by | Sep 27, 2025
Technical Datasheet – METYX USA Reinforcements
PRODUCT CODE
PRODUCT NAME BA-E 1700
PRODUCT DESCRIPTION +45 /-45 BIAXIAL
CUSTOMER CODE
CUSTOMER ID
REINFORCEMENT CONSTRUCTION
LAYER FIBER TYPE AREA WEIGHT
1 +45 600Tex E-glass 8.90 oz/yd
2
2 0 68Tex E-glass 0.03 oz/yd
2
3 90 68Tex E-glass 0.03 oz/yd
2
4 -45 275Tex E-glass 8.90 oz/yd
2
5 CSM E-glass
6 Stitch 76dtex PES 0.2 oz/yd
2
7
8
9
* Measurement method based on ISO 3374 . TOTAL*18.06oz/yd
2
( %3)
OTHER PORPERTIES ROLL INFO
Stitch Gauge Roll Width
Stitch Type Tricot Roll Weight
Stitch Length Roll Length
Pilot Yarn / Position NONE Core Diameter 3 in
Resin Compatibility Loss on Ignition Moisture Content
Polyester, Vinylester, Epoxy resins Max.%0,70 by weight (ISO 1887) Max.%0,20 by weight (ISO 3344)
Packaging
All rolls are wrapped with polyethylene bags; placed in pallet boxes or in single cardboard boxes or in pyramid
style on pallets.
Labelling
Each roll is labelled on the inner side of the core, on the bag or on the cardboard boxes including a unique
reference number for its traceability.
Storage
Store at %40-70 relative humidity and 64 -86 F (18 -30 C) temperature range. Recommended to be
brought to work area 24 hrs prior to use.
System Certification Product Certification
METYX products are produced by METYX USA company who is run by
ISO 9001:2015 QA System.
DNV-GL Approved
2504 Lowell Road Gastonia NC 28054
Phone : +1-704-824-1030 Fax : +1-704-824-1031 Web : www.metyx.com
FR-159-2/14.08.2018
by | Sep 27, 2025
SIL66BE-249ALH
Laminating Resin
(Surf/Sail Board)
Technical Data Sheet
INTERPLASTIC CORPORATION
3535 Latonia Avenue
Fort Wright, KY 41015-0159
859.292.7400Fax: 859.292.7424
www.interplastic.com
SIL66BE-249ALH is a surfboard laminating resin containing 35% maximum styrene. It contains
UV stabilizer and does not contain wax.
TYPICAL RESIN PROPERTIES @ 77 F RESULTS
Brookfield Viscosity @ 20 rpm, cps 410 560
Brookfield Spindle No. (RV) 2
Catalyst, %, DDM-9 MEK-P 1.00
Gel Time, minutes:seconds 11:00 19:00
Gel to Peak Time, minutes:seconds 9:00 19:00
Peak Exotherm, F 275 315
Solids, % 65.0 68.0
UV Test Positive
MECHANICAL PROPERTIES OF NEAT CURED RESIN RESULTS
Property:
ASTM Test Method
Psi Mpa
Flexural Strength D-790 20,200 139.3
Flexural Modulus D-790 5.85 x 10
5
4033
Tensile Strength D-638 10,500 72.4
Tensile Modulus D-638 6.17 x 10
5
4254
Tensile Elongation D-638 2.1 %
Heat Distortion Temperature D-648 149 F / 65.0 C
Hardness, Barcol 934-1 D-2583 42 – 44
Revised: 7/06
All specifications and properties specified above are approximate. Specifications and properties of material delivered may vary slightly from
those given above. Interplastic Corporation makes no representations of fact regarding the material except those specified above. No person
has any authority to bind Interplastic Corporation to any representation except those specified above. Final determination of the suitability of
the material for the use contemplated is the sole responsibility of the Buyer. The Thermoset Resins Division’s technical sales representatives
will assist in developing procedures to fit individual requirements.
by | Sep 27, 2025
Property Standard Units
150g Pot Life ASTM D2471minutes
500g Pot Life ASTM D2471minutes
Viscosity MixedASTM D2196 cP
Viscosity (resin)ASTM D2196 cP
Viscosity (hardener)ASTM D2196 cP
COMBINED FEATURES Method Resin:Hardener
Weight 3.70:1
Weight Range 3.80:1 – 3.50:1
Volume 3.00:1
Volume Range 3.08:1 – 2.84:1
State Units 72 F (22 C)
Cured lb/gal (g/cc)9.60 (1.15)
Resin lb/gal (g/cc)9.69 (1.16)
Hardener lb/gal (g/cc)7.85 (0.94)
2018 Gougeon Brothers, Inc.
180
120
600
HANDLING PROPERTIES
Technical Data
72 F (22 C)
Resin:Hardener
2,500
35
HIGH-TEMP INFUSION EPOXYMIX RATIO
100:33.3
100:32.4 – 100:35.2
100:27.0
100:26.3 – 100:28.5
DENSITY
Rev 1 / April 2018
Test specimens were neat epoxy (without fiber reinforcement).
