Property Standard Units
100g Pot Life ASTM D2471minutes
Viscosity MixedASTM D2196 cP
Viscosity (resin)ASTM D2196 cP
Viscosity (hardener)ASTM D2196 cP
Method Resin:Hardener
COMBINED FEATURES Weight 4.0:1
Weight Range 3.78:1 4.46:1
Volume 3.70:1
Volume Range 3.52:1 4.15:1
State Units 72 F (22 C)
Cured lb/gal (g/cc)9.8 (1.17)
2015 Gougeon Brothers, Inc.
HANDLING PROPERTIES
Technical Data
72 F (22 C)
15-19
2775
4,800
2,400
TOUGHENED LAMINATING EPOXY
MIX RATIO
100:25.0
Resin:Hardener
26.40:1 22.40:1
100:27.0
28.40:1 24.10:1
DENSITY
Test specimens were neat epoxy (without fiber reinforcement).
Typical values, not to be construed as specification.
Rev 4/ Dec 2015
Medium viscosity for good wet out of all
synthetic composite fabrics and core materials.
Extra Fast cure speed hardener provides a 25
minute working time at 72 F (22 C). A typical
laminate will be gelled in about 1 to 2 hours.
Room temperature cure properties suitable for
many composite components and structures.
T
g as high as 162 F (72 C) with proper post
cure providing excellent temperature stability
and great part cosmetics.
Cost effective, high performance epoxy
formulation for synthetic composite
manufacturing.
Quality-control tinting is available at no extra
charge; simply add “QC” after the product code
on your order.
Shelf life is 3 years for resin and 2 years for
hardener when properly stored
2
.
M1002
M2015
Hardness ASTM D2240Type D
Compression Yield ASTM D695psi (MPa)
Tensile Strength ASTM D638psi (MPa)
Tensile Modulus ASTM D638psi (GPa)
Tensile Elongation ASTM D638 %
Flexural Strength ASTM D790psi (MPa)
Flexural Modulus ASTM D790psi (GPa)
Tg DSC Onset 1st Heat ASTM E1356 F ( C)
Heat Deflection TemperatureASTM D648 F ( C)
Tg DSC Ultimate ASTM E1356 F ( C)
Rev 4/ Dec 2015
2015 Gougeon Brothers, Inc.
M1002~M2015
TOUGHENED LAMINATING EPOXY
MECHANICAL PROPERTIES
RT Gelation
+ 140 F (60 C)
x 8 hrs
RT Gelation
+ 180 F (82 C)
x 8 hrs
82 83 83 84 84
Property Standard Units
72 F (22 C)
x 2 wk
RT Gelation
+ 110 F (43 C)
x 8 hrs
RT Gelation
+ 125 F (52 C)
x 8 hrs
13,290(92) 13,800(95)
8,490(59) 8,670(60) 9,280(64) 10,000(69) 9,250(64)
14,000(97) 14,200(98) 13,600(94)
(3.12)4.80E+00(.) 4.53E+05(3.12)
4.2 3.9 3.9 4.1
4.68E+05(3.23)4.54E+05(3.13)4.52E+05
4.3
14,800(102) 15,819(109) 15,600(108) 15,700(108) 15,500(107)
4.64E+05(3.2) 4.53E+05(3.12)4.52E+05(3.12)4.49E+05(3.1) 4.53E+05(3.12)
THERMAL PROPERTIES
Property Standard Units
72 F (22 C)
x 2 wk
RT Gelation
+ 110 F (43 C)
x 8 hrs
RT Gelation
+ 125 F (52 C)
x 8 hrs
RT Gelation
+ 140 F (60 C)
x 8 hrs
RT Gelation
+ 180 F (82 C)
x 8 hrs
130 (54) 143 (62) 141 (61) 151 (66) 153 (67)
1
Additional post cure may be required; contact Technical Department for details.
2
Store PRO-SET Epoxy resins and hardeners at room temperature in sealed containers until shortly before use. As with many
high-performance epoxy resins, repeated exposure to low temperatures during storage may cause the resin to crystallize. If this
occurs, warm the resin to 125 F and stir to dissolve crystals. Hardeners may form carbamation when exposed to CO
2 and moisture
in the atmosphere for extended periods of time. Prevent carbamation by protecting hardeners from exposure until immediately prior
to processing.
