Method State
Weight Resin
Volume Hardener
Property
Hardness
Compression Yield 11,800
Tensile Strength 7,070
Tensile Modulus 4.20E+05
Tensile Elongation
Flexural Strength 12,100
Flexural Modulus 4.00E+05
Lap Shear on 1018 Steel 1,980
Lap Shear on 2024T Aluminum 1,980
Tensile Adhesion to 1018 Steel 2,580
Tensile Adhesion to 2024T Aluminum 1,720
Property
Tg DSC Onset 1st Heat 127(53)
Heat Deflection Temperature 123(51)
2015 Gougeon Brothers, Inc.
1
Store PRO-SET Epoxy resins and hardeners at room temperature in sealed containers until shortly before use. As with many
high-performance epoxy resins, repeated exposure to low temperatures during storage may cause the resin to crystallize. If this
occurs, warm the resin to 125 F and stir to dissolve crystals. Hardeners may form carbamation when exposed to CO
2 and
moisture in the atmosphere for extended periods of time. Prevent carbamation by protecting hardeners from exposure until
immediately prior to processing.
Test specimens were neat epoxy (without fiber reinforcement).
Typical values, not to be construed as specification.
Rev 2 / Dec 2015
THERMAL PROPERTIES
Standard Units 72 F (22 C) x 2 wk
ASTM E1356 F ( C)
ASTM D4541psi (MPa) (12)
ASTM D648 F ( C)
ASTM D1002psi (MPa) (14)
ASTM D4541psi (MPa) (18)
ASTM D790 psi (GPa) (2.76)
ASTM D1002psi (MPa) (14)
ASTM D638 % 4.4
ASTM D790 psi (MPa) (83)
ASTM D638 psi (MPa) (49)
ASTM D638 psi (GPa) (2.9)
ASTM D2240 Type D 84
ASTM D695 psi (MPa) (81)
8.51 (1.02)
Standard Units 72 F (22 C) x 2 wk
MECHANICAL PROPERTIES
ADHESIVE EPOXY
Resin:HardenerResin:Hardener Units
2.00:1 100:50.0 lb/gal (g/cc)
72 F (22 C)
2.29:1 100:43.7 lb/gal (g/cc)9.76 (1.17)
Minimum Cure Temp ASTM D2196 F ( C) 65 (18)
MIX RATIO DENSITY
100g Pot Life ASTM D2471minutes 45-55
Working Time (1/2″ bead)ASTM D2471minutes135-165
72 F (22 C)
HANDLING PROPERTIES
Technical Data
Property Standard Units
COMBINED FEATURES
Shear thinning resins and hardeners are
thixotropic gels. The mixture fills gaps and will
not sag on vertical surfaces. The material
wets out the substrate, making priming or
pre-wetting unnecessary on most surfaces,
while ensuring a good bond.
Slow cure speed hardener provides
approximately 150 minutes of working time at
72 F (22 C).
Room temperature cure properties suitable
for many composite components and
structures.
High performance pre-thickened, two-part
epoxy adhesives for secondary bonding of
laminated composites, steel, aluminum, cast
iron, concrete, stone, and most wood
species. PRO-SET Adhesives will bond these
materials, to one another in any combination.
Coverage one cartridge set dispenses
approximately 47 ft of 1/4″ bead, or 17 ft of
1/2″ bead and will cover approximately 7 sq ft
when spread with a 1/8″ x 1/8″ notched
spreader, or 12 sq ft with a 1/16″ x 1/16″
notched spreader.
Shelf life is 18 months for resin and 18
months for hardener when properly stored
1
.
ADV-175
ADV-277