Typical values, not to be construed as specification.
VISCOSITY VS TEMPERATURE
High-temperature, high-performance epoxy
formulation for synthetic composite mold and
tooling manufacture.
T
g as high as 300 F (149 C) with proper post
cure. Provides excellent temperature stability
and great part cosmetics.
Slow cure speed hardener provides 5 to 6
hours of working time at 72 F (22 C). A typical
laminate will gel in 10 to 12 hours at room
temperature.
This combination is specifically formulated
for resin infusion and VARTM processes. Not
for use in open mold applications.
Elevated temperature cure is required.
Parts can be pulled after 24-48 hours at room
temperature or sooner after a mild initial cure
of 90-110 F (32- 43 C). Post cure 140 F (60 C)
x 2hr + 275 F (135 C) x 12hr, with ramp rates
no greater than 15 C/hour, to achieve
maximum properties.
Quality-control tinting is available at no extra
charge; simply add “QC” after the product
code on your order.
Shelf life is 3 years for resin and 18 months
for hardener when properly stored
2
.
HTP 180
HTP 280
0
200
400
600
800
1000
1200
1400
5060708090100110120130
Viscosity
(cP)
Temperature ( F)
Hardness ASTM D2240 Type D
Compression Yield ASTM D695 psi (MPa)
Tensile Strength ASTM D638 psi (MPa)
Tensile Modulus ASTM D638 psi (GPa)
Tensile Elongation ASTM D638 %
Flexural Strength ASTM D790 psi (MPa)
Flexural Modulus ASTM D790 psi (GPa)
Tg DMA Peak Tan Delta ASTM E1640
1
F ( C)
Tg DMA Onset Storage ModulusASTM E1640
1
F ( C)
Tg DSC Onset 1st Heat ASTM E1356 F ( C)
Heat Deflection TemperatureASTM D648 F ( C)
Rev 1 / April 2018
2018 Gougeon Brothers, Inc.
MECHANICAL PROPERTIES
HTP 180~HTP 280
HIGH-TEMP INFUSION EPOXY
10,800(74)
Property Standard Units
RT + 140 F (60 C) x 2hr +
275 F (135 C) x 12hr
94
15,300(105)
17,800(123)
4.14E+05(2.85)
4.34E+05(2.99)
5.5
THERMAL PROPERTIES
1
1 Hz, 3 C per minute.
2
Store PRO-SET Epoxy resins and hardeners at room temperature in sealed containers until shortly before use. As
with many high-performance epoxy resins, repeated exposure to low temperatures during storage may cause the resin
to crystallize. If this occurs, warm the resin to 125 F and stir to dissolve crystals. Hardeners may form carbamation
when exposed to CO
2 and moisture in the atmosphere for extended periods of time. Prevent carbamation by protecting
hardeners from exposure until immediately prior to processing.
Property Standard Units
RT + 140 F (60 C) x 2hr +
275 F (135 C) x 12hr
320 (160)
304 (151)
304 (151)
282 (139)
by | Sep 27, 2025
TECHNICAL DATA SHEE T
BR100
RELEASE FABRIC
Aerovac
955-10 National Parkway
Schaumburg, IL 60 173
USA
TDS BR100_02.21_Issue1
BR100
Release fabric
Ideally suited to resin rich applications
Features and Benefits
Fluorocarbon coated, light weight, porous nylon
fabric.
Release coating ensures easier stripping of the
fabric from resin rich composites.
Tight weave construction gives close control of resin
bleed.
The material is supplied pink in colour for
identification purposes.
When using release fabrics on composite laminates
that will be subject to secondary bonding or painting
operations, there is a potential for minor transfer onto
the component, despite the release solution being fully
polymerised.It is therefore recommended that prior to
bonding or painting the laminate should be suitably
prepared (industry standard method is preparation by
slight abrading or sanding the surface followed by
cleaning with an approved solvent).
