PRODUCT DATA SHEET
SikaBlock PP152
Version 01.01 (01 – 2025), en_US
PRODUCT DATA SHEET
SikaBlock PP152 (Formerly PP-1052)
Polyurethane Tooling Board
TYPICAL PRODUCT DATA (FOR FURTHER VALUES SEE SAFETY DATA SHEET)
DESCRIPTION
SikaBlock PP152 is a filled,
polyurethane- based tooling board for
foundry pattern making, molds, tools,
and other applications.
PRODUCT BENEFITS
– Very good abrasion resistance
– Good toughness and impact resistance
– Easy to seal and varnish
– Low dust formation when milled
– High dimensional stability
– Easy machinability
– Good compression strength and edge
stability
– Can be polished to a high gloss
AREAS OF APPLICATION
SikaBlock PP152 is suitable for a wide range of
applications, ranging from prototype and low-
volume models and tools, to high- volume
foundry patterns, core boxes, match plates,
gating and risering. Other potential
applications include metal forming, vacuum
forming, headliner tools, hammer forming,
stretch press dies, hemmingbucks and
production checking, holding, and assembly
fixtures.
Tests with actual materials and conditions
have to be performed to ensure satisfactory
performance.
Chemical base Polyurethane
Color Red
Density at 74 F (23 C) ASTM D792-91 71 lbs/ft
3
(1.14 g/cc)
Shore D hardness (at 77 F/220 F and 25 C/104 C), ASTM D2240
80 and 55
Flexural strength, ASTM D790 12,800 psi (88 Mpa)
Flexural modulus, ASTM D790 331,000 psi (2,280 MPa)
Tensile strength, ASTM D638 8,900 psi (61 MPa)
Tensile elongation, ASTM D638
7.0 %
Compressive strength, ASTM D695 4,051 psi (28 Mpa)
Unnotched Izod Impact (complete break), ASTM D256 0.124 ft-lb/in. (6.62 J/m)
Heat deflection temperature at 265 psi 140 F (60 C)
Coefficient of Thermal Expansion (CTE) , ASTM E1545
36 ppm/ F (64 ppm/ C)
SikaBlock
PP152
2
/
3
Metric Machining Envelope English Machining Envelope
TYPICAL STABILITY DATA
Condition Weight (g) Length (mm)
Initial (2 x 4 x 4 pieces) 593.81 99.69
After 24 hours at -30 F 594.00 99.40
After 24 hours at standard lab conditions 593.85 99.68
After 6 hours at 130 F 593.80 99.94
After 24 hours at standard lab conditions 593.86 99.69
After 168 hours at 100 F/100% relative humidity 595.74 99.75
After 24 hours at standard lab conditions 594.32 99.70
Additional 24 hours at standard lab conditions 594.31 99.70
MACHINING RECOMMENDATIONS
A
A)
These are possible recommendations. There may be some variance depending on cutters and CNC mill capabilities.
MACHINING PARAMETERS
A
Cutter Edge Velocity (Vc) Feed per Tooth (fz)
Rough shape 328 1,312 ft/min (100 to 400 m/min) 0.006 0.028 in (0.15 to 0.70 mm)/revolution
Finish 1,312 2,625 ft/min (400 to 800 m/min) 0.002 0.004 in (0.06 to 0.10 mm)/revolution
N = ((12 English or 1,000 metric) X Vc) / (Pl X Dc)
– Vc: Cutter edge velocity in ft/min (m/minute)
– Dc: Cutting diameter in inches (mm)
– n: Spindle speed in revolution/minute
Vf = n X fz X Z
– fz: Feed per tooth in inches (mm)/revolution
– Z: Number of teeth
– Vf: Feed speed in inches (mm)/minute
A)
These are possible recommendations. There may be some variance depending on cutters and CNC mill capabilities.
SikaBlock
PP152
3
/
3
Sika Corporation
30800 Stephenson Highway
Madison Heights, MI 48071
U.S.A.
Telephone: +1 248- 577-0020
Email: tsmh@us.sika.com
www.sikaindustry.com
PROCESSING CONDITIONS
Cutting suggestions for tooling planks
cutting horizontally on a planer mill: Head is
a 10 insert, 8 in diameter. For best results
use 5 inserts. Inserts are SFE-42E-10J-C5. We
have found a C2 Carbide insert does not chip
as easily. RPM 2200-2400 table feed 50-55
inches per minute. Some modifications may
be needed.
Saw Blades: A carbide- tipped, positive rake
saw blade with air slots should be used, if
possible. We suggest alternate top bevel ATB
or triple chip grind TCG rpm, depending on the
saw. We suggest 3,500 max rpm. Check with
manufacturer on saw and blade size. 12
blade, 48 teeth 16 blade, 48 teeth 18 blade,
60 teeth.
When sawing, you may need to back
part away from blade to relieve heat and
binding, then proceed with cut. It may be
necessary to take more than one cut to
achieve best finish.
Assembly/Finish: SikaBlock PP152 can be
bonded with the TCC-230 epoxy adhesive.
TCC-5220 is recommended to be used for the
patch paste.
Normal health and safety precautions should be
observed when handling these products:
Ensure adequate ventilation
Wear gloves, glasses, and protective clothes
For further information, please consult the Safety
Data Sheets.
STORAGE CONDITIONS
Store flat in a dry place. Allow time for
material to come to ambient temperature
prior to bonding or machining.
PACKAGING INFORMATION
Packaging information is available upon
request. Please contact your local Sika sales
representative.
FURTHER INFORMATION
Advice on specific applications will be given on
request. To contact Sika Corporation s Industry
Technical Services Department, send an email to
tsmh@us.sika.com. Copies of Safety Data
Sheets and Product Data Sheets are available
upon request.
BASIS OF PRODUCT DATA
All technical data stated in this document are
based on laboratory tests. Actual measured data
may vary due to circumstances beyond our
control.
ENVIRONMENTAL, HEALTH AND SAFETY
For further information and advice regarding
transportation, handling, storage and disposal of
chemical products, user should refer to the
actual Safety Data Sheets containing physical,
environmental, toxicological and other safety
related data. User must read the current
actual Safety Data Sheets before using any
products. In case of an emergency, call
CHEMTREC at 1-800-424-9300, International
703-527-3887.
LEGAL DISCLAIMER
Prior to each use of any product of Sika Corporation,
its subsidiaries or affiliates ( SIKA ), the user must
always read and follow the warnings and
instructions on the product s most current product
label, Product Data Sheet and Safety Data Sheet
which are available at usa.sika.com or by contacting
SIKA s Technical Service Department via email at
tsmh@us.sika.com. Nothing contained in any SIKA
literature or materials relieves the user of the
obligation to read and follow the warnings and
instructions for each SIKA product as set forth in the
current product label, Product Data Sheet and
Safety Data Sheet prior to use of the SIKA product.
