Technical Datasheet – METYX Composite Reinforcements
PRODUCT CODE 4201227
PRODUCT NAME CLT400 E05C-0/90 BX C-50-50KW-1270MM
PRODUCT DESCRIPTION
CUSTOMER CODE
CUSTOMER ID
REINFORCEMENT CONSTRUCTION
LAYER FIBER TYPE AREA WEIGHT
1
90
50K-3.750 TEX 200 gr/m
2 50K-3.750 TEX 200 gr/m
0
3
4
7.6 TEX 8 gr/m
5
6
7
8
9
TOTAL* 408 gr/m ( %5)* Measurement method based on ISO 3374 .
OTHER PORPERTIES ROLL INFO
Stitch Gauge 5 stitches/inch Roll Width 127 cm
Stitch Type Tricot Roll Weight 26 kg
Stitch Length 2,5 mm Roll Length 50 m
Pilot Yarn / Position– Core Diameter 3 inc (7.62cm)
Resin Compatibility Loss on Ignition Moisture Content
Vinylester, Epoxy, Polyester resins – Max.%0,20 by weight (ISO 3344)
Packaging
All rolls are wrapped with polyethylene bags; placed in pallet boxes or in single cardboard boxes or in
pyramid style on pallets.
Labelling
Each roll is labelled on the inner side of the core, on the bag or on the cardboard boxes including a unique
reference number for its traceability.
Storage
Store at %40-70 relative humidity and 18-30 C temperature range. Recommended to be brought to working
area 24 hrs prior to use.
System Certification Product Certification
ISO 9001; 14001; 45001; 27001 DNV-GL Approved
Orhanli Mh. G ls m Sok. No:14, 34956, Tuzla Istanbul T RK YE
Phone :+90-216-394-32- +90-216-394-32- www.metyx.com
FR-159-2/14.08.2018
by | Sep 27, 2025
Fax : Web :
Orhanli Mh. G ls m Sok. No:14, 34956, Tuzla Istanbul T RK YE
Phone :+90-216-394-32- +90-216-394-32- www.metyx.com
FR-159-2/14.08.2018
Storage
Store at %40-70 relative humidity and 18-30 C temperature range. Recommended to be brought to working
area 24 hrs prior to use.
System Certification Product Certification
ISO 9001; 14001; 45001; 27001 DNV-GL Approved
Vinylester, Epoxy, Polyester resins – Max.%0,20 by weight (ISO 3344)
Packaging
All rolls are wrapped with polyethylene bags; placed in pallet boxes or in single cardboard boxes or in
pyramid style on pallets.
Labelling
Each roll is labelled on the inner side of the core, on the bag or on the cardboard boxes including a unique
reference number for its traceability.
Pilot Yarn / Position– Core Diameter 3 inc(76.2cm)
Resin Compatibility Loss on Ignition Moisture Content
Stitch Type Pillar Roll Weight 25 kg
Stitch Length 2,6mm Roll Length 50 m
OTHER PORPERTIES ROLL INFO
Stitch Gauge 5 Stitches/inch Roll Width 127 cm
9
TOTAL* 405 gr/m ( %5)* Measurement method based on ISO 3374 .
7
8
5
6
3 STITCH PES 5 gr/m
4
1 45 50K – 3.750 TEX 200 gr/m
2 45 50K – 3.750 TEX 200 gr/m
CUSTOMER CODE
CUSTOMER ID
REINFORCEMENT CONSTRUCTION
LAYER FIBER TYPE AREA WEIGHT
Technical Datasheet – METYX Composite Reinforcements
PRODUCT CODE 4201115
PRODUCT NAME CX400 E05F-45/45 BX CF-50K-50-1270MM
PRODUCT DESCRIPTION
by | Sep 27, 2025
Fax : Web :
Orhanli Mh. G ls m Sok. No:14, 34956, Tuzla Istanbul T RK YE
Phone :+90-216-394-32- +90-216-394-32- www.metyx.com
FR-159-2/14.08.2018
Storage
Store at %40-70 relative humidity and 18-30 C temperature range. Recommended to be brought to working
area 24 hrs prior to use.
