongation ASTM D638 %
Flexural Strength ASTM D790psi (MPa)
Flexural Modulus ASTM D790psi (GPa)
Tg DMA Peak Tan Delta ASTM E1640
1
F ( C)
Tg DMA Onset Storage ModulusASTM E1640
1
F ( C)
Tg DSC Onset 1st Heat ASTM E1356 F ( C)
Heat Deflection TemperatureASTM D648 F ( C)
Tg DSC Ultimate ASTM E1356 F ( C)
Rev 3 / Dec 2015
2015 Gougeon Brothers, Inc.
INF-114~INF-213
INFUSION EPOXY
MECHANICAL PROPERTIES
RT Gelation
+ 140 F (60 C)
x 8 hrs
RT Gelation
+ 180 F (82 C)
x 8 hrs
86 86 86 86
Property Standard Units
72 F (22 C)
x 4 wk
77 F (25 C)
x 2 wk
RT Gelation
+ 120 F (49 C)
x 8 hrs
86
15,000(103) 15,100(104) 14,000(97) 14,000(97) 14,000(97)
7,900(54) 8,410(58) 9,600(66) 9,800(68) 10,100(70)
5.4E+5(3.72) 5.38E+5(3.71)4.95E+05(3.41)4.66E+05(3.21)4.99E+05(3.44)
1.8 1.9 4.2 4.2 4.2
(3.32)4.56E+05(3.14)
(111) 16,200(112) 16,300(112)
4.74E+5(3.27) 4.7E+5(3.24)
11,900(82) 13,000(90) 16,100
THERMAL PROPERTIES
Property Standard Units
72 F (22 C)
x 4 wk
4.86E+05(3.35)4.81E+05
77 F (25 C)
x 2 wk
RT Gelation
+ 120 F (49 C)
x 8 hrs
RT Gelation
+ 140 F (60 C)
x 8 hrs
RT Gelation
+ 180 F (82 C)
x 8 hrs
155 (68) 156 (69) 177 (81) 197 (92) 213 (100)
190 (88)
1
1 Hz, 3 C per minute.
2
Additional post cure may be required; contact Technical Department for details.
3
Store PRO-SET Epoxy resins and hardeners at room temperature in sealed containers until shortly before
use. As with many high-performance epoxy resins, repeated exposure to low temperatures during storage
may cause the resin to crystallize. If this occurs, warm the resin to 125 F and stir to dissolve crystals.
Hardeners may form carbamation when exposed to CO
2 and moisture in the atmosphere for extended periods
of time. Prevent carbamation by protecting hardeners from exposure until immediately prior to processing.
182 (83)
125 (52) 129 (54) 131 (55) 153 (67) 170 (77)
143 (62) 144 (62) 155 (68) 177 (81) 193 (89)
132 (56) 135 (57) 147 (64) 161 (72)