SIKA warrants this product for one year from date
of installation to be free from manufacturing
defects and to meet the technical properties on the
current Product Data Sheet if used as directed
within the product s shelf life. User determines
suitability of product for intended use and assumes
all risks. User s and/or buyer s sole remedy shall be
limited to the purchase price or replacement of this
product exclusive of any labor costs. NO OTHER
WARRANTIES EXPRESS OR IMPLIED SHALL APPLY
INCLUDING ANY WARRANTY OF
MERCHANTABILITY OR FITNESS FOR A
PARTICULAR PURPOSE. SIKA SHALL NOT BE LIABLE
UNDER ANY LEGAL THEORY FOR SPECIAL OR
CONSEQUENTIAL DAMAGES. SIKA SHALL NOT BE
RESPONSIBLE FOR THE USE OF THIS PRODUCT IN A
MANNER TO INFRINGE ON ANY PATENT OR ANY
OTHER INTELLECTUAL PROPERTY RIGHTS HELD BY
OTHERS. Sale of SIKA products are subject to the
Terms and Conditions of Sale which are available at
https://usa.sika.com/en/group/SikaCorp/termsand
conditions.html or by calling +1 800-933-7452.
by | Sep 27, 2025
MP-1055 MODEL PLANK
Technical Data Sheet
POLYURETHANE MODELING BOARD
Masters Patterns Prototypes
Density 41 lbs/ft
3
(0.66g/cc), Hardness 60 Shore D
Page 1/3- June12, 2017 US Rev 04
SikaAxson US
+1 248 588 2270
axsonmh@axson.com
sikaaxson.us
CHINA
+86 21 58 68 30 37
marketing.china@axson.com
FRANCE
+33 1 34 40 34 60
axson@axson.com
INDIA
+91 20 25 56 07 10-11
info.india@axson.com
ITALY
+39 02 96 70 23 36
axson@axson.it
JAPAN
+81 5 64 26 25 91
sales.japan@axson.com
SIKA GERMANY
SikaAxson
+49 7125 940 492
tooling@de.sika.com
www.sikaaxson.de
MEXICO
+52 55 52 64 49 22
marketing@axson.com.mx
SLOVAKIA
+42 1 76 42 25 26
axson.sk@axson.com
SPAIN
+34 9 32 25 16 20
spain@axson.com
U.K.
+44 16 38 66 00 62
sales.uk@axson.com
DESCRIPTION
Machinable board designed for production of patterns, mock-ups, prototypes and masters by milling or machining by
hand. Additional applications manufacture of molds for low pressure reaction injection molding, vacuum forming
molds for lower number of pieces.
PROPERTIES
PHYSICAL PROPERTIES
Test Method Units Test Value
Color Visual brown
Density at 74 F (23 C) ASTM D 792-91 lbs/ft
3
(g/cc) 41 (0.66)
MECHANICAL PROPERTIES at 23 C
Hardness (77 F/150 F: 25 C/66 C) ASTM D 2240 Shore D1 60/50
Flexural strength ASTM D 790-95a psi (MPa) 3,618 (25)
Flexural modulus ASTM D 790-95a psi (MPa) 209,540 (1,445)
Tensile strength ASTM D 638-95 psi (MPa) 2,910 (20)
Elongation ASTM D 638-95 % 1.4
Compressive strength ASTM D 695-91 psi (MPa) 4,054 (28)
Unnotched Izod Impact (complete break) ASTM D 256-93 ft.Lbf/in (J/m) 1.21 (64.6)
Heat deflection temperature@264 psi ASTM D 648-82 F ( C) 140 (60)
Coefficient of thermal expansion (CTE) TMA 10
-6
. F
-1
( C) 34 (62)
STABILITY OF MP-1055 MODEL PLANK
Condition Weight(g) Length(mm)
Initial (2 x 4 x 4 pieces) 368.38 105.44
After 24 hours at -30 F 368.62 105.20
After 24 hours at standard lab conditions 368.38 105.44
After 6 hours at 130 F 368.33 105.63
After 24 hours at standard lab conditions 368.37 105.44
After 168 hours at 100 F/100% Relative Humidity 369.62 105.53
After 24 hours at standard lab conditions 368.93 105.43
Additional 24 hours at standard lab conditions 368.89 105.46
ASSEMBLY / FINISH
Ambient Use Adhesive System – TCC230 Epoxy Adhesive with TCC-102 or TCC-104 Hardeners
Patch Paste – P-34 Model Plank Filler with White Cream Hardener
Dense fine surface
Easy to seal and good to varnish
Low dust formation when milled
Easy machinability
Very high dimensional stability
Good compressive strength and edge stability
Good heat distortion temperature
MP-1055 MODEL PLANK
Technical Data Sheet
POLYURETHANE MODELING BOARD
Masters Patterns Prototypes
Density 41 lbs/ft
3
(0.66g/cc), Hardness 60 Shore D
Page 2/3- June12, 2017 US Rev 04
SikaAxson US
+1 248 588 2270
axsonmh@axson.com
sikaaxson.us
CHINA
+86 21 58 68 30 37
marketing.china@axson.com
FRANCE
+33 1 34 40 34 60
axson@axson.com
INDIA
+91 20 25 56 07 10-11
info.india@axson.com
ITALY
+39 02 96 70 23 36
axson@axson.it
JAPAN
+81 5 64 26 25 91
sales.japan@axson.com
SIKA GERMANY
SikaAxson
+49 7125 940 492
tooling@de.sika.com
www.sikaaxson.de
MEXICO
+52 55 52 64 49 22
marketing@axson.com.mx
SLOVAKIA
+42 1 76 42 25 26
axson.sk@axson.com
SPAIN
+34 9 32 25 16 20
spain@axson.com
U.K.
+44 16 38 66 00 62
sales.uk@axson.com
Machining Recommendations
Metric Machining Envelope English Machining Envelope
Machining Parameters
Cutter edge velocity
(Vc in ft/min (m/min))
Feed per tooth
(fz in inches (mm)/revolution)
Rough shape 328 -1640 (100 to 500) 0.006 0.028 (0.15 to 0.70)
Finish 1312 2625 (400 to 800) 0.003 0.004 (0.07 to 0.10)
n = ((12 English or 1000 metric) X Vc) / (PI X Dc) Vf = n X fz X Z
Vc: Cutter edge velocity in ft/min (m/minute) fz: Feed per tooth in inches (mm)/revolution
Dc: Cutting diameter in inches (mm) Z: Number of teeth
n: Spindle speed in revolution/minute Vf: Feed speed in inches (mm)/minute
These are possible recommendations. There may be some variance depending on cutters and CNC mill capabilities.
CUTTING SUGGESTIONS FOR TOOLING PLANKS
CUTTING HORIZONTALLY ON A PLANER MILL: Head is a 10 insert, 8 in diameter.For best results use 5
inserts.Inserts are SFE-42E-10J-C5.We have found a C2 Carbide insert does not chip as easily.RPM 2200-2400
table feed 50-55 inches per minute.Some modifications may be needed.
SAW BLADES: A carbide-tipped, positive rake saw blade with air slots should be used, if possible.We suggest
alternate top bevel ATB or triple chip grind TCG rpm, depending on the saw.We suggest 3,500 max rpm.Check
with manufacturer on saw and blade size.
12 blade, 48 teeth
16 blade, 48 teeth
18 blade, 60 teeth
When sawing, you may need to back part away from blade to relieve heat and binding, then proceed with cut.It
may be necessary to take more than one cut to achieve best finish.