System Certification Product Certification
ISO 9001; 14001; 45001; 27001 DNV-GL Approved
Vinylester, Epoxy, Polyester resins – Max.%0,20 by weight (ISO 3344)
Packaging
All rolls are wrapped with polyethylene bags; placed in pallet boxes or in single cardboard boxes or in
pyramid style on pallets.
Labelling
Each roll is labelled on the inner side of the core, on the bag or on the cardboard boxes including a unique
reference number for its traceability.
Pilot Yarn / Position– Core Diameter 3 inc(76.2cm)
Resin Compatibility Loss on Ignition Moisture Content
Stitch Type Pillar Roll Weight 25 kg
Stitch Length 2,6mm Roll Length 50 m
OTHER PORPERTIES ROLL INFO
Stitch Gauge 5 Stitches/inch Roll Width 127 cm
9
TOTAL* 405 gr/m ( %5)* Measurement method based on ISO 3374 .
7
8
5
6
3 STITCH PES 5 gr/m
4
1 45 50K – 3.750 TEX 200 gr/m
2 45 50K – 3.750 TEX 200 gr/m
CUSTOMER CODE
CUSTOMER ID
REINFORCEMENT CONSTRUCTION
LAYER FIBER TYPE AREA WEIGHT
Technical Datasheet – METYX Composite Reinforcements
PRODUCT CODE 4201115
PRODUCT NAME CX400 E05F-45/45 BX CF-50K-50-1270MM
PRODUCT DESCRIPTION
by | Sep 27, 2025
1
2
3
4
5
6
7
* Checked via own test based on ISO 3374. TOTAL* 461 gr / m2 ( %5 )
5stitches/inch Roll Width 127 cm
Roll Weight 37 kg
mm Roll Length 63 m
/ Core Diameter 76 mm
Packaging
Labelling
Storage
FIBER TYPE LAYER AREA WEIGHT
8 gr / m268 Tex
68 Tex
76 Dtex
1600 Tex – 24K Carbon
68 Tex
440 gr / m2
4 gr / m2
Technical Datasheet – METYX Composite Reinforcements
REINFORCEMENT CONSTRUCTION
5200.006.201
CL440 E05A-0 UNIDIRECTIONAL CARBON 24K-127CM
.
.
.
PRODUCT CODE
PRODUCT NAME
PRODUCT DESCRIPTION
Stitch Length
Pilot Yarn / Position
ROLL INFOOTHER PROPERTIES
4 gr / m2
5 gr / m2
Certification DNV
All rolls are wrapped with polyethylene bags; placed in pallet boxes or in single cardboard
boxes or in pyramid style on pallets.
Each roll is labelled on the inner side of the core, on the bag or on the cardboard boxes
including a unique reference number for its traceability.
Tricot
Lloyd s Register
2,6
Phone : +90-216-394-32-60
Fax : +90-216-394-32-58
Web : www.metyx.com
Metyx products are produced by Telateks A.S. company who
is run by ISO 9001:2008 QA System.
TYPE Approved
Note: The above specifications reflect the product data on release date but are subject to change without prior notice.
–
CUSTOMER CODE
CUSTOMER ID
Stitch Gauge
Stitch Type
0
+45
-90
-45
Stitch
FR-4.01-12B.00TDM- .00/20.03.08
Resin Compatibility Loss on Ignition Moisture Content
–Vinylester, Epoxy resins
Store at %40-70 relative humidity and 18-30
o
C temperature range.
Recommended to be brought to working area 24 hrs prior to use.