PROPERTIES
Maximum cure temperature 204 C 400 F
Color Pink
Fabric type Nylon
Fabric weight 60g/m 1.77oz/yd
Release coating Fluorocarbon
AVAILABILITY
Standard width 1.52m 60in
Standard length 100m 109yd
Slit widths available
STORAGE
No special storage conditions required.
HEALTH & SAFETY
Please refer to the product MSDS for safe handling, personal protective equipment recommendations and disposal
considerations.
DISCLAIMER: The data and information provided in this document have been obtained from carefully controlled samples and are considered to be
representative of the product described. Aerovac does not express or imply any guarantee or warranty of any kind including, but not limited to, the accuracy, the
completeness or the relevance of the data and information set out herein. Because the properties of this product can be significantly affected by the fabrication
and testing techniques employed, and since Aerovac does not control the conditions under which its products are tested and used, Aerovac cannot guarantee
the properties provided will be obtained with other processes and equipment. No guarantee or warranty is provided if the product is adapted for a s pecific use or
purpose. Aerovac declines any liability with respect to the use made by any third party of the data and information contained herein. Aerovac has the right to
change any data or information when deemed appropriate. All trademarks are the property of their respective owners. 2021 , Aerovac. All rights reserved.
by | Sep 27, 2025
TECHNICAL DATA SHEE T
B4444
RELEASE FABRIC
Aerovac
955-10 National Parkway
Schaumburg, IL 60 173
USA
TDS B4444_02 .21_Issue1
B4444
Release fabric
Ideally suited to medium temperature applications
Features and Benefits
Silicone coated lightweight nylon fabric.
Coated with heat cured silicone release solution, to
aid removal from the cured laminate.
Phenolic resins are known to adhere to nylon release
fabrics, and it is therefore recommended that the
customer conduct their own internal compatibility
tests.
When using release fabrics on composite laminates
that will be subject to secondary bonding or painting
operations, there is a potential for minor transfer onto
the component, despite the release solution being fully
polymerised.It is therefore recommended that prior to
bonding or painting the laminate should be suitably
prepared (industry standard method is preparation by
slight abrading or sanding of the surface followed by
cleaning with an approved solvent).
PROPERTIES
Maximum cure temperature 204 C 400 F
Color Green
Fabric type Nylon
Fabric weight 60g/m 1.77oz/yd
Release coating Silicone
AVAILABILITY
Standard width 1.47m 58in
Standard length 100m 109yd
Slit widths available
STORAGE
No special storage conditions required.
HEALTH & SAFETY
Please refer to the product MSDS for safe handling, personal protective equipment recommendations and disposal
considerations.
DISCLAIMER: The data and information provided in this document have been obtained from carefully controlled samples and are considered to be
representative of the product described. Aerovac does not express or imply any guarantee or warranty of any kind including, but not limited to, the accuracy, the
completeness or the relevance of the data and information set out herein. Because the properties of this product can be significantly affected by the fabrication
and testing techniques employed, and since Aerovac does not control the conditions under which its products are tested and used, Aerovac cannot guarantee
the properties provided will be obtained with other processes and equipment. No guarantee or warranty is provided if the product is adapted for a s pecific use or
purpose. Aerovac declines any liability with respect to the use made by any third party of the data and information contained herein. Aerovac has the right to
change any data or information when deemed appropriate. All trademarks are the property of their respective owners. 2021 , Aerovac. All rights reserved.
by | Sep 27, 2025
A Quality Product from Hawkeye Industries, Inc.
Duratec
904-001 Hi-Gloss Additive
Duratec 904-001 has a 20
year history of successful
use, blended with numerous
gelcoats across North America
and Europe.
A superior product to blend
with Gelcoat to create a
repair coating.
Can be blended with Tooling
gelcoat to reduce porosity
and improve the surface
quality.
Features
Contains Air-cure resins and
additives eliminate the use
of wax and PVA creating a
superior finish.
o Makes gelcoat spray
like paint
o Can be blended 50:50 for
or 25:75 to
flow and surface
needs wax)
Eliminate low-gloss areas
on the edges of repairs the
low-gloss donut often seen in
gelcoat repairs.
Reduce Porosity in tooling
gelcoat. Improves air release
thus preventing porosity.
