by | Sep 27, 2025
HexPly
M77
80 C – 160 C curing epoxy matrix
Product Data Sheet
Description
HexPly
M77 is a formulated epoxy resin matrix, specifically designed for prepreg applications and short cure
cycles. It is a very versatile matrix, allowing a range of processing temperatures from 80 C up to 160 C.
HexPly
M77 is based on a modified epoxy resin. It can be pre-impregnated into carbon, glass or aramid fibers
and exhibits a significant long out-life at room temperature.
Benefits and Features
High toughened epoxy
Excellent tack life
Suitable for a range of pressures (1 to 10 bar)
Short cure cycle at 120 160 C
Good surface finish
Medium tack and excellent drapability
Controlled flow for ease of processing
Long out-life at room temperature
Resin Matrix Properties
T
g
after 130 @15min: 135 C (DSC 25-250 C, 10 C/min)
Density: 1.1 1.2g/cm
Color: Milky
1
Copyright 2016 Hexcel Corporation All Rights Reserved.
Title
Subtitle Product Data Sheet
2
Viscosity
Heating Rate [ C/min] Min. Viscosity * [Pas] Temperature @ * [ C] Time @ * [min]
0.5 15 85 90
2.5 4 100 25
10 3 120 8
25 1.5 135 3
40 10070 130
Complex Viscosity *
1
10
100
1000
10000
100000
1000000
Dyn. 0.5 C/min
40 70 100 130 160
1
100
10
1000
10000
100000
1000000
Dyn. 2.5 C/min
40 10070 130 160 190
1
10
100
1000
10000
100000
1000000
Dyn. 10 C/min
40 70 100 130 160 190
1
100
10
1000
10000
100000
1000000
Dyn. 25 C/min
Temperature [ C]
1
100
10
1000
10000
100000
1000000
Iso 75 C
Iso 85 C
Iso 100 C
Iso 145 C
Complex Viscosity * [Pas]
0 250 500 750 1000 1250 1500 1750 2000 2250 2500 2750 3000
Time [s]
HexPly
M77
80 C – 160 C curing epoxy matrix
Copyright 2016 Hexcel Corporation All Rights Reserved.
Title
Subtitle Product Data Sheet
3
Curing Conditions
The ideal cure cycle is 7 min at 120 C and at a pressure >5bar . Alternative cure cycles can be used:
Temperature Time
110 C 18 min
120 C 7 min
130 C 5 min
140 C 3 min
150 C 2 min
160 C 1.5 min
Prepreg Types and Cured Prepreg Mechanical Properties
Mechanical Properties are based on 130 C cure for 10 min, at 5 bar pressure.
Reinforcement Prepreg data Mechanical data
Fiber
Fabric
Weave
Style
Fabric
Weight
[g/m ]
Fabric
Direction
0 /90
[g/m ]
Weight
[g/m ]
( 5%)
Resin
Content
[%] ( 3)
Tensile
Strength
[MPa]
Tensile
Modulus
[GPa]
ILSS
[MPa]
M77/55%/48P/G Glass plain 47 26/21 104 55 540 28 55
M77/52%/106P/G Glass plain106 54/52 221 52 480 27 67
M77/45%/160P/G Glass plain155 81/74 282 45
M77/38%/395P/G Glass plain386 204/182 623 38
M77/40%/LT570/G+F Glass
non
woven +
fleece
560
432/75
fleece 35
848 35
M77/42%/200T2/CHS-3K Carbon twill200 100/100 345 42
M77/42%/600T2/CHS Carbon twill600 300/3001034 42
M77/38%/UD150/CHS Carbon UD 150 90/0 242 38
M77/39%/UD600/CHS Carbon UD 600 600/0 984 39 2400 140 78
HexPly
M77
80 C – 160 C curing epoxy matrix
Copyright 2016 Hexcel Corporation All Rights Reserved.
Title
Subtitle
2016 Hexcel Corporation All rights reserved. Hexcel Corporation and its subsidiaries ( Hexcel ) believe that the technical data and other information
provided herein was materially accurate as of the date this document was issued. Hexcel reserves the right to update, revise or modify such technical data and
information at any time. Any performance values provided are considered representative but do not and should not constitute a substitute for your own testing of
the suitability of our products for your particular purpose. Hexcel makes no warranty or representation, express or implied, including but not limited to
the implied warranties of merchantability and fitness for a particular purpose, and disclaims any liability arising out of or related to, the use of or
reliance upon any of the technical data or information contained in this document.