Tool with 1 Tooth
0
100
200
300
400
500
600
700
800
900
1000
0
3000 6000 9000 12000 15000 18000 21000 24000 27000
Rotation Speed in RPM
Feed Speed in inches/m inute
Poor Surface Quality
Shavings Produced
Excess Dust
Tool with 1 Tooth
0
5000
10000
15000
20000
25000
0
3000 6000 9000 12000 15000 18000 21000 24000 27000
Rotation Speed in RPM
Feed Speed in mm/min ute
Poor Surface Quality
Shavings Produced
Excess Dust
MP-1055 MODEL PLANK
Technical Data Sheet
POLYURETHANE MODELING BOARD
Masters Patterns Prototypes
Density 41 lbs/ft
3
(0.66g/cc), Hardness 60 Shore D
Page 3/3- June12, 2017 US Rev 04
SikaAxson US
+1 248 588 2270
axsonmh@axson.com
sikaaxson.us
CHINA
+86 21 58 68 30 37
marketing.china@axson.com
FRANCE
+33 1 34 40 34 60
axson@axson.com
INDIA
+91 20 25 56 07 10-11
info.india@axson.com
ITALY
+39 02 96 70 23 36
axson@axson.it
JAPAN
+81 5 64 26 25 91
sales.japan@axson.com
SIKA GERMANY
SikaAxson
+49 7125 940 492
tooling@de.sika.com
www.sikaaxson.de
MEXICO
+52 55 52 64 49 22
marketing@axson.com.mx
SLOVAKIA
+42 1 76 42 25 26
axson.sk@axson.com
SPAIN
+34 9 32 25 16 20
spain@axson.com
U.K.
+44 16 38 66 00 62
sales.uk@axson.com
STORAGE CONDITIONS
Store flat in a dry place. Allow time for material to come to ambient temperature prior to bonding or machining.
HANDLING PRECAUTIONS
Normal health and safety precautions should be observed when handling these products:
Ensure good ventilation to prevent dust or chip accumulation
Wear gloves, and safety glasses.
Do not smoke when machining.
For additional information, please consult Safety Data Sheet (SDS).
DISCLAIMER
The information contained in this technical data sheet results from research and tests conducted in our laboratories under precise conditions.
Seller cannot anticipate all conditions under which seller s products, or the products of other manufacturers in combination with seller s
products, may be used. It is the responsibility of the user to determine the suitability of the SikaAxson s products, under their own conditions,
before commencing with the proposed application. In no event shall SikaAxson US be liable for any direct, indirect, punitive, incidental,
special, and/or consequential damages, to property or life, whatsoever arising out of or connected with the use or misuse of our products.
by | Sep 27, 2025
MP-1055 MODEL PLANK
Technical Data Sheet
POLYURETHANE MODELING BOARD
Masters Patterns Prototypes
Density 41 lbs/ft
3
(0.66g/cc), Hardness 60 Shore D
Page 1/3- June12, 2017 US Rev 04
SikaAxson US
+1 248 588 2270
axsonmh@axson.com
sikaaxson.us
CHINA
+86 21 58 68 30 37
marketing.china@axson.com
FRANCE
+33 1 34 40 34 60
axson@axson.com
INDIA
+91 20 25 56 07 10-11
info.india@axson.com
ITALY
+39 02 96 70 23 36
axson@axson.it
JAPAN
+81 5 64 26 25 91
sales.japan@axson.com
SIKA GERMANY
SikaAxson
+49 7125 940 492
tooling@de.sika.com
www.sikaaxson.de
MEXICO
+52 55 52 64 49 22
marketing@axson.com.mx
SLOVAKIA
+42 1 76 42 25 26
axson.sk@axson.com
SPAIN
+34 9 32 25 16 20
spain@axson.com
U.K.
+44 16 38 66 00 62
sales.uk@axson.com
DESCRIPTION
Machinable board designed for production of patterns, mock-ups, prototypes and masters by milling or machining by
hand. Additional applications manufacture of molds for low pressure reaction injection molding, vacuum forming
molds for lower number of pieces.
PROPERTIES
PHYSICAL PROPERTIES
Test Method Units Test Value
Color Visual brown
Density at 74 F (23 C) ASTM D 792-91 lbs/ft
3
(g/cc) 41 (0.66)
MECHANICAL PROPERTIES at 23 C
Hardness (77 F/150 F: 25 C/66 C) ASTM D 2240 Shore D1 60/50
Flexural strength ASTM D 790-95a psi (MPa) 3,618 (25)
Flexural modulus ASTM D 790-95a psi (MPa) 209,540 (1,445)
Tensile strength ASTM D 638-95 psi (MPa) 2,910 (20)
Elongation ASTM D 638-95 % 1.4
Compressive strength ASTM D 695-91 psi (MPa) 4,054 (28)
Unnotched Izod Impact (complete break) ASTM D 256-93 ft.Lbf/in (J/m) 1.21 (64.6)
Heat deflection temperature@264 psi ASTM D 648-82 F ( C) 140 (60)
Coefficient of thermal expansion (CTE) TMA 10
-6
. F
-1
( C) 34 (62)
STABILITY OF MP-1055 MODEL PLANK
Condition Weight(g) Length(mm)
Initial (2 x 4 x 4 pieces) 368.38 105.44
After 24 hours at -30 F 368.62 105.20
After 24 hours at standard lab conditions 368.38 105.44
After 6 hours at 130 F 368.33 105.63
After 24 hours at standard lab conditions 368.37 105.44
After 168 hours at 100 F/100% Relative Humidity 369.62 105.53
After 24 hours at standard lab conditions 368.93 105.43
Additional 24 hours at standard lab conditions 368.89 105.46
ASSEMBLY / FINISH
Ambient Use Adhesive System – TCC230 Epoxy Adhesive with TCC-102 or TCC-104 Hardeners
Patch Paste – P-34 Model Plank Filler with White Cream Hardener
Dense fine surface
Easy to seal and good to varnish
Low dust formation when milled
Easy machinability
Very high dimensional stability
Good compressive strength and edge stability
Good heat distortion temperature
MP-1055 MODEL PLANK
Technical Data Sheet
POLYURETHANE MODELING BOARD
Masters Patterns Prototypes
Density 41 lbs/ft
3
(0.66g/cc), Hardness 60 Shore D
Page 2/3- June12, 2017 US Rev 04
SikaAxson US
+1 248 588 2270
axsonmh@axson.com
sikaaxson.us
CHINA
+86 21 58 68 30 37
marketing.china@axson.com
FRANCE
+33 1 34 40 34 60
axson@axson.com
INDIA
+91 20 25 56 07 10-11
info.india@axson.com
ITALY
+39 02 96 70 23 36
axson@axson.it
JAPAN
+81 5 64 26 25 91
sales.japan@axson.com
SIKA GERMANY
SikaAxson
+49 7125 940 492
tooling@de.sika.com
www.sikaaxson.de
MEXICO
+52 55 52 64 49 22
marketing@axson.com.mx
SLOVAKIA
+42 1 76 42 25 26
axson.sk@axson.com
SPAIN
+34 9 32 25 16 20
spain@axson.com
U.K.