Better profile: as compared to
un-modified gelcoat or
gelcoat with wax and styrene.
o Easy to spray from HVLP
Guns.
Greatly reduced yellowing:
Gelcoat patched with Styrene
and Wax
Contains special additives to
prevent UV-induced yellowing
and gloss loss.
Faster and Easier Repair:
The air-cure blend created
with Duratec 904-001 and
gelcoat cures fast and hard,
creating a shiny smooth
surface that is easy to sand.
o Faster Repair
o Eliminate the gummy
seen with wax
and styrene
o Prevent the dull surface
seen with wax/gelcoat
blends
Hi-Gloss Additive
904-001
Limited/ warranty statement: Our products are intended for sale to industrial and commercial customers. We request that customers inspect and test our
products before use and satisfy themselves as to contents and suitability. Nothing herein shall constitute a warranty, expressed or implied, including any
warranty of merchantability or fitness, nor is protection from any law or patent to be inferred. All patent rights are reserved. The exclusive remedy for all
proven claims is replacement of our materials and in no event shall we be liable for special, incidental or consequential damages.
P.O.Box
(USA) (Outside
Email: hawkeyesales@hawkeyeind.com .duratec1.com
904-001
Duratec
Hi-Gloss Additive
Physical Properties:
Recommended Use:
Gelcoat Repair
1. A test blend is recommended, as every blend is unique and the cure must be tested and assured.
The cure time of the blend will vary, as every gelcoat is different. Note the cup-gel time.
2. Remove any cracked or damaged gelcoat. Grind out cracks down to the laminate.
3. Repair laminate or assure the laminate is sound.
4. The temperature should be at least 60 F. Low temperatures extend cure times.
5. Sand with 180 grit to a few inches outside the repair area.
a. Bevel the edge of the existing gelcoat.
b. Use a repair putty (like Duratec 1810-013 Marine Fairing Putty) to fill in any low areas
6. Blend One: 1 part (25%) Duratec 904-001 and 3 parts (75%) gelcoat.
a. Catalyze with 2% 50% MEKP catalyst like Norox 925 (about 20 milliliters per quart. Note: the 1:3 blend is
to maximize the hide (opacity). If opacity is not an issue, use Blend Two for all the repairs.
b. Spray 3-4 passes over the repair, building up 12-15 mils. Allow at least two minutes between passes. Do not
allow the Duratec/gelcoat blend to cure beyond the sticky/thumbprint stage between coats .usually about
30 minutes at 77 F when sprayed, faster in the cup.
7. Blend two:
a. 1 part Duratec 904-001 and one part gelcoat. Catalyze with 2% of a 50% MEKP catalyst like Norox 925H.
b. Spray at least 2 passes over the repair, building up a additional 8 mils or more. Be sure to get back onto the
first passes while they are sticky. Cover all the previously coated area. It is possible to feather the edge of the
repaired area with the second blend.
8. Allow to cure completely.
9. Sand with the finest grit that is reasonable for the surface finish. With a good finish starting with 400 grit is possible.
a. The surface must be open for at least 8 hours between initial sanding and polishing. The open time allows for
styrene release and full cure.
10. Sand with progressively finer grits like 400, 600, 800, 1000, Compound and polish with products formulated for
gelcoat like Aqua Buff 1000 and Aqua Buff 2000.
Tooling Gelcoat Upgrade:
Blend 10-25% Duratec 904-001 into the tooling gelcoat to improve the flow and spraying characteristics of tooling gelcoat.
Catalyze with 2% MEKP catalyst (as recommended by the gelcoat supplier)
Revised 02-03-14
Limited/ warranty statement: Our products are intended for sale to industrial and commercial customers. We request that customers inspect and test our
products before use and satisfy themselves as to contents and suitability. Nothing herein shall constitute a warranty, expressed or implied, including any
warranty of merchantability or fitness, nor is protection from any law or patent to be inferred. All patent rights are reserved. The exclusive remedy for all
proven claims is replacement of our materials and in no event shall we be liable for special, incidental or consequential damages.