Address:
Orhanli Beldesi 34956
Tuzla Istanbul TURKIYE
by | Sep 27, 2025
Unit 4
The Reservation
Sleaford Enterprise Park
Sleaford
Lincolnshire
NG34 7BY
www.shdcomposites.com
Tel: +44 (0) 1529 307629
sales@shdcomposites.com
SHD/MISC/945 Issue: 1 21
st
June 2022
Revised: 04
th
August 2022 Uncontrolled copy when printed
VTC401
Epoxy Component Prepreg
Introduction
VTC401 is an epoxy resin system designed to give an initial cure at low temperatures or snap cure at high
temperatures with enhanced toughness, honeycomb bondability and higher service temperature, giving
greater flexibility in component manufacture. It can be supplied on a variety of fabrics in UD format to meet
your cost and manufacturing requirements.
Typical applications: General purpose Visual
Available variants VTC401B, black pigmented
VTC401LV, high tack
Key Features & Benefits
Cure temperature from 65 C to 120 C
Service temperature up to 120 C
Low CTE and shrinkage
Work life at 20 C: 21 days
Storage life at -18 C: 12 months
Very low VOC content no added solvents during manufacture
Snap cure available for hot press moulding consult SHD for details
Storage & Out Life
This material should be kept frozen at -18 C. It must be kept sealed in a polythene bag which must not be
opened until fully thawed to room temperature. If the material is not fully used, then the material must be
resealed in the polythene bag to prevent moisture absorption.
Unit 4
The Reservation
Sleaford Enterprise Park
Sleaford
Lincolnshire
NG34 7BY
www.shdcomposites.com
Tel: +44 (0) 1529 307629
sales@shdcomposites.com
SHD/MISC/945 Issue: 1 21
st
June 2022
Revised: 04
th
August 2022 Uncontrolled copy when printed
Cure Cycles & performances
CURE CYCLE OPTIONS:
Temperature Duration Tg
65 C (minimum) 16 hours 75 C
80 C 4 hours 90 C
100 C 1 hour 110 C
120 C (maximum) 45 minutes 130 C
Curing Schedule is meant to be a guide only and is subject to local conditions.
To avoid exotherm particular care must be taken with thick laminates.
Ramp rates must not exceed 3.0 C per minute during initial cure.
Ramp rates must not exceed 0.3 C per minute during post cure (free standing).
Typical Tg:
DMA Dry Tg
120 C for 1hr
Tg E Onset
Tg Peak Tan
130
139
C
C
Modified ASTM D7028
(Single Cantilever)
Tests performed on VTC401-G280T-42%RW-1250 laminates
Unit 4
The Reservation
Sleaford Enterprise Park
Sleaford
Lincolnshire
NG34 7BY
www.shdcomposites.com
Tel: +44 (0) 1529 307629
sales@shdcomposites.com
SHD/MISC/945 Issue: 1 21
st
June 2022
Revised: 04
th
August 2022 Uncontrolled copy when printed
Cured Material Properties
Tests performed on VTC401-C245T-HS-3K-42%RW laminates (245gsm 2×2 twill, T300 3k carbon fabric)
Test Results Standard
Vf
Fibre volume fraction 48.84 % BS EN ISO 14127
Method B
CPT
Cured ply thickness 0.285 mm BS EN ISO 14127
Method B
Tensile 0
Tensile 90
Tensile strength
Tensile modulus
Tensile strength
Tensile modulus
634
55.7
638
55.1
MPa
GPa
MPa
GPa
BS EN ISO 527-4
Compressive 0
Compressive 90
Compressive strength
Compressive strength
684
598
MPa
MPa
prEN 2850 Type B
Flexural 0
Flexural 90
Flexural strength
Flexural modulus
Flexural strength
Flexural modulus
873
51.2
854
49.4
MPa
GPa
MPa
GPa
BS EN ISO 14125
In-Plane Shear 45
In-Plane shear strength (ultimate)
121.6 MPa BS EN ISO 14129
Interlaminar Shear 0
Interlaminar Shear 90
Interlaminar shear strength
Interlaminar shear strength
71.3
72.2
MPa
MPa
BS EN ISO 14130
DMA Dry Tg
Initial cure
Tg E Onset
Tg Peak Tan
123
134
C
C
Modified ASTM D7028
(Single Cantilever)
Mechanical testing carried out at 21 2 C. Initial cure: 10mins at 80 C followed by 45mins at 120 C, autoclave 6bar. All figures in this report are actual test results
and have not been normalised. Testing was either completed by SHD Composites laboratories, or independently by UKAS approved organisations. Complete test
reports can be supplied independently upon request.