+44 16 38 66 00 62
sales.uk@axson.com
Machining Recommendations
Metric Machining Envelope English Machining Envelope
Machining Parameters
Cutter edge velocity
(Vc in ft/min (m/min))
Feed per tooth
(fz in inches (mm)/revolution)
Rough shape 328 -1640 (100 to 500) 0.006 0.028 (0.15 to 0.70)
Finish 1312 2625 (400 to 800) 0.003 0.004 (0.07 to 0.10)
n = ((12 English or 1000 metric) X Vc) / (PI X Dc) Vf = n X fz X Z
Vc: Cutter edge velocity in ft/min (m/minute) fz: Feed per tooth in inches (mm)/revolution
Dc: Cutting diameter in inches (mm) Z: Number of teeth
n: Spindle speed in revolution/minute Vf: Feed speed in inches (mm)/minute
These are possible recommendations. There may be some variance depending on cutters and CNC mill capabilities.
CUTTING SUGGESTIONS FOR TOOLING PLANKS
CUTTING HORIZONTALLY ON A PLANER MILL: Head is a 10 insert, 8 in diameter.For best results use 5
inserts.Inserts are SFE-42E-10J-C5.We have found a C2 Carbide insert does not chip as easily.RPM 2200-2400
table feed 50-55 inches per minute.Some modifications may be needed.
SAW BLADES: A carbide-tipped, positive rake saw blade with air slots should be used, if possible.We suggest
alternate top bevel ATB or triple chip grind TCG rpm, depending on the saw.We suggest 3,500 max rpm.Check
with manufacturer on saw and blade size.
12 blade, 48 teeth
16 blade, 48 teeth
18 blade, 60 teeth
When sawing, you may need to back part away from blade to relieve heat and binding, then proceed with cut.It
may be necessary to take more than one cut to achieve best finish.
Tool with 1 Tooth
0
100
200
300
400
500
600
700
800
900
1000
0
3000 6000 9000 12000 15000 18000 21000 24000 27000
Rotation Speed in RPM
Feed Speed in inches/m inute
Poor Surface Quality
Shavings Produced
Excess Dust
Tool with 1 Tooth
0
5000
10000
15000
20000
25000
0
3000 6000 9000 12000 15000 18000 21000 24000 27000
Rotation Speed in RPM
Feed Speed in mm/min ute
Poor Surface Quality
Shavings Produced
Excess Dust
MP-1055 MODEL PLANK
Technical Data Sheet
POLYURETHANE MODELING BOARD
Masters Patterns Prototypes
Density 41 lbs/ft
3
(0.66g/cc), Hardness 60 Shore D
Page 3/3- June12, 2017 US Rev 04
SikaAxson US
+1 248 588 2270
axsonmh@axson.com
sikaaxson.us
CHINA
+86 21 58 68 30 37
marketing.china@axson.com
FRANCE
+33 1 34 40 34 60
axson@axson.com
INDIA
+91 20 25 56 07 10-11
info.india@axson.com
ITALY
+39 02 96 70 23 36
axson@axson.it
JAPAN
+81 5 64 26 25 91
sales.japan@axson.com
SIKA GERMANY
SikaAxson
+49 7125 940 492
tooling@de.sika.com
www.sikaaxson.de
MEXICO
+52 55 52 64 49 22
marketing@axson.com.mx
SLOVAKIA
+42 1 76 42 25 26
axson.sk@axson.com
SPAIN
+34 9 32 25 16 20
spain@axson.com
U.K.
+44 16 38 66 00 62
sales.uk@axson.com
STORAGE CONDITIONS
Store flat in a dry place. Allow time for material to come to ambient temperature prior to bonding or machining.
HANDLING PRECAUTIONS
Normal health and safety precautions should be observed when handling these products:
Ensure good ventilation to prevent dust or chip accumulation
Wear gloves, and safety glasses.
Do not smoke when machining.
For additional information, please consult Safety Data Sheet (SDS).
DISCLAIMER
The information contained in this technical data sheet results from research and tests conducted in our laboratories under precise conditions.
Seller cannot anticipate all conditions under which seller s products, or the products of other manufacturers in combination with seller s
products, may be used. It is the responsibility of the user to determine the suitability of the SikaAxson s products, under their own conditions,
before commencing with the proposed application. In no event shall SikaAxson US be liable for any direct, indirect, punitive, incidental,
special, and/or consequential damages, to property or life, whatsoever arising out of or connected with the use or misuse of our products.
by | Sep 27, 2025
MP-1055 MODEL PLANK
Technical Data Sheet
POLYURETHANE MODELING BOARD
Masters Patterns Prototypes
Density 41 lbs/ft
3
(0.66g/cc), Hardness 60 Shore D
Page 1/3- June12, 2017 US Rev 04
SikaAxson US
+1 248 588 2270
axsonmh@axson.com
sikaaxson.us
CHINA
+86 21 58 68 30 37
marketing.china@axson.com
FRANCE
+33 1 34 40 34 60
axson@axson.com
INDIA
+91 20 25 56 07 10-11
info.india@axson.com
ITALY
+39 02 96 70 23 36
axson@axson.it
JAPAN
+81 5 64 26 25 91
sales.japan@axson.com
SIKA GERMANY
SikaAxson
+49 7125 940 492
tooling@de.sika.com
www.sikaaxson.de
MEXICO
+52 55 52 64 49 22
marketing@axson.com.mx
SLOVAKIA
+42 1 76 42 25 26
axson.sk@axson.com
SPAIN
+34 9 32 25 16 20
spain@axson.com
U.K.
+44 16 38 66 00 62
sales.uk@axson.com
DESCRIPTION
Machinable board designed for production of patterns, mock-ups, prototypes and masters by milling or machining by
hand. Additional applications manufacture of molds for low pressure reaction injection molding, vacuum forming
molds for lower number of pieces.