Data Sheet
Continued
Page: 2
by | Sep 27, 2025
TECHNICAL DATASHEET
SAP No. 30015059 Article Description X-S-E-889g/m -1270mm
Textile Structure 7010538 SAERTEX
ARTICLE CONSTRUCTION (in accordance with EN 13473-1)
Layer Construction Areal weight Tolerance Material
3 CSM 275 g/m +/- 10,0 % Boron free glass
2 45 301 g/m +/- 5,0 % E-glass 600 TEX
1 -45 301 g/m +/- 5,0 % E-glass 600 TEX
Stitching
Stitching 2
6 g/m
6 g/m
+/- 1 g/m
+/- 1 g/m
PES [Polyester] 76 dtex
PES [Polyester] 76 dtex
Fiber input can be determined individually
FURTHER CHARACTERISTICS
Gauge 5,0 Stitching pattern warp Width (nominal) 1270 mm
Stitching pattern 2 tricot
Stitch length 3,00 mm Total tolerance 6,6 % Total areal weight 889 g/m
Labelling (Standard) Every roll is equipped with a label in the core. A further label is located outside on
the foil or on the box.
Packaging (Standard) Every roll is wound on a cardboard core and wrapped in foil. Further packaging
options can be determined individually.
Storage Keep in original packaging. Store in a dry environment. Avoid direct sunlight.
(recommendation) Fabrics to be kept under processing conditions at least 24 hours
prior to use to avoid problems with humidity and electrostatic charge.
– Confidential Information –
SAERTEX USA, LLC. has been certified in accordance with ISO 9001:2015.
REINFORCING YOUR IDEAS
by | Sep 27, 2025
PRODUCT PROPERTIES
All time calculations are based on temperatures of 77 F, 25 C
Lab tested with Norox 925 MEKP
Viscosity, #2 spindle, RVF, 20 rpm
1500 – 1900 cps
Thixotropic Index
min. 3.8
Gel time @ 2% MEKP
15-20 minutes
Weight per gallon
10.94 lbs/gal (approx)
Coverage per gallon @ 20 mils 80 sq. feet
KEY USES
Light-weight replacement
for gelcoat in fabricated
parts such as paddlesports
or automotive components.
Composite plugs & patterns.
Cabinets and
furniture
Marine and aircraft interiors
B-Sides for improved finish
Designed to level and flow across your mold surface, the Duratec White HV Hi-
Gloss coating will elevate your finished part surface and improve durability over
standard gelcoats or polyesters. Compatible with polyester, vinyl ester, and epoxy
laminates.
FEATURES
EASY TO APPLY
Sprayable and quick building,
to10-15 mils, 250-375 microns
thickness.
HIGH GLOSS
Sands easily and polishes to a
non-wax, tackfree high gloss
finish.
RESISTS FISHEYES
Unique additives reduce the risk of
fisheyes and pinholes during the
spray application.
ULTIMATE DURABILITY
Coating produced a hard, durable
surface with fantastic scratch
resistance for high-use areas.
COMPATIBILITY
Compatible with wood, polyester,
vinyl ester, and most epoxy
substrates.
DURATEC SOLID
WHITE HI-GLOSS
COATING
PRODUCT # 614-075
SAFETY & HA
NDLING
Duratec White HV Hi-Gloss Coating is
extremely flammable. Do not apply near
sparks, open flames or heat. Keep area ventilated. Do not smoke. Avoid
continuous breathing of
vapor. Duratec White HV Hi-Glo ss Coating contains
ingredients
which could be harmful if mishandled. Contact with skin and eyes
should be avoided and necessar
y protective equipment and clothing should be
worn. Individuals should wash
with soap and water before eating or drinking. All
containers should be
properly labeled to prevent accidental ingestion or improper
disposal. Individuals should re
seal any partly used material back in the container.
Store under cool, dry conditions
and away from open flames and high
temperatures.
For more detailed instructions on
storage, please see the MSDS sheet.
Liability/warranty statement: Our products are intended for sale to industrial and commercial customers. We request that
customers inspect and test our products before use and satisfy themselves as to contents and suitability. All claim requests
must be made in writing and are subject to review, including storage temperature verification and retain evaluations. The
e
xclusive remedy for all proven claims is replacement of our materials. In no event shall we be liable for special, incidental
or
consequential damages, including damages caused in transit (exworks terms). Nothing herein shall constitute a warranty,
e
xpressed or implied, including any warranty of merchantability or fitness, nor is protection from any law or patent to be
inferred. All patent and trademark rights are reserved.
DESCRIPTION
909-546-1160
hawkeyesales@hawkeyeind.com
PO BO X 415,
BLOOMINGTON, CA 92 316
WWW.HAWKEYEIND.COM
REVISED JULY 2021
REVISED JUNE 2024
DURATEC SOLID WHITE
HI-GLOSS COATING
AP
P LIC ATION G UID E | PR ODUC T
#
614-075
The following use instructions are broad to address multiple applications. We recommend testing for product
compatability with your process. Please contact our Tech Team at (909) 546-1160 with any questions.
