SIL66BE-249ALH
Laminating Resin
(Surf/Sail Board)
Technical Data Sheet
INTERPLASTIC CORPORATION
3535 Latonia Avenue
Fort Wright, KY 41015- 0159
859.292.7400 Fax: 859.292.7424
www.interplastic.com
SIL66BE-249ALH is a surfboard laminating resin containing 35% maximum styrene. It contains
UV stabilizer and does not contain wax.
TYPICAL RESIN PROPERTIES @ 77 F RESULTS
Brookfield Viscosity @ 20 rpm, cps 410 610
Brookfield Spindle No. (RV) 2
Catalyst, %, DDM-9 MEK-P 1.00
Gel Time, minutes:seconds 11:00 19:00
Gel to Peak Time, minutes:seconds 9:00 19:30
Peak Exotherm, F 275 315
Solids, % 65.0 68.0
UV Test Positive
MECHANICAL PROPERTIES OF NEAT CURED RESIN RESULTS
Property:
ASTM Test Method
Psi Mpa
Flexural Strength D-790 20,200 139.3
Flexural Modulus D-790 5.85 x 10
5
4033
Tensile Strength D-638 10,500 72.4
Tensile Modulus D-638 6.17 x 10
5
4254
Tensile Elongation D-638 2.1 %
Heat Distortion Temperature D-648 149 F / 65.0 C
Hardness, Barcol 934-1 D-2583 42 – 44
Revised: 05/14
All specifications and properties specified above are approximate. Specifications and properties of material delivered may vary slightly
from those given above. Interplastic Corporation makes no representations of fact regarding the material except those specified above.
No person has any authority to bind Interplastic Corporation to any representation except those specified above. Final determination of
the suitability of the material for the use contemplated is the sole responsibility of the Buyer. The Thermoset Resins Division’s technical
sales representatives will assist in developing procedures to fit individual requirements.
by | Sep 27, 2025
SIL66BQ-249 / SIL66BQ-249A
Surfboard Resin
Technical Data Sheet
INTERPLASTIC CORPORATION
3535 Latonia Avenue
Fort Wright, KY 41015-0159
859.292.7400 Fax: 859.292.7424
www.interplastic.com
SIL66BQ-249 has exceptionally good color and cures almost water clear in laminates or films.
It has a low viscosity for easy wet out and is promoted for room temperature cure. We suggest
SIL66BQ-249 whenever color is of paramount importance.
SIL66BQ-249A is a version containing UV Stabilizer.
SIL66BQ-249/249A is also suitable as a base coat for flooring use in meat and poultry
processing facilities that must conform to USDA requirements. SIL66BQ-250/250A is used as
the top coat, as it contains wax.
TYPICAL RESIN PROPERTIES @ 77 F RESULTS
Brookfield Viscosity @ 20 rpm, cps 400 600
Brookfield Spindle No. (RV) 2
Catalyst, %, DDM-9 MEK-P 1.00
Gel Time, minutes:seconds 11:00 19:00
Gel to Peak Time, minutes:seconds 12:00 23:00
Peak Exotherm, F 255 295
Solids, % 61.5 64.5
UV Test Positive for 249A
Specific Gravity 1.07 1.11
MECHANICAL PROPERTIES OF NEAT CURED RESIN RESULTS
Property
ASTM Test Method
Psi Mpa
Flexural Strength D-790 20,100 138.6
Flexural Modulus D-790 5.94 x 10
5
4095
Tensile Strength D-638 10,100 69.6
Tensile Modulus D-638 6.10 x 10
5
4206
Tensile Elongation D-638 1.9%
1.9 Heat Distortion Temperature D-648 156 F / 68.9 C
68.9 C Hardness, Barcol 934-1 D-2583 42 – 44
44
Revised: 2/18
All specifications and properties specified above are approximate. Specifications and properties of material delivered may vary slightly
from those given above. Interplastic Corporation makes no representations of fact regarding the material except those specified
above. No person has any authority to bind Interplastic Corporation to any representation except those specified above. Final
determination of the suitability of the material for the use contemplated is the sole responsibility of the Buyer. Our technical sales
representatives will assist in developing procedures to fit individual requirements, but all advice is accepted at your risk and should be
checked for suitability to your particular processes. These test data and properties are based on results obtained for a specific
material under the specified test conditions. They are not to be used as specifications and are not warranted as performance attributes
for any product or system. Specifications and properties of standard production material may vary slightly from those in this report.
Interplastic Corporation makes no warranties regarding any material and/or samples described in this report unless that representation
is provided to your company in writing by a Technical Director of Interplastic Corporation or one of his or her managers.
by | Sep 27, 2025
by | Sep 27, 2025
PRODUCT DATASHEET
For more information and technical assistance contact Phillips 66 COPYLENE
Polypropylene at www.COPYLENE.com.
COPYLENE
CR350CS-01
Random Copolymer
Potential Applications: Product Description
COPYLENE
CR350CS-01 is a clarified, reactor grade, random
copolymer specially designed for clear injection molding appli-
cations and is formulated with lube for excellent mold release
for larger articles.