PROPERTIES
PHYSICAL PROPERTIES
Test Method Units Test Value
Color Visual brown
Density at 74 F (23 C) ASTM D 792-91 lbs/ft
3
(g/cc) 41 (0.66)
MECHANICAL PROPERTIES at 23 C
Hardness (77 F/150 F: 25 C/66 C) ASTM D 2240 Shore D1 60/50
Flexural strength ASTM D 790-95a psi (MPa) 3,618 (25)
Flexural modulus ASTM D 790-95a psi (MPa) 209,540 (1,445)
Tensile strength ASTM D 638-95 psi (MPa) 2,910 (20)
Elongation ASTM D 638-95 % 1.4
Compressive strength ASTM D 695-91 psi (MPa) 4,054 (28)
Unnotched Izod Impact (complete break) ASTM D 256-93 ft.Lbf/in (J/m) 1.21 (64.6)
Heat deflection temperature@264 psi ASTM D 648-82 F ( C) 140 (60)
Coefficient of thermal expansion (CTE) TMA 10
-6
. F
-1
( C) 34 (62)
STABILITY OF MP-1055 MODEL PLANK
Condition Weight(g) Length(mm)
Initial (2 x 4 x 4 pieces) 368.38 105.44
After 24 hours at -30 F 368.62 105.20
After 24 hours at standard lab conditions 368.38 105.44
After 6 hours at 130 F 368.33 105.63
After 24 hours at standard lab conditions 368.37 105.44
After 168 hours at 100 F/100% Relative Humidity 369.62 105.53
After 24 hours at standard lab conditions 368.93 105.43
Additional 24 hours at standard lab conditions 368.89 105.46
ASSEMBLY / FINISH
Ambient Use Adhesive System – TCC230 Epoxy Adhesive with TCC-102 or TCC-104 Hardeners
Patch Paste – P-34 Model Plank Filler with White Cream Hardener
Dense fine surface
Easy to seal and good to varnish
Low dust formation when milled
Easy machinability
Very high dimensional stability
Good compressive strength and edge stability
Good heat distortion temperature
MP-1055 MODEL PLANK
Technical Data Sheet
POLYURETHANE MODELING BOARD
Masters Patterns Prototypes
Density 41 lbs/ft
3
(0.66g/cc), Hardness 60 Shore D
Page 2/3- June12, 2017 US Rev 04
SikaAxson US
+1 248 588 2270
axsonmh@axson.com
sikaaxson.us
CHINA
+86 21 58 68 30 37
marketing.china@axson.com
FRANCE
+33 1 34 40 34 60
axson@axson.com
INDIA
+91 20 25 56 07 10-11
info.india@axson.com
ITALY
+39 02 96 70 23 36
axson@axson.it
JAPAN
+81 5 64 26 25 91
sales.japan@axson.com
SIKA GERMANY
SikaAxson
+49 7125 940 492
tooling@de.sika.com
www.sikaaxson.de
MEXICO
+52 55 52 64 49 22
marketing@axson.com.mx
SLOVAKIA
+42 1 76 42 25 26
axson.sk@axson.com
SPAIN
+34 9 32 25 16 20
spain@axson.com
U.K.
+44 16 38 66 00 62
sales.uk@axson.com
Machining Recommendations
Metric Machining Envelope English Machining Envelope
Machining Parameters
Cutter edge velocity
(Vc in ft/min (m/min))
Feed per tooth
(fz in inches (mm)/revolution)
Rough shape 328 -1640 (100 to 500) 0.006 0.028 (0.15 to 0.70)
Finish 1312 2625 (400 to 800) 0.003 0.004 (0.07 to 0.10)
n = ((12 English or 1000 metric) X Vc) / (PI X Dc) Vf = n X fz X Z
Vc: Cutter edge velocity in ft/min (m/minute) fz: Feed per tooth in inches (mm)/revolution
Dc: Cutting diameter in inches (mm) Z: Number of teeth
n: Spindle speed in revolution/minute Vf: Feed speed in inches (mm)/minute
These are possible recommendations. There may be some variance depending on cutters and CNC mill capabilities.
CUTTING SUGGESTIONS FOR TOOLING PLANKS
CUTTING HORIZONTALLY ON A PLANER MILL: Head is a 10 insert, 8 in diameter.For best results use 5
inserts.Inserts are SFE-42E-10J-C5.We have found a C2 Carbide insert does not chip as easily.RPM 2200-2400
table feed 50-55 inches per minute.Some modifications may be needed.
SAW BLADES: A carbide-tipped, positive rake saw blade with air slots should be used, if possible.We suggest
alternate top bevel ATB or triple chip grind TCG rpm, depending on the saw.We suggest 3,500 max rpm.Check
with manufacturer on saw and blade size.
12 blade, 48 teeth
16 blade, 48 teeth
18 blade, 60 teeth
When sawing, you may need to back part away from blade to relieve heat and binding, then proceed with cut.It
may be necessary to take more than one cut to achieve best finish.
Tool with 1 Tooth
0
100
200
300
400
500
600
700
800
900
1000
0
3000 6000 9000 12000 15000 18000 21000 24000 27000
Rotation Speed in RPM
Feed Speed in inches/m inute
Poor Surface Quality
Shavings Produced
Excess Dust
Tool with 1 Tooth
0
5000
10000
15000
20000
25000
0
3000 6000 9000 12000 15000 18000 21000 24000 27000
Rotation Speed in RPM
Feed Speed in mm/min ute
Poor Surface Quality
Shavings Produced
Excess Dust
MP-1055 MODEL PLANK
Technical Data Sheet
POLYURETHANE MODELING BOARD
Masters Patterns Prototypes
Density 41 lbs/ft
3
(0.66g/cc), Hardness 60 Shore D
Page 3/3- June12, 2017 US Rev 04
SikaAxson US
+1 248 588 2270
axsonmh@axson.com
sikaaxson.us
CHINA
+86 21 58 68 30 37
marketing.china@axson.com
FRANCE
+33 1 34 40 34 60
axson@axson.com
INDIA
+91 20 25 56 07 10-11
info.india@axson.com
ITALY
+39 02 96 70 23 36
axson@axson.it
JAPAN
+81 5 64 26 25 91
sales.japan@axson.com
SIKA GERMANY
SikaAxson
+49 7125 940 492
tooling@de.sika.com
www.sikaaxson.de
MEXICO
+52 55 52 64 49 22
marketing@axson.com.mx
SLOVAKIA
+42 1 76 42 25 26
axson.sk@axson.com
SPAIN
+34 9 32 25 16 20
spain@axson.com
U.K.
+44 16 38 66 00 62
sales.uk@axson.com
STORAGE CONDITIONS
Store flat in a dry place. Allow time for material to come to ambient temperature prior to bonding or machining.
HANDLING PRECAUTIONS
Normal health and safety precautions should be observed when handling these products:
Ensure good ventilation to prevent dust or chip accumulation
Wear gloves, and safety glasses.
Do not smoke when machining.
For additional information, please consult Safety Data Sheet (SDS).
DISCLAIMER
The information contained in this technical data sheet results from research and tests conducted in our laboratories under precise conditions.
Seller cannot anticipate all conditions under which seller s products, or the products of other manufacturers in combination with seller s
products, may be used. It is the responsibility of the user to determine the suitability of the SikaAxson s products, under their own conditions,
before commencing with the proposed application. In no event shall SikaAxson US be liable for any direct, indirect, punitive, incidental,
special, and/or consequential damages, to property or life, whatsoever arising out of or connected with the use or misuse of our products.
by | Sep 27, 2025
MP-1055 MODEL PLANK
Technical Data Sheet
POLYURETHANE MODELING BOARD
Masters Patterns Prototypes
Density 41 lbs/ft
3
(0.66g/cc), Hardness 60 Shore D
Page 1/3- June12, 2017 US Rev 04
SikaAxson US
+1 248 588 2270
axsonmh@axson.com
sikaaxson.us
CHINA
+86 21 58 68 30 37
marketing.china@axson.com
FRANCE
+33 1 34 40 34 60
axson@axson.com
INDIA
+91 20 25 56 07 10-11
info.india@axson.com
ITALY
+39 02 96 70 23 36
axson@axson.it
JAPAN
+81 5 64 26 25 91
sales.japan@axson.com
SIKA GERMANY
SikaAxson
+49 7125 940 492
tooling@de.sika.com
www.sikaaxson.de
MEXICO
+52 55 52 64 49 22
marketing@axson.com.mx
SLOVAKIA
+42 1 76 42 25 26
axson.sk@axson.com
SPAIN
+34 9 32 25 16 20
spain@axson.com
U.K.
