Woven roving EWR800
Product description
EWR800 woven roving from E-glass direct roving by weaving machines.
Applicable for hand lay-up process, mould pressing, machinery formation.
Compatible with unsaturated polyester resin and vinyl resin.
Characteristics Product code
Thickness steady EWR 800
Free of contamination E E -glass
Fast wet out WR Woven roving
High laminate strength 800 Unit weight (g/m
2
)
Good mechanical properties Width Net width of fabrics (mm)
Technical data
Unit weight
(g/m
2
)
Warp Weft
Moisture
(%)
Loss on
ignition (%)
Tensile
strength
on
warp(N)
Tensile
strength
on weft(N)
tex
Density
(roving/10cm)
tex
Density
(roving/10cm)
800 8% 2400 5% 18.1 10% 2400 5% 15.5 10% 0.2 0.4 0.8 4600 4400
According to the standard GB/T 18370-2001
Package
E-glass woven roving is packed and sealed in PE bags by roll, put into cartons or wrapped with
craft paper, and put flat on pallets or in bulk package. And pallets should not be stacked more than
2 layers.
Roll width(mm) roll weight(kg) rolls/pallet pallet size(mm) weight per pallet(kg)
1270 50 16 1350*1120 800
Storage
This product should be stored in a dry, cool and rainproof place, with temperature from 5 to 35
and humidity between 35% and 65%. It is recommended to be put under room temperature for
over 24 hours prior to use and kept in intact package when it is not used to avoid damp.
by | Sep 27, 2025
13177 Ramona Blvd Suite F, USA Tel: 626-343-5968 Fax: 626-414-6964
3D fabric is woven out of 100% E-glass fiber, as well as carbon fiber, Kevlar fiber and other high-performance fibers. This
structure consists of two decklayers formed by warp and weft direction fiber and Z direction fiber which interconnect both
decklayers. The typical structure of vertical piles can be recognized by the 8-shaped piles in warp direction. Other shapes of
vertical piles, such as I-shape and V- shape, can be realized too. The thickness between two decklayers (Z direction) can be
designed from 2mm to 40mm in order to meet different needs.
Type
3 5 8 10 12 15 18 20
Core Thickness (N) mm 3.0 5.0 8.0 10.0 12.0 15.0 18.0 20.0
Decklayer Thickness (N) mm 0.36 0.36 0.36 0.58 0.58 0.58 0.58 0.58
Fabric Weight (N) g/ 720 810 920 1440 1510 1580 1720 1880
Laminate Weight Polyester Resin(N) g/ 1510 1680 1900 2930 3060 3250 3440 3570
by | Sep 27, 2025
13177 Ramona Blvd Suite F, USA Tel: 626-343-5968 Fax: 626-414-6964
3D fabric is woven out of 100% E-glass fiber, as well as carbon fiber, Kevlar fiber and other high-performance fibers. This
structure consists of two decklayers formed by warp and weft direction fiber and Z direction fiber which interconnect both
decklayers. The typical structure of vertical piles can be recognized by the 8-shaped piles in warp direction. Other shapes of
vertical piles, such as I-shape and V- shape, can be realized too. The thickness between two decklayers (Z direction) can be
designed from 2mm to 40mm in order to meet different needs.
Type
3 5 8 10 12 15 18 20
Core Thickness (N) mm 3.0 5.0 8.0 10.0 12.0 15.0 18.0 20.0
Decklayer Thickness (N) mm 0.36 0.36 0.36 0.58 0.58 0.58 0.58 0.58
Fabric Weight (N) g/ 720 810 920 1440 1510 1580 1720 1880
Laminate Weight Polyester Resin(N) g/ 1510 1680 1900 2930 3060 3250 3440 3570
by | Sep 27, 2025
Customer: Contract No.: 2015V35
P.O. No.: 091311
Quanity: Production Date: April, 2015
Batch No.: Testing Date: April 15, 2015
Unit Test MethodControl Standard Test Result
g/km ISO1889-1997 4400 (+/-5%) 4389
% ISO1887-1995 0.60+/-0.15 0.55
% ISO3344-1997 0.10 0.04
N/A ISO2078-1993 Silane Silane
Date: 15-Apr-15
Test Conclusion: The tested products conform to all above standard
Test Conducted by: Jingjun Chen
Quality Assurance:
(Signature)
Zhangjie
Glass Sizing
Test Condition:
Testing Temperature: 23 Centigrade
Relative Humidity: 57%
Moisture Content
CERTIFICATE OF ANALYSIS
Revchem Composites Inc
2720 S. Willow Ave, Bloomington,
CA 92316 USA
Product:
Fiberglass
Direct Roving 4400tex
21520 LB
2015V35
Characteristics
Tex, nominal
Nominal size content
by | Sep 27, 2025
Introduction
Multi-Axail Fabric is made of several layers of input roving which is laid down at precise angles and knitted together.