Typical Properties Method Value Unit
Physical
Melt Flow Rate (230 C/2.16kg) ASTM D 1238 35 g/10 min
Density Specific Gravity ASTM D 792 0.902 sp gr
Mechanical
Tensile Strength @ Yield
(2 in/min)
(50 mm/min)
ASTM D 638
4250 psi
29.3 MPa
Flexural Modulus
(0.05 in/min, 1% Secant, Procedure A)
(1 mm/min, 1% Secant, Procedure A)
ASTM D 790
155000 psi
1068 MPa
Tensile Elongation @Yld ASTM D 638 13.5%
Impact
Notched izod impact
(73 F, Method A)
(23 C, Method A)
ASTM D 256
1.0 ft-lb/in
53 J/m
DTUL @66psi Unannealed ASTM D 648 74 C
Product Properties
For regulatory compliance information, see COPYLENE
CR350CS-01 Product Stewardship Information Sheet. MSDS available upon request, or on our Web site at
www.COPYLENE.com. The product specifications are nominal properties and do not reflect normal testing variance and should not be used for specification
purposes.
Revision Date November 2012
COPYLENE
Injection Molding
CSB 12-3120
Before using this product, the user is advised and cautioned to make its own determination and assessment of
the safety and suitability of the product for the specific use in question and is further advised against relying on
the information contained herein as it may relate to any specific use or application. It is the ultimate responsibility
of the user to ensure that the product is suited and the information is applicable to the user s specific application.
Phillips 66 Company does not make, and expressly disclaims, all warranties, including warranties of merchant-
ability or fitness for a particular purpose, regardless of whether oral or written, express or implied, or allegedly
arising from any usage of any trade or from any course of dealing in connection with the use of the information
contained herein or the product itself. The user expressly assumes all risk and liability, whether based in contract,
tort or otherwise, in connection with the use of the information contained herein or the product itself. Further, in-
formation contained herein is given without reverence to any intellectual property issues, as well as federal, state
or local laws which may be encountered in the use thereof. Such questions should be investigated by the user.
PHILLIPS 66
, PHILLIPS 66
Shield, COPYLENE
and other trademarks displayed herein are registered trademarks of Phillips 66
Company or one of its subsidiaries.
by | Sep 27, 2025
by | Sep 27, 2025
by | Sep 27, 2025
by | Sep 27, 2025
PRODUCT DATASHEET
For more information and technical assistance contact Phillips 66 COPYLENE
Polypropylene at www.COPYLENE.com.
COPYLENE
CR350CS-01
Random Copolymer
Potential Applications: Product Description
COPYLENE
CR350CS-01 is a clarified, reactor grade, random
copolymer specially designed for clear injection molding appli-
cations and is formulated with lube for excellent mold release
for larger articles.
Typical Properties Method Value Unit
Physical
Melt Flow Rate (230 C/2.16kg) ASTM D 1238 35 g/10 min
Density Specific Gravity ASTM D 792 0.902 sp gr
Mechanical
Tensile Strength @ Yield
(2 in/min)
(50 mm/min)
ASTM D 638
4250 psi
29.3 MPa
Flexural Modulus
(0.05 in/min, 1% Secant, Procedure A)
(1 mm/min, 1% Secant, Procedure A)
ASTM D 790
155000 psi
1068 MPa
Tensile Elongation @Yld ASTM D 638 13.5%
Impact
Notched izod impact
(73 F, Method A)
(23 C, Method A)
ASTM D 256
1.0 ft-lb/in
53 J/m
DTUL @66psi Unannealed ASTM D 648 74 C
Product Properties
For regulatory compliance information, see COPYLENE
CR350CS-01 Product Stewardship Information Sheet. MSDS available upon request, or on our Web site at
www.COPYLENE.com. The product specifications are nominal properties and do not reflect normal testing variance and should not be used for specification
purposes.
Revision Date November 2012
COPYLENE
Injection Molding
CSB 12-3120
Before using this product, the user is advised and cautioned to make its own determination and assessment of
the safety and suitability of the product for the specific use in question and is further advised against relying on
the information contained herein as it may relate to any specific use or application. It is the ultimate responsibility
of the user to ensure that the product is suited and the information is applicable to the user s specific application.
Phillips 66 Company does not make, and expressly disclaims, all warranties, including warranties of merchant-
ability or fitness for a particular purpose, regardless of whether oral or written, express or implied, or allegedly
arising from any usage of any trade or from any course of dealing in connection with the use of the information
contained herein or the product itself. The user expressly assumes all risk and liability, whether based in contract,
tort or otherwise, in connection with the use of the information contained herein or the product itself. Further, in-
formation contained herein is given without reverence to any intellectual property issues, as well as federal, state
or local laws which may be encountered in the use thereof. Such questions should be investigated by the user.
PHILLIPS 66
, PHILLIPS 66
Shield, COPYLENE
and other trademarks displayed herein are registered trademarks of Phillips 66
Company or one of its subsidiaries.