+44 16 38 66 00 62
sales.uk@axson.com
DESCRIPTION
Machinable board designed for production of patterns, mock-ups, prototypes and masters by milling or machining by
hand. Additional applications manufacture of molds for low pressure reaction injection molding, vacuum forming
molds for lower number of pieces.
PROPERTIES
PHYSICAL PROPERTIES
Test Method Units Test Value
Color Visual brown
Density at 74 F (23 C) ASTM D 792-91 lbs/ft
3
(g/cc) 41 (0.66)
MECHANICAL PROPERTIES at 23 C
Hardness (77 F/150 F: 25 C/66 C) ASTM D 2240 Shore D1 60/50
Flexural strength ASTM D 790-95a psi (MPa) 3,618 (25)
Flexural modulus ASTM D 790-95a psi (MPa) 209,540 (1,445)
Tensile strength ASTM D 638-95 psi (MPa) 2,910 (20)
Elongation ASTM D 638-95 % 1.4
Compressive strength ASTM D 695-91 psi (MPa) 4,054 (28)
Unnotched Izod Impact (complete break) ASTM D 256-93 ft.Lbf/in (J/m) 1.21 (64.6)
Heat deflection temperature@264 psi ASTM D 648-82 F ( C) 140 (60)
Coefficient of thermal expansion (CTE) TMA 10
-6
. F
-1
( C) 34 (62)
STABILITY OF MP-1055 MODEL PLANK
Condition Weight(g) Length(mm)
Initial (2 x 4 x 4 pieces) 368.38 105.44
After 24 hours at -30 F 368.62 105.20
After 24 hours at standard lab conditions 368.38 105.44
After 6 hours at 130 F 368.33 105.63
After 24 hours at standard lab conditions 368.37 105.44
After 168 hours at 100 F/100% Relative Humidity 369.62 105.53
After 24 hours at standard lab conditions 368.93 105.43
Additional 24 hours at standard lab conditions 368.89 105.46
ASSEMBLY / FINISH
Ambient Use Adhesive System – TCC230 Epoxy Adhesive with TCC-102 or TCC-104 Hardeners
Patch Paste – P-34 Model Plank Filler with White Cream Hardener
Dense fine surface
Easy to seal and good to varnish
Low dust formation when milled
Easy machinability
Very high dimensional stability
Good compressive strength and edge stability
Good heat distortion temperature
MP-1055 MODEL PLANK
Technical Data Sheet
POLYURETHANE MODELING BOARD
Masters Patterns Prototypes
Density 41 lbs/ft
3
(0.66g/cc), Hardness 60 Shore D
Page 2/3- June12, 2017 US Rev 04
SikaAxson US
+1 248 588 2270
axsonmh@axson.com
sikaaxson.us
CHINA
+86 21 58 68 30 37
marketing.china@axson.com
FRANCE
+33 1 34 40 34 60
axson@axson.com
INDIA
+91 20 25 56 07 10-11
info.india@axson.com
ITALY
+39 02 96 70 23 36
axson@axson.it
JAPAN
+81 5 64 26 25 91
sales.japan@axson.com
SIKA GERMANY
SikaAxson
+49 7125 940 492
tooling@de.sika.com
www.sikaaxson.de
MEXICO
+52 55 52 64 49 22
marketing@axson.com.mx
SLOVAKIA
+42 1 76 42 25 26
axson.sk@axson.com
SPAIN
+34 9 32 25 16 20
spain@axson.com
U.K.
+44 16 38 66 00 62
sales.uk@axson.com
Machining Recommendations
Metric Machining Envelope English Machining Envelope
Machining Parameters
Cutter edge velocity
(Vc in ft/min (m/min))
Feed per tooth
(fz in inches (mm)/revolution)
Rough shape 328 -1640 (100 to 500) 0.006 0.028 (0.15 to 0.70)
Finish 1312 2625 (400 to 800) 0.003 0.004 (0.07 to 0.10)
n = ((12 English or 1000 metric) X Vc) / (PI X Dc) Vf = n X fz X Z
Vc: Cutter edge velocity in ft/min (m/minute) fz: Feed per tooth in inches (mm)/revolution
Dc: Cutting diameter in inches (mm) Z: Number of teeth
n: Spindle speed in revolution/minute Vf: Feed speed in inches (mm)/minute
These are possible recommendations. There may be some variance depending on cutters and CNC mill capabilities.
CUTTING SUGGESTIONS FOR TOOLING PLANKS
CUTTING HORIZONTALLY ON A PLANER MILL: Head is a 10 insert, 8 in diameter.For best results use 5
inserts.Inserts are SFE-42E-10J-C5.We have found a C2 Carbide insert does not chip as easily.RPM 2200-2400
table feed 50-55 inches per minute.Some modifications may be needed.
SAW BLADES: A carbide-tipped, positive rake saw blade with air slots should be used, if possible.We suggest
alternate top bevel ATB or triple chip grind TCG rpm, depending on the saw.We suggest 3,500 max rpm.Check
with manufacturer on saw and blade size.
12 blade, 48 teeth
16 blade, 48 teeth
18 blade, 60 teeth
When sawing, you may need to back part away from blade to relieve heat and binding, then proceed with cut.It
may be necessary to take more than one cut to achieve best finish.
Tool with 1 Tooth
0
100
200
300
400
500
600
700
800
900
1000
0
3000 6000 9000 12000 15000 18000 21000 24000 27000
Rotation Speed in RPM
Feed Speed in inches/m inute
Poor Surface Quality
Shavings Produced
Excess Dust
Tool with 1 Tooth
0
5000
10000
15000
20000
25000
0
3000 6000 9000 12000 15000 18000 21000 24000 27000
Rotation Speed in RPM
Feed Speed in mm/min ute
Poor Surface Quality
Shavings Produced
Excess Dust
MP-1055 MODEL PLANK
Technical Data Sheet
POLYURETHANE MODELING BOARD
Masters Patterns Prototypes
Density 41 lbs/ft
3
(0.66g/cc), Hardness 60 Shore D
Page 3/3- June12, 2017 US Rev 04
SikaAxson US
+1 248 588 2270
axsonmh@axson.com
sikaaxson.us
CHINA
+86 21 58 68 30 37
marketing.china@axson.com
FRANCE
+33 1 34 40 34 60
axson@axson.com
INDIA
+91 20 25 56 07 10-11
info.india@axson.com
ITALY
+39 02 96 70 23 36
axson@axson.it
JAPAN
+81 5 64 26 25 91
sales.japan@axson.com
SIKA GERMANY
SikaAxson
+49 7125 940 492
tooling@de.sika.com
www.sikaaxson.de
MEXICO
+52 55 52 64 49 22
marketing@axson.com.mx
SLOVAKIA
+42 1 76 42 25 26
axson.sk@axson.com
SPAIN
+34 9 32 25 16 20
spain@axson.com
U.K.