PLEASE NOTE
WWW.HAWKEYEIND.COM 909-546-1160 HAWKEYESALES@HAWK
EYEIND.COM PO BOX 415, BLOOMINGTON, CA 92316
Liability/warranty statement: Our products are intended for sale to industrial and commercial customers. We request that customers inspect and test our products before use and satisfy
themselves as to contents and suitability. All claim requests must be made in writing and are subject to review, including storage temperature verification and retain evaluations. The
exclusive remedy for all proven claims is replacement of our materials. In no event shall we be liable for special, incidental or consequential damages, including damages caused in transit
(exworks terms). Nothing herein shall constitute a warranty, expressed or implied, including any warranty of merchantability or fitness, nor is protection from any law or patent to be
inferred. All patent and trademark rights are reserved.www.hawkeyeind.com
Prepare & Catalyze
Temperature should be at least 64 F for both the product and the part.
Mix with either a paint shaker or a drill-mounted mixer. A paint stir stick will not be enough for a proper mix.
Catalyze the Duratec at 2.0 % by weight with a full strength MEKP, like Norox 925.
Catalyze only an
amount that can be sprayed in 15 minutes, typically about a quart if using a HVLP spray gun. Mix well.
Apply
Duratec HV Hi-Gloss Coating should be applied by spraying. We recommend HVLP air-assisted spray guns.
Epoxy laminates should be washed with clean water and a heavy duty scrub sponge before and after
sanding. It is not necessary to water wash polyester, vinyl ester, or wood substrates. Abrade the entire
substrate surface with 180-grit to ensure proper mechanical adhesion. Wipe with a clean cloth. Do not use a
tack rag.
A
2.0-2.5 mm tip is recommended. Use 34-40 psi air pressure (at the gun). Adjust the needle and fan to
provide the proper spray. Use the lowest pressures possible to minimize orange peel.
The first coat should be a light dust coat. The dust coating does not completely cover the surface. Wait at
least two minutes, and apply another light coat. Continue to make build passes of 4-6 mils, with two minute
intervals, until about 20 mils of product is on the surface.
Allow to cure at room temperature for at least one hour. At that time, cure can be accelerated by putting the
part in a warm room at 120
F.
Sand
Once the surface is fully cured, sand to remove any texture or orange peel. Use as fine a grit of paper as
is reasonable. Continue sanding with progressively finer grits, up to 1000 grit paper Allow at least eight
hours after sanding before re
-coating or before polishing begins.
Compound and polish to high gloss. We recommend Aqua Buff 1000W or 1000F
, followed by Aqua Buff
2000.
DURATEC SOLID WHITE
HI-GLOSS COATING
T
ROUBLESHOOTING | PRODUC T # 61 4-075
Problem Cause Solution
Alligatoring
Not enough catalyst used.
Substrate/primer incompatibility or
chemical reaction.
Check for proper catalyst levels.
Expose surface to higher temperature
before spraying when ambient temp
is below 64 F, 18 C.
Product sprayed on cold surface.
Check compatibility of surface of product.
Curing on surface but
not on substrate
Coating sprayed on cold surface
Expose substrate to higher temperture
before spraying.
Dimples (Craters)
Film build up too rapid, solvent
trapped in product.
Increase the number of passes to achieve
desired thickness. Allow for ash o
between passes.
Fisheyes
Substrate contaminated.
Do not use a tack rag . Ensure rag does
not leave contaminant on surface.
Spray in a clean area to minimize airborne
dust, water, waxes, and/or silicones.
Spray with dry fltered air.
Contamination in the air.
Contamination in the line.
Orange Peel
Spray equipment set up incorrectly.
Spray pressure incorrect.
Pot pressure incorrect.
Follow the instructions for equipment
set up.
Set pressure at 34-40 psi.
Set pressure at 10-12 psi.
Pinholes
Porosity
Substrate porosity.
Fill porous areas with product using
squeegee, brush or roller before spraying.
Acetone used as thinner.
Spray pressure too high.
Spray orifce too small.
Reduce pressure to 34-40 psi.
Use larger orifce.
Use slower solvent such as MEK or
Duratec Reducer
Surface not hard
or glossy
Coating not allowed to breathe after sanding
Allow time for solvents to escape before compounding and polishing.
