SIL05BB-465
Figurine Casting Resin
Technical Data Sheet
INTERPLASTIC CORPORATION
3535 Latonia Avenue
Fort Wright, KY 41015-0159
859.292.7400 Fax: 859.292.7424
www.interplastic.com
SIL05BB-465 is specifically prepared for room temperature fabrication of plaques, furniture trim
and simulated wood parts. It has a minimum tack plus toughness and flexibility to withstand
handling and shipping rigors. Various fillers may be used with SIL05BB-465, such as talc,
calcium carbonate or light weight microballoons. Depending on the type and amount of fillers
used, finished goods will display different degrees of flexibility and weight. This resin can be
blended with other Silmar resins to develop tougher surfaces. SIL05BB-465 contains wax.
TYPICAL RESIN PROPERTIES @ 77 F RESULTS
Brookfield Viscosity @ 20 rpm 460 600
Brookfield Spindle No. (RVT) 2
Catalyst, %, DDM-9 MEK-P 1.25
Gel Time, minutes:seconds 5:00 10:00
Gel to Peak, minutes:seconds 9:00 16:00
Peak Exotherm, F (100g mass) 230 260
Solids, % 66.5 69.5
Moisture, % .150 max.
MECHANICAL PROPERTIES OF NEAT CURED RESIN RESULTS
Properties ASTM Test Method PSI Mpa*
Flexural Strength D-790 N/A N/A
Flexural Modulus D-790 N/A N/A
Tensile Strength D-638 395 2.7
Tensile Modulus D-638 1.07 x 10
3
7.4
Tensile Elongation, % D-638 52 52
Heat Distortion Temperature D-648 N/A
Hardness, Shore-D N/A 40-50
Mega Pascal in an international unit.
Revised: 1/22
Interplastic Corporation makes no warranties regarding any material and/or samples described in this report. All properties specified above are
approximate and may vary from material delivered. Delivered material complies with the certificate of analysis on each shipment of product.
Interplastic Corporation makes no representations of fact regarding the material except those specified above. Final determination of part or
application and the suitability of the material for the use contemplated is the sole responsibility of the buyer. Our technical sales representatives
will assist in developing procedures to fit individual requirements as a customer accommodation, but all advice is accepted at your risk and should
be checked for suitability to your particular processes and needs. These test data and properties are based on results obtained for a specific
material under the specified test conditions – they are not to be used as specifications and are not warranted as performance attributes for any
product or system.
.