+44 16 38 66 00 62
sales.uk@axson.com
STORAGE CONDITIONS
Store flat in a dry place. Allow time for material to come to ambient temperature prior to bonding or machining.
HANDLING PRECAUTIONS
Normal health and safety precautions should be observed when handling these products:
Ensure good ventilation to prevent dust or chip accumulation
Wear gloves, and safety glasses.
Do not smoke when machining.
For additional information, please consult Safety Data Sheet (SDS).
DISCLAIMER
The information contained in this technical data sheet results from research and tests conducted in our laboratories under precise conditions.
Seller cannot anticipate all conditions under which seller s products, or the products of other manufacturers in combination with seller s
products, may be used. It is the responsibility of the user to determine the suitability of the SikaAxson s products, under their own conditions,
before commencing with the proposed application. In no event shall SikaAxson US be liable for any direct, indirect, punitive, incidental,
special, and/or consequential damages, to property or life, whatsoever arising out of or connected with the use or misuse of our products.
by | Sep 27, 2025
MP-1055 MODEL PLANK
Technical Data Sheet
POLYURETHANE MODELING BOARD
Masters Patterns Prototypes
Density 41 lbs/ft
3
(0.66g/cc), Hardness 60 Shore D
Page 1/3- June12, 2017 US Rev 04
SikaAxson US
+1 248 588 2270
axsonmh@axson.com
sikaaxson.us
CHINA
+86 21 58 68 30 37
marketing.china@axson.com
FRANCE
+33 1 34 40 34 60
axson@axson.com
INDIA
+91 20 25 56 07 10-11
info.india@axson.com
ITALY
+39 02 96 70 23 36
axson@axson.it
JAPAN
+81 5 64 26 25 91
sales.japan@axson.com
SIKA GERMANY
SikaAxson
+49 7125 940 492
tooling@de.sika.com
www.sikaaxson.de
MEXICO
+52 55 52 64 49 22
marketing@axson.com.mx
SLOVAKIA
+42 1 76 42 25 26
axson.sk@axson.com
SPAIN
+34 9 32 25 16 20
spain@axson.com
U.K.
+44 16 38 66 00 62
sales.uk@axson.com
DESCRIPTION
Machinable board designed for production of patterns, mock-ups, prototypes and masters by milling or machining by
hand. Additional applications manufacture of molds for low pressure reaction injection molding, vacuum forming
molds for lower number of pieces.
PROPERTIES
PHYSICAL PROPERTIES
Test Method Units Test Value
Color Visual brown
Density at 74 F (23 C) ASTM D 792-91 lbs/ft
3
(g/cc) 41 (0.66)
MECHANICAL PROPERTIES at 23 C
Hardness (77 F/150 F: 25 C/66 C) ASTM D 2240 Shore D1 60/50
Flexural strength ASTM D 790-95a psi (MPa) 3,618 (25)
Flexural modulus ASTM D 790-95a psi (MPa) 209,540 (1,445)
Tensile strength ASTM D 638-95 psi (MPa) 2,910 (20)
Elongation ASTM D 638-95 % 1.4
Compressive strength ASTM D 695-91 psi (MPa) 4,054 (28)
Unnotched Izod Impact (complete break) ASTM D 256-93 ft.Lbf/in (J/m) 1.21 (64.6)
Heat deflection temperature@264 psi ASTM D 648-82 F ( C) 140 (60)
Coefficient of thermal expansion (CTE) TMA 10
-6
. F
-1
( C) 34 (62)
STABILITY OF MP-1055 MODEL PLANK
Condition Weight(g) Length(mm)
Initial (2 x 4 x 4 pieces) 368.38 105.44
After 24 hours at -30 F 368.62 105.20
After 24 hours at standard lab conditions 368.38 105.44
After 6 hours at 130 F 368.33 105.63
After 24 hours at standard lab conditions 368.37 105.44
After 168 hours at 100 F/100% Relative Humidity 369.62 105.53
After 24 hours at standard lab conditions 368.93 105.43
Additional 24 hours at standard lab conditions 368.89 105.46
ASSEMBLY / FINISH
Ambient Use Adhesive System – TCC230 Epoxy Adhesive with TCC-102 or TCC-104 Hardeners
Patch Paste – P-34 Model Plank Filler with White Cream Hardener
Dense fine surface
Easy to seal and good to varnish
Low dust formation when milled
Easy machinability
Very high dimensional stability
Good compressive strength and edge stability
Good heat distortion temperature
MP-1055 MODEL PLANK
Technical Data Sheet
POLYURETHANE MODELING BOARD
Masters Patterns Prototypes
Density 41 lbs/ft
3
(0.66g/cc), Hardness 60 Shore D
Page 2/3- June12, 2017 US Rev 04
SikaAxson US
+1 248 588 2270
axsonmh@axson.com
sikaaxson.us
CHINA
+86 21 58 68 30 37
marketing.china@axson.com
FRANCE
+33 1 34 40 34 60
axson@axson.com
INDIA
+91 20 25 56 07 10-11
info.india@axson.com
ITALY
+39 02 96 70 23 36
axson@axson.it
JAPAN
+81 5 64 26 25 91
sales.japan@axson.com
SIKA GERMANY
SikaAxson
+49 7125 940 492
tooling@de.sika.com
www.sikaaxson.de
MEXICO
+52 55 52 64 49 22
marketing@axson.com.mx
SLOVAKIA
+42 1 76 42 25 26
axson.sk@axson.com
SPAIN
+34 9 32 25 16 20
spain@axson.com
U.K.
+44 16 38 66 00 62
sales.uk@axson.com
Machining Recommendations
Metric Machining Envelope English Machining Envelope
Machining Parameters
Cutter edge velocity
(Vc in ft/min (m/min))
Feed per tooth
(fz in inches (mm)/revolution)
Rough shape 328 -1640 (100 to 500) 0.006 0.028 (0.15 to 0.70)
Finish 1312 2625 (400 to 800) 0.003 0.004 (0.07 to 0.10)
n = ((12 English or 1000 metric) X Vc) / (PI X Dc) Vf = n X fz X Z
Vc: Cutter edge velocity in ft/min (m/minute) fz: Feed per tooth in inches (mm)/revolution
Dc: Cutting diameter in inches (mm) Z: Number of teeth
n: Spindle speed in revolution/minute Vf: Feed speed in inches (mm)/minute
These are possible recommendations. There may be some variance depending on cutters and CNC mill capabilities.
CUTTING SUGGESTIONS FOR TOOLING PLANKS
CUTTING HORIZONTALLY ON A PLANER MILL: Head is a 10 insert, 8 in diameter.For best results use 5
inserts.Inserts are SFE-42E-10J-C5.We have found a C2 Carbide insert does not chip as easily.RPM 2200-2400
table feed 50-55 inches per minute.Some modifications may be needed.
SAW BLADES: A carbide-tipped, positive rake saw blade with air slots should be used, if possible.We suggest
alternate top bevel ATB or triple chip grind TCG rpm, depending on the saw.We suggest 3,500 max rpm.Check
with manufacturer on saw and blade size.
