Property Standard Units
150g Pot Life ASTM D2471minutes
500g Pot Life ASTM D2471minutes
Viscosity MixedASTM D2196 cP
Viscosity (resin)ASTM D2196 cP
Viscosity (hardener)ASTM D2196 cP
COMBINED FEATURES Method Resin:Hardener
Weight 4.70:1
Weight Range 5.26:1 – 4.54:1
Volume 4.00:1
Volume Range 4.53:1 – 3.91:1
State Units 72 F (22 C)
Cured lb/gal (g/cc)9.85 (1.18)
Resin lb/gal (g/cc)9.72 (1.17)
Hardener lb/gal (g/cc)8.37 (1.00)
2020 Gougeon Brothers, Inc.
40
HANDLING PROPERTIES
Technical Data
72 F (22 C)
38
2,550
8,200
240
100:25.0
HIGH-TEMP LAMINATING EPOXY
MIX RATIO
Resin:Hardener
100:21.5
100:19.0 – 100:22.0
100:22.1 – 100:25.6
DENSITY
VISCOSITY VS TEMPERATURE
Rev 2 / Sept 2020
Test specimens were neat epoxy (without fiber reinforcement).
Typical values, not to be construed as specification.
High-temperature, high-performance epoxy
formulation for synthetic composite part and
tooling manufacture.
T
gas high as 300 F (149 C) with proper post
cure. Provides excellent temperature stability
and great part cosmetics.
Fast cure speed hardener provides 1 to 2
hour working time at 72 F (22 C). A typical
laminate will gel in 4 to 6 hours at room
temperature.
Medium viscosity for wet out of synthetic
composite fabrics.
Elevated temperature cure is required.
Parts can be pulled after 24-48 hours at room
temperature or sooner after a mild initial cure
of 90-110 F (32-43 C). See chart for post cure
information.
Quality-control tinting is available at no extra
charge; simply add “QC” after the product
code on your order.
Shelf life is 3 years for resin and 18 months
for hardener when properly stored
2
.
HTP 182
HTP 284
0
1000
2000
3000
4000
5000
6000
5060708090100110120130
Viscosity (cP)
Temperature ( F)
Hardness ASTM D2240 Type D
Compression Yield ASTM D695psi (MPa)
Tensile Strength ASTM D638psi (MPa)
Tensile Modulus ASTM D638 psi (GPa)
Tensile Elongation ASTM D638 %
Flexural Strength ASTM D790psi (MPa)
Flexural Modulus ASTM D790 psi (GPa)
Tg DMA Peak Tan Delta ASTM E1640
1
F ( C)
Tg DMA Onset Storage ModulusASTM E1640
1
F ( C)
Tg DSC Onset 1st Heat ASTM E1356 F ( C)
Heat Deflection TemperatureASTM D648 F ( C)
Rev 2 / Sept 2020
2020 Gougeon Brothers, Inc.
MECHANICAL PROPERTIES
HTP 182~HTP 284
HIGH-TEMP LAMINATING EPOXY
Property Standard Units
RT + 140 F (60 C) x 2hr +
275 F (135 C) x 12hr
POST CURE SCHEDULE
14,535(100)
94
14,500(100)
10,300(71)
4.42E+05(3.05)
5.3
4.06E+05(2.8)
Coefficient of Thermal ExpansionASTM E831
in/(in* F)
( m/(m* C)
2.98 E-05
(53.68
@ -22 F-86 F
(-30 C-30 C)
4.52 E-05
(81.32)
@ 86 F-248 F
(30 C-120 C)
THERMAL PROPERTIES
Property Standard Units
RT + 140 F (60 C) x 2hr +
275 F (135 C) x 12hr
Post cure 140 F (60 C) x 2 hr + 275 F (135 C) x 12 hr with
ramp rates no greater than 12 F/hr, to achieve maximum
properties. For larger parts, additional dwells may be required.
318 (159)
298 (148)
300 (149)
280 (138)
1
1 Hz, 3 C per minute.
2
Store PRO-SET Epoxy resins and hardeners at room temperature in sealed containers until shortly before use. As
with many high-performance epoxy resins, repeated exposure to low temperatures during storage may cause the
resin to crystallize. If this occurs, warm the resin to 125 F and stir to dissolve crystals. Hardeners may form
carbamation when exposed to CO
2 and moisture in the atmosphere for extended periods of time. Prevent carbamation
by protecting hardeners from exposure until immediately prior to processing.
10
30
50
70
90
110
130
50
100
150
200
250
300
0510152025303540
Temperature (
C)
Temperature (
F)
Time (Hours)