For more information
Hexcel is a leading worldwide supplier of composite materials to aerospace and industrial markets.
Our comprehensive range includes:
-or < : Xuotes orders and product infor Tation call toll free 6 4 -or other worldwide sales office
telephone numbers and a full address list, please go to:
http: www.hexcel.com contact salesoffice
HexTow
carbon fibers
HexForce
reinforcements
HexPly
prepregs
HexMC
molding compounds
HexFlow
RTM resins
Redux
adhesives
HexTOOL
tooling materials
HexWeb
honeycombs
Acousti-CAP
sound attenuating
honeycomb
Engineered core
Engineered products Product Data Sheet
4
Storage and Handling
Shelf Life : 18 months
Out Life : 6 weeks (42 days)
Shelf Life: the maximum storage life for HexPly
prepreg, upon receipt by the customer, when stored continuously, in a sealed moisture-proof bag, at -18 C/0 F.
To accurately establish the exact expiry date, consult the box label.
Out Life: the maximum accumulated time allowed at room temperature between removal from the freezer and cure.
Prepreg should be stored as received in a cool dry place or in a refrigerator. After removal from refrigerator storage, prepreg
should be allowed to reach room temperature before opening the polyethylene bag, thus preventing condensation. (A full reel
in its packing can take up to 48 hours).
HexPly
M77
80 C - 160 C curing epoxy matrix
FTU-296-JA16
HexForce
TM
282
Carbon Fabric
Style 282 US System
Type of Yarns Warp Yarn: 3K Carbon, 33MSI
Fill Yarn: 3K Carbon, 33MSI
Fabric Weight, Dry 5.70 oz/yd
2
193 g/m
2
Weave Style Plain
Construction
Nominal Construction Warp Count: 12.5/in 4.92/cm
Fill Count: 12.5/in 4.92/cm
Fabric Thickness 10. 10 mil 0.26 mm
Important
All information is believed to be accurate but is given without acceptance of liability. All values have been generated
from limited data. The values listed for weight, thickness and breaking strengths are typical greige values, unless
otherwise noted. Users should make their own assessment of the suitability of any product for the purpose required.
All sales are made subject to our standard terms of sales which include limitations on liability and other important
terms. The fabric style listed may not be available from inventory and minimum order quantities may apply.
For More Information
Hexcel is a leading worldwide supplier of composite materials to aerospace and other demanding industries.
Our comprehensive product range includes:
Carbon Fiber
Reinforced Fabrics
Carbon, Glass, Aramid and Hybrid Prepregs
RTM Materials
HexTOOL
composite tooling material
Structural Film Adhesives
Honeycomb Cores
Engineered Core
1913 North King Street
Seguin, Texas 78155
Phone: 830-379-1580
Fax: 830-379-9544
Customer Service Toll Free: 1- 866-601-5430
For European sales office numbers and a full address list, please go to:
http://www.hexcel.com/contact/salesoffices
Copyright 2014 Hexcel and Hexcel logo are registered trademarks of Hexcel Corporation, Stamford, Connecticut.
HexForce is a trademark of Hexcel Corporation, Stamford, Connecticut.
June 2014
by | Sep 27, 2025
Document No.
MKT-002
PE 80Dtex
N/A
Layer
-45
+45
Liner (Upper)
Stabilisation Thread – 90
Stabilisation Thread – 0 68tex Glass
N/A
Stitch Fibre
MC8481270
Sigmatex Product Data Sheet
Description410GSM/-45+45/T700SC 12K 50C/1270mm
Fabric StyleBi-Axial
From global locations, Sigmatex supplies carbon fibre textiles including 3D, Spread Tow, Innegra, Recycled, Unidirectional, Multiaxial, and 2D across a broad
spread of industries ranging from the world s top supercar manufacturers to aerospace companies. In all cases, Sigmatex helps its customers to achieve
improved product performance through lightweight strength. Sigmatex was established in 1986 and has specialised in converting carbon fibre since then.