Unit 4
The Reservation
Sleaford Enterprise Park
Sleaford
Lincolnshire
NG34 7BY
www.shdcomposites.com
Tel: +44 (0) 1529 307629
sales@shdcomposites.com
SHD/MISC/945 Issue: 1 21
st
June 2022
Revised: 04
th
August 2022 Uncontrolled copy when printed
Viscosity Profile
Testing carried out using a rotational rheometer.
Health and Safety
This material contains epoxy resin which can cause allergic reactions with skin contact and must avoid
repeated and prolonged skin contact.
Please refer to the product Safety Data Sheet before using this material. The following precautions must be
taken when using epoxy resin prepregs:
Overalls must be worn.
Impervious gloves must be worn.
Curing schedule is meant to be as a guide only and is subject to local conditions.
To avoid exotherm, particular care must be taken with thick laminates.
Ramp rates must not exceed 3.0 C/min during initial cure and 0.3 C/min during post cure.
Disclaimer: Technical advice, instruction, data or recommendation, whether verbal or in writing, is given in good faith. The SHD company providing any such
advice gives no warranty or guarantee, whether express or implied, in relation to such advice.
Customers must carry out their own tests and assessments as necessary in order to determine the quality and suitability of the product for their particular
application and circumstances. Such testing should be performed under conditions identical to those to which the final component/product may be subjected.
Values listed in any SHD document are for typical properties of the product or substance in question and are not intended to be used in establishing either
statistical specifications nor engineering basis values. They do not constitute either minimum or maximum values for the product or substance in question.
by | Sep 27, 2025
SHD COMPOSITE MATERIALS INC
203 McKenzie Road
Mooresville
NC 28117
www.shdcomposites.com
Tel +1 (704) 6266876
sales@shdcomposites.com
Issued 01
st
February 2018
Note: The information and assistance provided herein is for your consideration without legal responsibility. Users are required to perform verification and
testing to confirm that the product meets with their requirements.
VTC401
Epoxy Component Prepreg
Introduction
VTC401 is an epoxy resin system designed to give an initial cure at low temperatures or snap cure at high
temperatures with enhanced toughness, honeycomb bondability and higher service temperature, giving
greater flexibility in component manufacture. It can be supplied on a variety of fabrics in UD format to meet
your cost and manufacturing requirements.
Typical applications: General purpose Visual
Key Features & Benefits
Cure temperature from 150 F to 250 F
Service temperature up to 275 F after post cure
Low CTE and shrinkage
Work life at 70 C: 21 days
Storage life at 0 F: 12 months
Very low VOC content no added solvents during manufacture
Snap cure available for hot press moulding consult SHD for details
Storage & Out Life
This material should be kept frozen at 0 F. It must be kept sealed in a polythene bag which must not be
opened until fully thawed to room temperature. If the material is not fully used, then the material must be
resealed in the polythene bag to prevent moisture absorption.
SHD COMPOSITE MATERIALS INC
203 McKenzie Road
Mooresville
NC 28117
www.shdcomposites.com
Tel +1 (704) 6266876
sales@shdcomposites.com
Issued 01
st
February 2018
Note: The information and assistance provided herein is for your consideration without legal responsibility. Users are required to perform verification and
testing to confirm that the product meets with their requirements.