129 (54) 142 (61) 148 (64) 152 (67) 155 (68)
162 (72)
Method
Weight
Volume
COMBINED FEATURES
State
Cured
Hardness
Compression Yield
Tensile Strength
Tensile Modulus
Tensile Elongation
Flexural Strength
Flexural Modulus
Tg DSC Onset 1st Heat F ( C) 175
Heat Deflection Temperature F ( C) 166
F ( C)
2015 Gougeon Brothers, Inc.
HANDLING PROPERTIES
Technical Data
Property Standard Units 72 F (22 C)
Viscosity (resin) ASTM D2196 cP 4,800
Viscosity (hardener)ASTM D2196 cP 40
100g Pot Life ASTM D2471 minutes 123-151
Viscosity Mixed ASTM D2196 cP 1,600
3.33:1 3.00:1 3.76:1 100:30.0 100:33.30 100:26.60
DENSITY
Units 72 F (22 C)
MIX RATIO
TOUGHENED LAMINATING EPOXY
Resin:Hardener Range Resin:Hardener Range
4.17:1 3.73:1 4.65:1 100:24.0 100:26.80 100:21.50
Property Standard Units
RT Gelation
+ 140 F (60 C)
x 8 hrs
RT Gelation
+ 180 F (82 C)
x 8 hrs
lb/gal (g/cc)9.81 (1.17)
MECHANICAL PROPERTIES
ASTM D2240 Type D 82 83
ASTM D695 psi (MPa)13,900(96) 13,800(95)
ASTM D638 psi (MPa)4.29E+05(2.96)3.86E+05(2.66)
ASTM D638 psi (MPa) 9,722(67) 9,500(66)
ASTM D638 % 4.5 6.4
ASTM D790 psi (MPa)18,500(128) 17,500(121)
THERMAL PROPERTIES
Property StandardUnits
RT Gelation
+ 140 F (60 C)
x 8 hrs
RT Gelation
+ 180 F (82 C)
x 8 hrs
ASTM D790 psi (MPa)5.56E+05(3.83)5.07E+05(3.5)
Ultimate Tg by DSC ASTM E1356 193(89)
1
Additional post cure may be required; contact Technical Department for details.
2
Store PRO-SET Epoxy resins and hardeners at room temperature in sealed containers until shortly before use. As with many
high-performance epoxy resins, repeated exposure to low temperatures during storage may cause the resin to crystallize. If this
occurs, warm the resin to 125 F and stir to dissolve crystals. Hardeners may form carbamation when exposed to CO
2 and moisture
in the atmosphere for extended periods of time. Prevent carbamation by protecting hardeners from exposure until immediately
prior to processing.
Test specimens were neat epoxy (without fiber reinforcement).
Typical values, not to be construed as specification.
Rev 4 / Dec 2015
Some separation may occur during storage. Stir resin before
mixing with hardener.
ASTM E1356 (79) 193(89)
ASTM D648 (74) 184(84)
Medium viscosity for good wet out of all
synthetic composite fabrics and core materials.
Extra Slow cure speed hardener provides 6 to
8 hours of working time at 72 F (22 C).
Elevated temperature cure is required;
thermal and mechanical properties suitable for
composite components and high temperature
tooling and molds.
T
g as high as 193 F (89 C) with proper post
cure providing excellent temperature stability
and great part cosmetics.
Cost effective, high performance epoxy
formulation for synthetic composite
manufacturing.
Quality-control tinting is available at no extra
charge; simply add “QC” after the product code
on your order.
Shelf life is 3 years for resin and 18 months for
hardener when properly stored
2
.
M1002
M2042
Method
Weight
Volume
COMBINED FEATURES
State
Cured
Hardness
Compression Yield
Tensile Strength
Tensile Modulus
Tensile Elongation
Flexural Strength
Flexural Modulus
Tg DSC Onset 1st Heat F ( C) 128
Heat Deflection Temperature F ( C) 125
F ( C)