For more information see www.sigmatex.com or contact a member of the sales team on +44 (0) 1928 570 050
This is an uncontrolled document and may be subject to change.
*Tolerances on fabric properties can be provided on request.
“Layer” Mass
Warp Bow 5mm per 1m length (max)
“Stitch” Mass 6
As per customer requirements
Width 1270 mm
“Stabilisation” Mass
gsm
Typical Length (lm)See Above
“All-Up” Mass 410 gsm
Property
Bow
Nominal Weight (gsm)
T700SC 12K 50C 200
Fibre Description
T700SC 12K 50C 200
Spacing 0 22.5mm
Spacing 90 N/A
Stitch Pattern Chain
Axis angle 1.5 per m width
See Above
Construction Verify
Thickness Verify
N/ALiner (Lower)
Requirement
Fabric Properties
Property Nominal Units
Printed versions of this document
may not be at the latest issue level.
Author:
K. Gardner / G. Shaw
Page 1 of 1
MKT-002 Iss.002 Fabric Data Sheet
by | Sep 27, 2025
by | Sep 27, 2025
HexPly
M10E
Epoxy Resin System
Product Data Sheet
Description
HexPly
M10E is an epoxy resin system preimpregnated into aramid, glass or graphite multiaxial fabrics and
unidirectional fibers. HexPly
M10E prepregs are recommended for the production of low cost, large thick-
sectioned industrial structures.
Features
Flexible Cure Cycle (185 F to 300 F)
Vacuum Bag or Autoclave Cure
High Flow, Low Viscosity System
Medium to High Tack
Can be Stored at Room Temperature for 60 Days
Optically Clear Resin
Properties
Glass transition temperature: Dry, 241 F, Wet, 194 F
Resin density 1.19
Barcol Hardness 33
Availability
Form
Hexcel
Designation
Fiber
Fiber Areal
Wt. G/m
2
Weave
Count
Warp x Fill
Available Widths
Standard Widths
in (cm)
Fabric PW 282 3K 197 Plain weave12 by 12 50
Graphite UD
AS3C-S
150-300 GSM
AS3C-S
12K
150-300 12 , 24
Physical Properties
Property Carbon Tapes
Tensile and compressiveM10E 37% AS3C-S, 300 GSM
1
Copyright 2020 Hexcel Corporation All Rights Reserved.
Product Data Sheet
2
Mechanical Properties
Property Temperature Condition Carbon Tapes
Tensile Strength Room Temp. Dry 293 ksi
Tensile Modulus Room Temp. Dry 17.6 Msi
Tensile Strain Room Temp. Dry 1.54%
Compression Strength Room Temp. Dry 154 ksi
Compression Modulus Room Temp. Dry 17.0 Msi
Compression Strain (calculated) Room Temp. Dry 0.91%
Cure Cycle
185 F, 14 hours
200 F, 120 minutes
250 F, 30 minutes
300 F, 8 minutes
Cure Procedure
Vacuum bag or autoclave cure using ramp rate of 2-5 F per minute. Recommend hold at 250 F for 30 minutes.
Storage (maximum, from date of manufacture)
At 0 F, 18 months
At 41 F, 6 months
At 72 F, 2 months
FTI-329-MY20
HexPly
M10E
epoxy resin system
2020 Hexcel Corporation All rights reserved. Hexcel Corporation and its subsidiaries ( Hexcel ) believe that the technical data and other information
provided herein was materially accurate as of the date this document was issued. Hexcel reserves the right to update, revise or modify such technical data and
information at any time. Any performance values provided are considered representative but do not and should not constitute a substitute for your own testing
of the suitability of our products for your particular purpose. Hexcel makes no warranty or representation, express or implied, including but not limited to the
implied warranties of merchantability and fitness for a particular purpose, and disclaims any liability arising out of or related to, the use of or reliance upon any of
the technical data or information contained in this document.
For more information
Hexcel is a leading worldwide supplier of composite materials to aerospace and industrial markets.