Mechanical Properties
Tests performed on VTC401-C200T-T300-2X2T-3K-42%RW laminates
Test Results Standard
Compression Compressive strength 631 MPa BS EN ISO 14126 : 1999
Tension Tensile strength 573 MPa BS EN ISO 527-4 : 1997
Tensile modulus 52.7 GPa
Flexure Flexural strength 863 MPa BS EN ISO 14125 : 1998
Flexural modulus 51.7 GPa
Strain to failure 1.7 %
Interlaminar Shear Strength Interlaminar shear strength 74.0 MPa BS EN 2563 : 1997
DMA Tg Storage Modulus Onset 290 F AITM 1-0003 Issue 3
Tg Tan Peak 305 F
Mechanical testing carried out at 80 F, 50 5% RH. All mechanical tests were completed independently by UKAS approved
organisations. Complete tests reports can be supplied independently upon request. All figures are actual test results and haven t
been normalised.
Cure Cycles & performances
Cure Initial Min Cure Tg
150 F (minimum) 16 hours 160 F
175 F 4 hours 185 F
210 F 1 hour 220 F
250 F (maximum) 45 minutes 260 F
275 F Post-cure 2 hours 285 F
Curing Schedule is meant to be a guide only and is subject to local conditions.
To avoid exotherm particular care must be taken with thick laminates.
Ramp rates must not exceed 5 F per minute during initial cure.
Ramp rates must not exceed 1 F per minute during post cure (free standing).
Volatile content < 1.0%
Fibre volume fraction 50 to 60%
Voidage (autoclave cure) < 1.0%
SHD COMPOSITE MATERIALS INC
203 McKenzie Road
Mooresville
NC 28117
www.shdcomposites.com
Tel +1 (704) 6266876
sales@shdcomposites.com
Issued 01
st
February 2018
Note: The information and assistance provided herein is for your consideration without legal responsibility. Users are required to perform verification and
testing to confirm that the product meets with their requirements.
Viscosity Profile
Testing carried out at 80 F, 50 5% RH. Ramp rate: 4 F/min.
Health and Safety
This material contains epoxy resin which can cause allergic reactions with skin contact and must avoid
repeated and prolonged skin contact.
Please refer to the product Safety Data Sheet before using this material. The following precautions must be
taken when using epoxy resin prepregs:
Overalls must be worn.
Impervious gloves must be worn.
Curing schedule is meant to be as a guide only and is subject to local conditions.
To avoid exotherm, particular care must be taken with thick laminates.
Ramp rates must not exceed 5 F/min during initial cure and 1 F/min during post cure.
SHD Composite Materials Ltd cannot accept any liability for injury or damage where the above precautions have not been taken or where the material is used
for any purpose other than its intended use.
1
10
100
1000
10000
100000
1000000
10000000
20 40 60 80 100 120 140
Pa.s
C
VTC401Viscosity Profile
by | Sep 27, 2025
by | Sep 27, 2025
HexForce
3783
Fiber Glass Fabric
Product Data
STYLE 3783 US System SI Units
Type of Yarns Warp Yarn: ECG 37 1/0 EC9 134
Fill Yarn: ECG 37 1/0 EC9 134
Fabric Weight, Dry 16.08 oz/yd
2
546 g/m
2
Weave Style 8 Harness Satin
CONSTRUCTION
Nominal Construction Warp Count: 54/in 21.25/cm
Fill Count: 48/in 18.89/cm
Fabric Thickness 15.70 mil 0.40 mm
Breaking Strength Warp 750 lbf/in
Filling 560 lbf/in
IMPORTANT
All information is believed to be accurate but is given without acceptance of liability. All values have been
generated from limited data. The values listed for weight, thickness and breaking strengths are typical greige
values, unless otherwise noted. Users should make their own assessment of the suitability of any product for
the purpose required. All sales are made subject to our standard terms of sales which include limitations on
liability and other important terms. The fabric style listed may not be available from inventory and minimum
order quantities may apply.