2015 Gougeon Brothers, Inc.
HANDLING PROPERTIES
Technical Data
Property Standard Units 72 F (22 C)
Viscosity (resin) ASTM D2196 cP 4,800
Viscosity (hardener)ASTM D2196 cP 180
100g Pot Life ASTM D2471 minutes 25-31
Viscosity Mixed ASTM D2196 cP 2,200
3.57:1 3.46:1 4.07:1 100:28.0 100:28.90 100:24.60
DENSITY
Units 72 F (22 C)
MIX RATIO
TOUGHENED LAMINATING EPOXY
Resin:Hardener Range Resin:Hardener Range
4.17:1 4.07:1 4.78:1 100:24.0 100:24.60 100:20.90
Property Standard Units
72 F (22 C)
x 2 wk
RT Gelation
+ 140 F (60 C)
x 8 hrs
lb/gal (g/cc)9.81 (1.17)
MECHANICAL PROPERTIES
ASTM D2240 Type D 82 83
ASTM D695 psi (MPa)13,800(95) 14,600(101)
ASTM D638 psi (MPa)4.86E+05(3.35)4.59E+05(3.16)
ASTM D638 psi (MPa) 7,160(49) 9,600(66)
ASTM D638 % 2.0 3.4
ASTM D790 psi (MPa)12,500(86) 18,300(126)
THERMAL PROPERTIES
Property StandardUnits
72 F (22 C)
x 2 wk
RT Gelation
+ 140 F (60 C)
x 8 hrs
ASTM D790 psi (MPa)4.72E+05(3.25)5.96E+05(4.11)
Ultimate Tg by DSC ASTM E1356 172(78)
1
Additional post cure may be required; contact Technical Department for details.
2
Store PRO-SET Epoxy resins and hardeners at room temperature in sealed containers until shortly before use. As with many
high-performance epoxy resins, repeated exposure to low temperatures during storage may cause the resin to crystallize. If this
occurs, warm the resin to 125 F and stir to dissolve crystals. Hardeners may form carbamation when exposed to CO
2 and moisture
in the atmosphere for extended periods of time. Prevent carbamation by protecting hardeners from exposure until immediately
prior to processing.
Test specimens were neat epoxy (without fiber reinforcement).
Typical values, not to be construed as specification.
Rev 4 / Dec 2015
Some separation may occur during storage. Stir resin before
mixing with hardener.
ASTM E1356 (53) 161(72)
ASTM D648 (52) 159(71)
Medium viscosity for good wet out of all
synthetic composite fabrics and core materials.
Fast cure speed hardener provides 1.5 to 2.5
hours of working time at 72 F (22 C).
Room temperature cure properties suitable for
many composite components and structures.
T
g as high as 172 F (78 C) with proper post
cure providing excellent temperature stability
and great part cosmetics.
Cost effective, high performance epoxy
formulation for synthetic composite
manufacturing.
Quality-control tinting is available at no extra
charge; simply add “QC” after the product code
on your order.
Shelf life is 3 years for resin and 2 years for
hardener when properly stored
2
.
M1002
M2043
Method
Weight
Volume
COMBINED FEATURES
State
Cured
Hardness
Compression Yield
Tensile Strength
Tensile Modulus
Tensile Elongation
Flexural Strength
Flexural Modulus
Tg DSC Onset 1st Heat F ( C) 127
Heat Deflection Temperature F ( C) 124
F ( C)
2015 Gougeon Brothers, Inc.
HANDLING PROPERTIES
Technical Data
Property Standard Units 72 F (22 C)
Viscosity (resin) ASTM D2196 cP 4,800
Viscosity (hardener)ASTM D2196 cP 75
100g Pot Life ASTM D2471 minutes 48-60
Viscosity Mixed ASTM D2196 cP 1,400
3.45:1 3.25:1 3.82:1 100:29.0 100:30.80 100:26.20
DENSITY
Units 72 F (22 C)
MIX RATIO
TOUGHENED LAMINATING EPOXY
Resin:Hardener Range Resin:Hardener Range
4.17:1 3.91:1 4.61:1 100:24.0 100:25.60 100:21.70
Property Standard Units
72 F (22 C)
x 2 wk
RT Gelation
+ 140 F (60 C)
x 8 hrs
lb/gal (g/cc)9.81 (1.17)
MECHANICAL PROPERTIES
ASTM D2240 Type D 80 84
ASTM D695 psi (MPa)13,600(94) 14,100(97)
ASTM D638 psi (MPa)4.76E+05(3.28)4.52E+05(3.12)
ASTM D638 psi (MPa) 7,550(52) 9,690(67)
ASTM D638 % 2.1 4.0
ASTM D790 psi (MPa)12,400(85) 14,100(97)
THERMAL PROPERTIES
Property StandardUnits
72 F (22 C)
x 2 wk
RT Gelation
+ 140 F (60 C)
x 8 hrs
ASTM D790 psi (MPa)4.73E+05(3.26)5.99E+05(4.13)
Ultimate Tg by DSC ASTM E1356 162(72)
1
Additional post cure may be required; contact Technical Department for details.
2
Store PRO-SET Epoxy resins and hardeners at room temperature in sealed containers until shortly before use. As with many
high-performance epoxy resins, repeated exposure to low temperatures during storage may cause the resin to crystallize. If this
occurs, warm the resin to 125 F and stir to dissolve crystals. Hardeners may form carbamation when exposed to CO
2 and
moisture in the atmosphere for extended periods of time. Prevent carbamation by protecting hardeners from exposure until
immediately prior to processing.
