SIL66BE-249ALH_TDS.pdf

SIL66BE-249ALH
Laminating Resin
(Surf/Sail Board)
Technical Data Sheet
INTERPLASTIC CORPORATION
3535 Latonia Avenue
Fort Wright, KY 41015-0159
859.292.7400Fax: 859.292.7424
www.interplastic.com
SIL66BE-249ALH is a surfboard laminating resin containing 35% maximum styrene. It contains
UV stabilizer and does not contain wax.
TYPICAL RESIN PROPERTIES @ 77 F RESULTS
Brookfield Viscosity @ 20 rpm, cps 410 560
Brookfield Spindle No. (RV) 2
Catalyst, %, DDM-9 MEK-P 1.00
Gel Time, minutes:seconds 11:00 19:00
Gel to Peak Time, minutes:seconds 9:00 19:00
Peak Exotherm, F 275 315
Solids, % 65.0 68.0
UV Test Positive
MECHANICAL PROPERTIES OF NEAT CURED RESIN RESULTS
Property:
ASTM Test Method
Psi Mpa
Flexural Strength D-790 20,200 139.3
Flexural Modulus D-790 5.85 x 10
5
4033
Tensile Strength D-638 10,500 72.4
Tensile Modulus D-638 6.17 x 10
5
4254
Tensile Elongation D-638 2.1 %
Heat Distortion Temperature D-648 149 F / 65.0 C
Hardness, Barcol 934-1 D-2583 42 – 44
Revised: 7/06
All specifications and properties specified above are approximate. Specifications and properties of material delivered may vary slightly from
those given above. Interplastic Corporation makes no representations of fact regarding the material except those specified above. No person
has any authority to bind Interplastic Corporation to any representation except those specified above. Final determination of the suitability of
the material for the use contemplated is the sole responsibility of the Buyer. The Thermoset Resins Division’s technical sales representatives
will assist in developing procedures to fit individual requirements.