Our comprehensive range includes:
For U.S. quotes, orders and product information call toll-free 1-800-688-7734. For other worldwide sales office
telephone numbers and a full address list, please go to:
https://www.hexcel.com/contact
HexTow
carbon fibers
HexForce
reinforcements
HiMax
multiaxial
reinforcements
HexPly
prepregs
HexMC
-i molding compounds
HexFlow
RTM resins
HexBond
adhesives
HexTool
tooling materials
HexWeb
honeycombs
Acousti-Cap
sound
attenuating honeycomb
Engineered core
Engineered products
Polyspeed
laminates
& pultruded profiles
HexAM
additive manufacturing
by | Sep 27, 2025
HexPly
M10E
Epoxy Resin System
Product Data Sheet
Description
HexPly
M10E is an epoxy resin system preimpregnated into aramid, glass or graphite multiaxial fabrics and
unidirectional fibers. HexPly
M10E prepregs are recommended for the production of low cost, large thick-
sectioned industrial structures.
Features
Flexible Cure Cycle (185 F to 300 F)
Vacuum Bag or Autoclave Cure
High Flow, Low Viscosity System
Medium to High Tack
Can be Stored at Room Temperature for 60 Days
Optically Clear Resin
Properties
Glass transition temperature: Dry, 241 F, Wet, 194 F
Resin density 1.19
Barcol Hardness 33
Availability
Form
Hexcel
Designation
Fiber
Fiber Areal
Wt. G/m
2
Weave
Count
Warp x Fill
Available Widths
Standard Widths
in (cm)
Fabric PW 282 3K 197 Plain weave12 by 12 50
Graphite UD
AS3C-S
150-300 GSM
AS3C-S
12K
150-300 12 , 24
Physical Properties
Property Carbon Tapes
Tensile and compressiveM10E 37% AS3C-S, 300 GSM
1
Copyright 2020 Hexcel Corporation All Rights Reserved.
Product Data Sheet
2
Mechanical Properties
Property Temperature Condition Carbon Tapes
Tensile Strength Room Temp. Dry 293 ksi
Tensile Modulus Room Temp. Dry 17.6 Msi
Tensile Strain Room Temp. Dry 1.54%
Compression Strength Room Temp. Dry 154 ksi
Compression Modulus Room Temp. Dry 17.0 Msi
Compression Strain (calculated) Room Temp. Dry 0.91%
Cure Cycle
185 F, 14 hours
200 F, 120 minutes
250 F, 30 minutes
300 F, 8 minutes
Cure Procedure
Vacuum bag or autoclave cure using ramp rate of 2-5 F per minute. Recommend hold at 250 F for 30 minutes.
Storage (maximum, from date of manufacture)
At 0 F, 18 months
At 41 F, 6 months
At 72 F, 2 months
FTI-329-MY20
HexPly
M10E
epoxy resin system
2020 Hexcel Corporation All rights reserved. Hexcel Corporation and its subsidiaries ( Hexcel ) believe that the technical data and other information
provided herein was materially accurate as of the date this document was issued. Hexcel reserves the right to update, revise or modify such technical data and
information at any time. Any performance values provided are considered representative but do not and should not constitute a substitute for your own testing
of the suitability of our products for your particular purpose. Hexcel makes no warranty or representation, express or implied, including but not limited to the
implied warranties of merchantability and fitness for a particular purpose, and disclaims any liability arising out of or related to, the use of or reliance upon any of
the technical data or information contained in this document.
For more information
Hexcel is a leading worldwide supplier of composite materials to aerospace and industrial markets.
Our comprehensive range includes:
For U.S. quotes, orders and product information call toll-free 1-800-688-7734. For other worldwide sales office
telephone numbers and a full address list, please go to:
https://www.hexcel.com/contact
HexTow
carbon fibers
HexForce
reinforcements
HiMax
multiaxial
reinforcements
HexPly
prepregs
HexMC
-i molding compounds
HexFlow
RTM resins
HexBond
adhesives
HexTool
tooling materials
HexWeb
honeycombs
Acousti-Cap
sound
attenuating honeycomb
Engineered core
Engineered products
Polyspeed
laminates
& pultruded profiles
HexAM
additive manufacturing
by | Sep 27, 2025
HexForce
TM
HMGP200-P ZB
Carbon Fabric
Style HMGP200- P ZB US System
Type of Yarns Warp Yarn: HEXCEL HM63 12K GP
Fill Yarn: HEXCEL HM63 12K GP
Fabric Weight, Dry 5.89 oz/yd
2
200 g/m
2
Weave Style Plain
Finish ZB
Construction
Nominal Construction Warp Count: 6.0/in 15.24/cm
Fill Count: 6.0/in 15.24/cm
Important
All information is believed to be accurate but is given without acceptance of liability. All values have been generated
from limited data. The values listed for weight, thickness and breaking strengths are typical greige values, unless
otherwise noted. Users should make their own assessment of the suitability of any product for the purpose required.