Low reactivity catalyst used / coating under catalyzed.
Catalyze at 2% with full strength MEKP. Do not use 30 percent MEKP or catalyst with less than 8.8 percent active oygen.
See the Liability and Warranty statement on Page 1
by | Sep 27, 2025
Technical Datasheet – METYX USA Reinforcements
PRODUCT CODE
PRODUCT NAME BA-E 1700
PRODUCT DESCRIPTION +45 /-45 BIAXIAL
CUSTOMER CODE
CUSTOMER ID
REINFORCEMENT CONSTRUCTION
LAYER FIBER TYPE AREA WEIGHT
1 +45 600Tex E-glass 8.90 oz/yd
2
2 0 68Tex E-glass 0.03 oz/yd
2
3 90 68Tex E-glass 0.03 oz/yd
2
4 -45 275Tex E-glass 8.90 oz/yd
2
5 CSM E-glass
6 Stitch 76dtex PES 0.2 oz/yd
2
7
8
9
* Measurement method based on ISO 3374 . TOTAL*18.06oz/yd
2
( %3)
OTHER PORPERTIES ROLL INFO
Stitch Gauge Roll Width
Stitch Type Tricot Roll Weight
Stitch Length Roll Length
Pilot Yarn / Position NONE Core Diameter 3 in
Resin Compatibility Loss on Ignition Moisture Content
Polyester, Vinylester, Epoxy resins Max.%0,70 by weight (ISO 1887) Max.%0,20 by weight (ISO 3344)
Packaging
All rolls are wrapped with polyethylene bags; placed in pallet boxes or in single cardboard boxes or in pyramid
style on pallets.
Labelling
Each roll is labelled on the inner side of the core, on the bag or on the cardboard boxes including a unique
reference number for its traceability.
Storage
Store at %40-70 relative humidity and 64 -86 F (18 -30 C) temperature range. Recommended to be
brought to work area 24 hrs prior to use.
System Certification Product Certification
METYX products are produced by METYX USA company who is run by
ISO 9001:2015 QA System.
DNV-GL Approved
2504 Lowell Road Gastonia NC 28054
Phone : +1-704-824-1030 Fax : +1-704-824-1031 Web : www.metyx.com
FR-159-2/14.08.2018
by | Sep 27, 2025
TS.SP.02.48US/06.11.2019/02
Yenibosna Merkez Mah. Ladin Sok. No:36/70 Townofis
34197 Bah elievler / STANBUL / TURKEY
t. +90 212 580 5559 f. +90 212 580 5521
www.akpakimya.com e. info@akpakimya.com
AKPEROX L40S
Description : Dibenzoyl Peroxide Liquid Dispersion
Specifications;
Density (@25 C) : 1,175 0,005 gr/cm
3
Viscosity (@20 C) : 1000 200 c Pa.s
Appearance : White Liquid
Active Oxygen Content : 2,57 – 2,71 %
Peroxide Content : 39,0 – 41,0 %
SADT : 50 C
CAS Nr : 94-36-0
EINECS/ELINCS Nr : 202-327-6
REACH Reg. No : 01-2119511472-50-0017
UN Nr : 3107
Application : AKPEROX L40S can be used for room temperature curing of polyester and vinyl
ester resins in combination with amine accelerators such as dimethyl aniline,
diethyl aniline and dimethyl para toluidine. The system AKPEROX L40S/Amine
gives you a very fast cure that is hardly influenced by the humidity and fillers.
AKPEROX L40S may be flushed from spray equipment using isopropanol, methanol
or acetone followed by soap and water.
Usage & Amount : Recommended to use 1% 3% in general, according to climate conditions and
product formulation. It should be stirred immediately prior to use. In order to
obtain longer workable time, amount of usage should be reduced.It is usable with
Amine.
Packaging : 25 kgs Jerry Can
Handling & Storage : Must be between kept 0 C and +25 C. Keep pails tightly closed. Store and handle
in a dry, well-ventilated place. Keep away from sources of heat, ignition and direct
sunlight in original packaging. Provide grounding and venting in order to prevent
static electricity build-up. Avoid any contact with Amine and Cobalt Accelerators,
Acids, Alkalis and heavy metal compounds such as driers and metal soaps. Storage
Class; IIB
Shelf Life : 6 Months
For unopened packages at recommended storage conditions.