12 blade, 48 teeth
16 blade, 48 teeth
18 blade, 60 teeth
When sawing, you may need to back part away from blade to relieve heat and binding, then proceed with cut.It
may be necessary to take more than one cut to achieve best finish.
Tool with 1 Tooth
0
100
200
300
400
500
600
700
800
900
1000
0
3000 6000 9000 12000 15000 18000 21000 24000 27000
Rotation Speed in RPM
Feed Speed in inches/m inute
Poor Surface Quality
Shavings Produced
Excess Dust
Tool with 1 Tooth
0
5000
10000
15000
20000
25000
0
3000 6000 9000 12000 15000 18000 21000 24000 27000
Rotation Speed in RPM
Feed Speed in mm/min ute
Poor Surface Quality
Shavings Produced
Excess Dust
MP-1055 MODEL PLANK
Technical Data Sheet
POLYURETHANE MODELING BOARD
Masters Patterns Prototypes
Density 41 lbs/ft
3
(0.66g/cc), Hardness 60 Shore D
Page 3/3- June12, 2017 US Rev 04
SikaAxson US
+1 248 588 2270
axsonmh@axson.com
sikaaxson.us
CHINA
+86 21 58 68 30 37
marketing.china@axson.com
FRANCE
+33 1 34 40 34 60
axson@axson.com
INDIA
+91 20 25 56 07 10-11
info.india@axson.com
ITALY
+39 02 96 70 23 36
axson@axson.it
JAPAN
+81 5 64 26 25 91
sales.japan@axson.com
SIKA GERMANY
SikaAxson
+49 7125 940 492
tooling@de.sika.com
www.sikaaxson.de
MEXICO
+52 55 52 64 49 22
marketing@axson.com.mx
SLOVAKIA
+42 1 76 42 25 26
axson.sk@axson.com
SPAIN
+34 9 32 25 16 20
spain@axson.com
U.K.
+44 16 38 66 00 62
sales.uk@axson.com
STORAGE CONDITIONS
Store flat in a dry place. Allow time for material to come to ambient temperature prior to bonding or machining.
HANDLING PRECAUTIONS
Normal health and safety precautions should be observed when handling these products:
Ensure good ventilation to prevent dust or chip accumulation
Wear gloves, and safety glasses.
Do not smoke when machining.
For additional information, please consult Safety Data Sheet (SDS).
DISCLAIMER
The information contained in this technical data sheet results from research and tests conducted in our laboratories under precise conditions.
Seller cannot anticipate all conditions under which seller s products, or the products of other manufacturers in combination with seller s
products, may be used. It is the responsibility of the user to determine the suitability of the SikaAxson s products, under their own conditions,
before commencing with the proposed application. In no event shall SikaAxson US be liable for any direct, indirect, punitive, incidental,
special, and/or consequential damages, to property or life, whatsoever arising out of or connected with the use or misuse of our products.
by | Sep 27, 2025
SPECIFICATIONS
REK100G
High Temperature Graphite Flat Stock
Panel is Laminated With Carbon Graphite Cloth and High
Temperature Epoxy, With Peel Ply on Each Side.
PHYSICAL PROPERTIES:
Fiber Content by
Density
Flexural Strength (ASTM
0790)
Flexural Modulus (ASTM 0790)
Flexural Strength at 350 F
(ASTM
0790)
Flexural Modulus at 350 F
(ASTM 0
Heat Deflection (ASTM 0648)
Glass Transition (ASTM 03481
Coefficient of Linear Thermal
Expansion (ASTM
0696)
33.8% Resin/66.2% Carbon Fiber
76.25Ib/cu.ft
..
52,300 PSI
6.
11 X 10.6 PSI
35,000 PSI
4.07
X10.6 PSI
451
0
F/233 C
1.9
X 10.6/
o
F
3.4
X10.6/
o
C
f~~nullluiil
PLASTICS 42130 Mound Rd. Sterling Heights, Michigan 48314 (586) 739-8850 Fax (586) 739-0750
25
by | Sep 27, 2025
SPECIFICATIONS
REK100G
High Temperature Graphite Flat Stock
Panel is Laminated With Carbon Graphite Cloth and High
Temperature Epoxy, With Peel Ply on Each Side.
PHYSICAL PROPERTIES:
Fiber Content by
Density
Flexural Strength (ASTM
0790)
Flexural Modulus (ASTM 0790)
Flexural Strength at 350 F
(ASTM
0790)
Flexural Modulus at 350 F
(ASTM 0
Heat Deflection (ASTM 0648)
Glass Transition (ASTM 03481
Coefficient of Linear Thermal
Expansion (ASTM
0696)
33.8% Resin/66.2% Carbon Fiber
76.25Ib/cu.ft
..
52,300 PSI
6.
11 X 10.6 PSI
35,000 PSI
4.07
X10.6 PSI
451
0
F/233 C
1.9
X 10.6/
o
F
3.4
X10.6/
o
C
f~~nullluiil
PLASTICS 42130 Mound Rd. Sterling Heights, Michigan 48314 (586) 739-8850 Fax (586) 739-0750
25
by | Sep 27, 2025
SPECIFICATIONS
REK100G
High Temperature Graphite Flat Stock
Panel is Laminated With Carbon Graphite Cloth and High
Temperature Epoxy, With Peel Ply on Each Side.
PHYSICAL PROPERTIES:
Fiber Content by
Density
Flexural Strength (ASTM
0790)
Flexural Modulus (ASTM 0790)
Flexural Strength at 350 F
(ASTM
0790)
Flexural Modulus at 350 F
(ASTM 0
Heat Deflection (ASTM 0648)
Glass Transition (ASTM 03481
Coefficient of Linear Thermal
Expansion (ASTM
0696)
33.8% Resin/66.2% Carbon Fiber
76.25Ib/cu.ft
..
52,300 PSI
6.
11 X 10.6 PSI
35,000 PSI
4.07
X10.6 PSI
451
0
F/233 C
1.9
X 10.6/
o
F
3.4
X10.6/
o
C
f~~nullluiil
PLASTICS 42130 Mound Rd. Sterling Heights, Michigan 48314 (586) 739-8850 Fax (586) 739-0750
25
by | Sep 27, 2025
SPECIFICATIONS
REK100G
High Temperature Graphite Flat Stock
Panel is Laminated With Carbon Graphite Cloth and High
Temperature Epoxy, With Peel Ply on Each Side.
PHYSICAL PROPERTIES:
Fiber Content by
Density
Flexural Strength (ASTM
0790)
Flexural Modulus (ASTM 0790)
Flexural Strength at 350 F
(ASTM
0790)
Flexural Modulus at 350 F
(ASTM 0
Heat Deflection (ASTM 0648)
Glass Transition (ASTM 03481
Coefficient of Linear Thermal
Expansion (ASTM
0696)
33.8% Resin/66.2% Carbon Fiber
76.25Ib/cu.ft
..
52,300 PSI
6.
11 X 10.6 PSI
35,000 PSI
4.07
X10.6 PSI
451
0
F/233 C
1.9
X 10.6/
o
F
3.4
X10.6/
o
C
f~~nullluiil
PLASTICS 42130 Mound Rd. Sterling Heights, Michigan 48314 (586) 739-8850 Fax (586) 739-0750
25