All sales are made subject to our standard terms of sales which include limitations on liability and other important
terms. The fabric style listed may not be available from inventory and minimum order quantities may apply.
For More Information
Hexcel is a leading worldwide supplier of composite materials to aerospace and other demanding industries.
Our comprehensive product range includes:
Carbon Fiber
Reinforced Fabrics
Carbon, Glass, Aramid and Hybrid Prepregs
RTM Materials
HexTOOL
composite tooling material
Structural Film Adhesives
Honeycomb Cores
Engineered Core
1913 North King Street
Seguin, Texas 78155
Phone: 830-379-1580
Fax: 830-379-9544
Customer Service Toll Free: 1- 866-601-5430
For European sales office numbers and a full address list, please go to:
http://www.hexcel.com/contact/salesoffices
Copyright 2014 Hexcel and Hexcel logo are registered trademarks of Hexcel Corporation, Stamford, Connecticut.
HexForce is a trademark of Hexcel Corporation, Stamford, Connecticut.
June 2014
by | Sep 27, 2025
Inspired by Innovation :: Driven by Excellence
BGF INDUSTRIES, INC.
3802 Robert Porcher Way Greensboro, North Carolina 27410 USA
336-545-0011 fax: 336-545-0233 toll free: 800-476-4845
www.bgf.com
info@bgf.com
STYLE: 7590
FINISH: 504 Volan
WEAVE: 2×2 RH Twill
WARP YARNS: ECG 75 1/2
FILL YARNS: ECG 75 1/2
COUNT (ends x picks/inch): 18×18
WEIGHT (osy): 5.8
Information herein is based on BGF’s testing procedures and standards which we believe are accurate and reliable. BGF
makes no warranties as to any other characteristics of the products, their fitness for a particular purpose of the customer or
infringement of any patent for any particular use by the customer.
PRODUCT INFORMATION
STYLE 7590
by | Sep 27, 2025
HexPly
M77HF
quick cure epoxy system for industrial applications
Product Data Sheet
Description
HexPly
M77HF prepreg is a fiber-reinforced modified epoxy resin system specifically designed for bladder
molding or sheet wrap tube applications. Unique chemistry provides fully cured parts in only three minutes at
300 F (149 C).
Features
Quick cure, three minutes at 300 F (149 C)
Available in wide variety of carbon or glass tapes and fabrics
High temperature stability for hot de-mold
Low viscosity, 10 poise at 230 F (110 C)
Applications
Neat Resin Properties
Neat Resin Property HexPly
M77HF
Specific Gravity 1.34
Glass Transition Temperature-DMTA, F ( C) 266 (130)
Tensile Strength, ksi (MPa) 11.8 (81)
Tensile Modulus, Msi (GPa) 0.50 (3.45)
Tensile Strain, % 3.7
K
1C
Fracture Toughness, ksi-in
1/2
(MPa-m
1/2
) 1.28 (1.41)
Cure Time at 300 F, minutes 3
Cure Time at 275 F, minutes 5
Cure Time at 225 F, minutes 30
Gel Time vs. Temperature
1
Golf Shafts
Bicycle Components
Hockey Sticks
Arrow Shafts
Fishing Rods
Prosthetics
Tool Temp Gel Time Cure Time in V (poise)
250 6.5 10
260 4 6 8
275 3 5 5
250 260 275 300
Product Data Sheet
2
Viscosity at Different Heat Up Rates
Availability
HexPly
M77HF is available in natural color, black and green and a wide variety of carbon or glass tapes and
fabrics. The currently made products are:
Form
Hexcel
Designation
Fiber