The input roving varies according to different specification. It’s a high performance fabric compatible with various.
resin systems
It’s widely used in hand lay-up, pultrusion, RTM process + / -45
for various industries such as:vessels, boats, containers, aircraft,
automotive parts, wind blades,sport equipment, tanks& pipes, panels.
Features
High mechanical strength, high impact reponse, fast wet-out
Better surface finish, excellent laminate properties
Product & Specification
Test Standard Tolerance
(oz./sq.yd) (g/sq.m) %
830 yield (600tex) ISO 3374 6.0 204 5
830 yield (600tex) ISO 3374 6.0 204 5
207yield (2400tex) ISO 3374 8.1 275 10
Polyester 83 Denier ISO 3374 0.2 7 5
ISO 3374 20.3 690 7
Physical propertyTest Standard control data
Basic weight ISO 3374 5%
ISO 3344 0.2%
ISO 1887 0.5% -4.0%
Tech. Parameter & Package
It’s wrapped with plastic film and packed in carton. Both large roll and standard roll available:
Roll type:Large roll standard roll
Roll Width:60″ / 1524mm
Roll Weight:242.5 lb / 110kg
Roll Length:
9 ctn/plt, 2183lb/plt, 990kg/plt
6 ctn/plt, 1455lb/plt, 660kg/plt
Storage:
Stored under dry, cool condiction. Temperature and humidity to be 15 – 35 and 35% – 65%.
The fiberglass materials should remain in good package before being used.
Package:
9 ctn/plt, 1826lb/plt, 828kg/plt16 ctn/plt, 1764lb/plt, 800kg/plt
6 ctn/plt, 1217lb/plt, 552kg/plt12 ctn/plt, 1323lb/plt, 600kg/plt
50″ /1270mm
202.8 lb / 92kg 110.2 lb / 50kg
91.5 yd / 83.7m 111.5 yd / 102m 62.8 yd / 57.5m
Chopped Mat
Polyester Stitch
Total Weight
Moisture content
Ignition Loss
50″ /1270mm
DBM1208
Architecture Yield Input Area Weight
+45
-45
by | Sep 27, 2025
Certificate No.:2021v4409
Customer: Invoice No.: 2021V44
Quanity:
Production Date: April, 2021
Testing Date:April 26, 2021
UnitOverall DensityControl Standard Test Result
g/m2 ISO3374-2000 +/-5% 610.8
mm ISO5025-1997 1270 +/-10 1270
% ISO3344-1997 0.20 0.05
% ISO1887-1995
0.63+/-0.28 (exclude
stitch yarn)
0.47
Date: April 26,2021
SINAUVA COMPOSITES CO., LTD.
CERTIFICATE OF ANALYSIS
Revchem Composites
Product:
DB170 x50″
+/-45 E-Glass 600g x 1270mm
1400kgs (3086 lbs)
Characteristics
Average Mass
per Unit Area
Roll Width
Moisture Content
Ignition Loss
Test Conducted by: Zhu Liang
Quality Assurance: Chen Chen
Testing Temperature: 23 Centigrade
Relative Humidity: 60%
Test Conclusion: The tested products conform to all above standard
Test Condition:
by | Sep 27, 2025
by | Sep 27, 2025
TECHNICAL DATA SHEET
(EBX400)
Description
Multi-axial fabric is stitched with E-glass direct roving by polyester thread, applicable for vacuum infusion,
prepreg, and hand lay-up process, compatible with unsaturated polyester resin, applied to production of molding,
yachts, boats, nacelle cover etc.
Characteristics Product code
Roving in fabric maintains high strength without bending EBX400(+45/ -45)C240UP-1270E6
Lower resin consumption and lower weight of final product EBX E-glass biaxial fabric
Smooth surface on the composites, with minimized fabric trails 400 Unit weight
High fiber content in final product to increase its mechanical properties 240 Chopped strand mat
UP Unsaturated polyester
Technical Data
Structure specification for EBX400(+45/-45)C240UP
Layer process
Layer
Filament
Diameter
Weight(g)
+45 14 200
-45 14 200
Chopped stand mat 12 240
stitch 7
Packaging
Taishan multi-axial fabric is of unfixed roll weight, packed in PE bags by roll, put into cartons or
wrapped with kraft paper, and put flat on the pallets or in bulk package and pallets should not be
stacked more than 2layers.
Storage
This product should be stored in a dry, cool and rainproof place, with temperature from 5 to 35
and humidity between 35% and 65%. It is recommended to be put under room temperature for over
24 hours prior to use. Keeping in intact package when not used to avoid damp
by | Sep 27, 2025
by | Sep 27, 2025