Test specimens were neat epoxy (without fiber reinforcement).
Typical values, not to be construed as specification.
Rev 4 / Dec 2015
Some separation may occur during storage. Stir resin before
mixing with hardener.
ASTM E1356 (53) 153(67)
ASTM D648 (51) 162(72)
Medium viscosity for good wet out of all
synthetic composite fabrics and core materials.
Medium cure speed hardener provides 2.5 to
4.5 hours of working time at 72 F (22 C).
Room temperature cure properties suitable for
many composite components and structures.
T
g as high as 162 F (72 C) with proper post
cure providing excellent temperature stability
and great part cosmetics.
Cost effective, high performance epoxy
formulation for synthetic composite
manufacturing.
Quality-control tinting is available at no extra
charge; simply add “QC” after the product code
on your order.
Shelf life is 3 years for resin and 2 years for
hardener when properly stored
2
.
M1002
M2044
Method
Weight
Volume
COMBINED FEATURES
State
Cured
Hardness
Compression Yield
Tensile Strength
Tensile Modulus
Tensile Elongation
Flexural Strength
Flexural Modulus
Tg DSC Onset 1st Heat F ( C) 176
Heat Deflection Temperature F ( C) 170
F ( C)
2015 Gougeon Brothers, Inc.
HANDLING PROPERTIES
Technical Data
Property Standard Units 72 F (22 C)
Viscosity (resin) ASTM D2196 cP 4,800
Viscosity (hardener)ASTM D2196 cP 115
100g Pot Life ASTM D2471 minutes 72-88
Viscosity Mixed ASTM D2196 cP 2,100
3.57:1 3.16:1 3.95:1 100:28.0 100:31.60 100:25.30
DENSITY
Units 72 F (22 C)
MIX RATIO
TOUGHENED LAMINATING EPOXY
Resin:Hardener Range Resin:Hardener Range
4.17:1 3.83:1 4.78:1 100:24.0 100:26.10 100:20.90
Property Standard Units
RT Gelation
+ 140 F (60 C)
x 8 hrs
RT Gelation
+ 180 F (82 C)
x 8 hrs
lb/gal (g/cc)9.81 (1.17)
MECHANICAL PROPERTIES
ASTM D2240 Type D 83 83
ASTM D695 psi (MPa)14,100(97) 13,900(96)
ASTM D638 psi (MPa)4.33E+05(2.99)3.94E+05(2.72)
ASTM D638 psi (MPa)10,000(69) 9,590(66)
ASTM D638 % 5.5 5.7
ASTM D790 psi (MPa)18,800(130) 1,770(12)
THERMAL PROPERTIES
Property StandardUnits
RT Gelation
+ 140 F (60 C)
x 8 hrs
RT Gelation
+ 180 F (82 C)
x 8 hrs
ASTM D790 psi (MPa)5.55E+05(3.83)5.14E+05(3.54)
Ultimate Tg by DSC ASTM E1356 197(92)
1
Additional post cure may be required; contact Technical Department for details.
2
Store PRO-SET Epoxy resins and hardeners at room temperature in sealed containers until shortly before use. As with many
high-performance epoxy resins, repeated exposure to low temperatures during storage may cause the resin to crystallize. If this
occurs, warm the resin to 125 F and stir to dissolve crystals. Hardeners may form carbamation when exposed to CO
2 and
moisture in the atmosphere for extended periods of time. Prevent carbamation by protecting hardeners from exposure until
immediately prior to processing.
Test specimens were neat epoxy (without fiber reinforcement).
Typical values, not to be construed as specification.
Rev 4 / Dec 2015
Some separation may occur during storage. Stir resin before
mixing with hardener.
ASTM E1356 (80) 197(92)
ASTM D648 (77) 189(87)
Medium viscosity for good wet out of all
synthetic composite fabrics and core materials.
Slow cure speed hardener provides 4.5 to 6
hours of working time at 72 F (22 C).
Elevated temperature cure is required;
thermal and mechanical properties suitable for
composite components and high temperature
tooling and molds.
T
g as high as 197 F (92 C) with proper post
cure providing excellent temperature stability
and great part cosmetics.
Cost effective, high performance epoxy
formulation for synthetic composite
manufacturing.
Quality-control tinting is available at no extra
charge; simply add “QC” after the product code
on your order.
Shelf life is 3 years for resin and 18 months for
hardener when properly stored
2
.
M1002
M2046