Fiber Areal
Wt. g/m
2
Weave
Count
Warp x Fill
Widths
Available In
(cm)
Resin
Content
%
Glass
Fabric
6543GL/M77HF-
12G
SCG 75 1/2 x
ECE 225 1/0
288 4H Satin 48 x 30 38 (96.5) 32
6557GL/M77HF-
12G
SCG 150 1/2 x
ECE 225 1/0
180 4H Satin 57 x 30 38 (96.5) 33
7781GL/M77HF-7B ECDE 75 1/0 301 8H Satin 57 x 54 50 (127) 45
Carbon
Fabric
W3X 282/M77HFS 3K 33MSI 197 Plain 12 x 12 50 (127) 40
Carbon
Tape
AS4AGP6K/M77HF 6K 80 Tape n/a 24 (61) 38
AS4AGP12K/
M77HF
12K 120, 150 Tape n/a 24 (61) 38
IM2C-GS/M77HF IM2C-GS 110 Tape n/a 24 (61) 40
HexPly
M77HF
quick cure epoxy system for industrial applications
Product Data Sheet
3
Mechanical Properties
Prepreg
CHS/M77HF;
35%;150AW
MS40/M77HF;
31%;120AW
IM4/M77HF;
31%;120AW
CHS24K/M77HF;
36%;150AW
Fiber AS4C MS40 IM4 T600
FAW (gsm) 150 120 120 150
Tensile Strength,
ksi (GPa)
336 (2.32) 372 (2.56) 323 (2.23)
329 (2.27)
Tensile Modulus,
Msi (GPa)
18.1 (125) 26.7 (184) 21.1 (145)
17.1 (118)
Compression Strength,
ksi (GPa)
218 (1.50) 233 (1.61) 222 (1.53)
240 (1.65)
Compression Modulus,
Msi (GPa)
16.9 (117) 24.3 (168) 20.0 (138)
17.8 (123)
Short Beam Shear,
ksi (MPa)
12.2 (84.1) 12.2 (84.1) 12.4 (85.5)
12.9 (88.9)
Flexural Strength,
ksi (Gpa)
191 (1.32) 193 (1.33) 203 (1.40)
214 (1.48)
Flexural Modulus,
Msi (GPa)
16.9 (117) 24 (165) 19.2 (132)
16.5 (114)
1. Normalized to 55% fiber volume 2.75 F, dry.
Cure Cycle
HexPly
M77HF is designed to be cured using bladder molding, cello wrap, compression molding, or autoclave
conditions. The standard autoclave cure is 10 minutes at 250 F (121 C) with 85 psig minimum pressure.
*At higher elevations 22 inches Hg may be impossible to reach, in which case 20 inches Hg is permissible.
Alternative Cure Cycles:
1) 3 minutes at 300 F (149 C)
2) 6 minutes at 260 F (127 C)
3) 10 minutes at 250 F (121 C)
300
250
0 20 40 60 80 100 130
200
150
100
50
0
Time (minutes)
Hold 10 min
250 F
120 F
Heat-up
2-5 F/min
Cool-down
5 F/min
22 F in Hg vacuum to start;
Vent when pressure reaches 20 psig
85-100 psig
HexPly
M77HF
quick cure epoxy system for industrial applications
Product Data Sheet
4
Storage
Shelf Life: 18 months at 0 F (-18 C) (maximum, from date of manufacture)
Out Life: 30 days at 73 F (23 C)
Tack Life: 10 days at 73 F (23 C)
Storage Conditions
HexPly
M77HF prepregs should be stored as received in a cool dry place or in a refrigerator. After removal from
refrigerator storage, prepreg should be allowed to reach room temperature before opening the polythene bag,
thus preventing condensation. (A full creel in its packaging can take up to 48 hours).
Precautions for Use
The usual precautions when handling uncured synthetic resins and fine fibrous materials should be observed,
and a Safety Data Sheet is available for this product. The use of clean disposable inert gloves provides protection
for the operator and avoids contamination of material and components.
Shipping
Prepreg is generally shipped in a sealed polyethylene bag in refrigerated transportation or in containers with dry ice.
Disposal of Scrap
Disposal of this material should be in a secure landfill in accordance with state and federal regulations.