FOR FURTHER INFORMATION, PLEASE CONTACT US
1913 North King Street
Seguin, Texas 78155
Phone: 830-379-1580
Fax: 830-379-9544
Customer Service Toll Free: 1-866-601-5430
For European sales office numbers and a full address list, please go to:
http://www.hexcel.com/contact/salesoffices
Hexcel and Hexcel logo are registered trademarks of Hexcel Corporation, Stamford, Connecticut.
HexForce is a trademark of Hexcel Corporation, Stamford, Connecticut.
by | Sep 27, 2025
Product Data
3733
Fiber Glass Fabric
STYLE 3733 US System SI Units
Type of Yarns Warp Yarn: ECG 37 1/0 EC9 134
Fill Yarn: ECG 37 1/0 EC9 134
Fabric Weight, Dry 5.80 oz/yd
2
197 g/m
2
Weave Style Plain
CONSTRUCTION
Nominal Construction Warp Count: 18/in 7.1/cm
Fill Count: 18/in 7.1/cm
Fabric Thickness 8.0 mils 0.20 mm
Yarn Breaking Strength Warp 250 lbf/in 219 daN/5cm
Filling 200 lbf/in 175 daN/5cm
Markets
Recreational
Applications
Low Pressure Composites
IMPORTANT
All information is believed to be accurate but is given without acceptance of liability. All values have been generated from
limited data. The values listed for weight, thickness, and breaking strengths are typical greige values, unless otherwise
noted. Users should make their own assessment of the suitability of any product for the purpose required. All sales are
made subject to our standard terms of sales which include limitations on liability and other important terms. The fabric
style listed may not be available from inventory, and minimum order quantities may apply.
FOR FURTHER INFORMATION, PLEASE CONTACT US
2200 S. Murray Ave. 580 North Gilbert St. 3, Avenue Condorcet
Anderson, SC 29622 Fullerton, CA 92833 69608 Villeurbanne Cedex
USA USA France
Phone: 864-225-7028 Phone: 714-278-0850 Phone: 33 4 72 44 40 00
Fax: 864-260-6581 Fax: 714-526-2367 Fax: 33 4 78 89 72 30
by | Sep 27, 2025
Product Data
3733
Fiber Glass Fabric
STYLE 3733 US System SI Units
Type of Yarns Warp Yarn: ECG 37 1/0 EC9 134
Fill Yarn: ECG 37 1/0 EC9 134
Fabric Weight, Dry 5.80 oz/yd
2
197 g/m
2
Weave Style Plain
CONSTRUCTION
Nominal Construction Warp Count: 18/in 7.1/cm
Fill Count: 18/in 7.1/cm
Fabric Thickness 8.0 mils 0.20 mm
Yarn Breaking Strength Warp 250 lbf/in 219 daN/5cm
Filling 200 lbf/in 175 daN/5cm
Markets
Recreational
Applications
Low Pressure Composites
IMPORTANT
All information is believed to be accurate but is given without acceptance of liability. All values have been generated from
limited data. The values listed for weight, thickness, and breaking strengths are typical greige values, unless otherwise
noted. Users should make their own assessment of the suitability of any product for the purpose required. All sales are
made subject to our standard terms of sales which include limitations on liability and other important terms. The fabric
style listed may not be available from inventory, and minimum order quantities may apply.
FOR FURTHER INFORMATION, PLEASE CONTACT US
2200 S. Murray Ave. 580 North Gilbert St. 3, Avenue Condorcet
Anderson, SC 29622 Fullerton, CA 92833 69608 Villeurbanne Cedex
USA USA France
Phone: 864-225-7028 Phone: 714-278-0850 Phone: 33 4 72 44 40 00
Fax: 864-260-6581 Fax: 714-526-2367 Fax: 33 4 78 89 72 30