Interplastic Corporation makes no warranties regarding any material and/or samples described in this report. All properties
specified above are approximate and may vary from material delivered. Delivered material complies with the Certificate of
Analysis on each shipment of product. Interplastic Corporation makes no representations of fact regarding the material
except those specified above. Final determination of part or application and the suitability of the material for the use
contemplated is the sole responsibility of the buyer. Our technical sales representatives will assist in developing procedures
to fit individual requirements as a customer accommodation, but all advice is accepted at your risk and should be checked for
suitability to your particular processes and needs. These test data and properties are based on results obtained for a specific
material under the specified test conditions. They are not to be used as specifications and are not warranted as performance
attributes for any product or system.
INTERPLASTIC CORPORATION
2015 Northeast Broadway Street
Minneapolis, Minnesota 55413-1775
651.481.6860 Fax 612.331.4235
www.interplastic.com
Revised: 1/2024
MVR8071 is a promoted, non-thixotropic, vinyl ester/polyester resin blend. It is designed for the fabrication of thick parts
using the vacuum infusion process (VIP). MVR8071 is designed to provide a low exotherm in thick parts while maintaining
an excellent degree of cure.
FEATURES BENEFITS
Low Viscosity Rapid filling of parts
Low Exotherm/Low Shrinkage Improved surface quality
Excellent Fiberglass Wet-Out High laminate physical properties
Good Resin Cure Improved resistance to post-cure
RELATED PRODUCTS GEL TIME
MVR8071-40 35-43 Minutes
LIQUID PROPERTIES RESULTS
Viscosity, Brookfield Model LV #2 Spindle @ 60 rpm, 77 F (25 C), cPs 100-125
100 grams resin @ 77 F (25 C), initiated with 1.5% MEKP-925H by weight*
Gel Time, min:sec 45:00-53:00
Gel to Peak Exotherm Time, min:sec 17:00-26:00
Peak Exotherm 260-310 F (127-154 C)
Non-Volatile Content, % 62.0-66.0
Hazardous Air Pollutant (Styrene) Content, % 29.0-34.0
Weight per Gallon, Typical Value, lbs. 8.5-9.5
TYPICAL PROPERTIES
Thickness 1/8 inch (3.2 mm) Casting
Construction Not Applicable
Flexural Strength, ASTM D790 18,000 psi 124 MPa
Flexural Modulus, ASTM D790 5.4 x 10
5
psi 3,720 MPa
Tensile Strength, ASTM D638 9,200 psi 63 MPa
Tensile Modulus, ASTM D638 5.4 x 10
5
psi 3,720 MPa
Tensile Elongation, ASTM D638 2.0 % 2.0 %
Heat Distortion Temperature, ASTM D648 187 F 86 C
*Gel time and reactivity will vary due to the type and concentration of Free Radical Initiator (catalyst), shop temperature, humidity, and type of fillers used. In order to meet
your individual needs, consult our technical sales representative for assistance. If using methyl ethyl ketone peroxide (MEKP) to gel and cure CoREZYN vinyl ester resins,
we recommend only these three brands: Cadox L-50a (Nouryon), Luperox DHD-9 (Arkema), and Norox MEKP-925 (United Initiators). These must be used at the
appropriate percentage and suitable temperature. Contact your Interplastic Corporation representative for assistance.
MVR8071
Vacuum Infusion Resin
Technical Data Sheet