FTI 409 ST22
HexPly
M77HF
quick cure epoxy system for industrial applications
2022 Hexcel Corporation All rights reserved. Hexcel Corporation and its subsidiaries ( Hexcel ) believe that the technical data and other information
provided herein was materially accurate as of the date this document was issued. Hexcel reserves the right to update, revise or modify such technical data and
information at any time. Any performance values provided are considered representative but do not and should not constitute a substitute for your own testing
of the suitability of our products for your particular purpose. Hexcel makes no warranty or representation, express or implied, including but not limited to the
implied warranties of merchantability and fitness for a particular purpose, and disclaims any liability arising out of or related to, the use of or reliance upon any of
the technical data or information contained in this document.
For more information
Hexcel is a leading worldwide supplier of lightweight composite materials to aerospace and industrial markets.
Our comprehensive range includes:
For U.S. quotes, orders and product information call toll-free 1-800-688-7734. For other worldwide sales office
telephone numbers and a full address list, please go to:
https://www.hexcel.com/contact
HexTow
carbon fibers
HexForce
reinforcements
HiMax
multiaxial
reinforcements
HexPly
prepregs
HexMC
-i molding compounds
HexFlow
RTM resins
HexBond
adhesives
HexTool
tooling materials
HexWeb
honeycomb
Acousti-Cap
sound
attenuating honeycomb
Engineered core
Engineered products
Polyspeed
laminates
& pultruded profiles
HexAM
additive manufacturing
by | Sep 27, 2025
HexForce
GA130
Carbon Fabric
Product Data
STYLE GA130 US System
Type of Yarns Warp Yarn: 12K Carbon, 33MSI
Fill Yarn: Proprietary Heatset
Fabric Weight, Dry 13.20 oz/yd
2
448 g/m
2
Weave Style Plain Heatset
CONSTRUCTION
Nominal Construction Warp Count: 14/in
Fill Count: 4/in
Fabric Thickness 16.9 mil 0.43 mm
IMPORTANT
All information is believed to be accurate but is given without acceptance of liability. All values have been
generated from limited data. The values listed for weight, thickness and breaking strengths are typical greige
values, unless otherwise noted. Users should make their own assessment of the suitability of any product for
the purpose required. All sales are made subject to our standard terms of sales which include limitations on
liability and other important terms. The fabric style listed may not be available from inventory and minimum
order quantities may apply.
FOR FURTHER INFORMATION, PLEASE CONTACT US
1913 North King Street
Seguin, Texas 78155
Phone: 830-379-1580
Fax: 830-379-9544
Customer Service Toll Free: 1-866-601-5430
For European sales office numbers and a full address list, please go to:
http://www.hexcel.com/contact/salesoffices
Hexcel and Hexcel logo are registered trademarks of Hexcel Corporation, Stamford, Connecticut.
HexForce is a trademark of Hexcel Corporation, Stamford, Connecticut.
by | Sep 27, 2025
HexForce
GA090
Carbon Fabric
Product Data
STYLE GA090 US System
Type of Yarns Warp Yarn: 12K Carbon, 33MSI
Fill Yarn: Proprietary Heatset
Fabric Weight, Dry 8.9 oz/yd
2
302 g/m
2
Weave Style Plain Heatset
CONSTRUCTION
Nominal Construction Warp Count: 10/in
Fill Count: 4/in
Fabric Thickness 12.5 mil 0.32 mm
IMPORTANT
All information is believed to be accurate but is given without acceptance of liability. All values have been
generated from limited data. The values listed for weight, thickness and breaking strengths are typical greige
values, unless otherwise noted. Users should make their own assessment of the suitability of any product for
the purpose required. All sales are made subject to our standard terms of sales which include limitations on
liability and other important terms. The fabric style listed may not be available from inventory and minimum
order quantities may apply.
FOR FURTHER INFORMATION, PLEASE CONTACT US
1913 North King Street
Seguin, Texas 78155
Phone: 830-379-1580
Fax: 830-379-9544
Customer Service Toll Free: 1-866-601-5430
For European sales office numbers and a full address list, please go to:
http://www.hexcel.com/contact/salesoffices
Hexcel and Hexcel logo are registered trademarks of Hexcel Corporation, Stamford, Connecticut.
HexForce is a trademark of Hexcel Corporation, Stamford, Connecticut.